NASA NTRS1993

Transformation to Ni5Al3 in a 63.0 at. pct Ni-Al alloy

Microstructures of 63 at. pct P/M Ni-Al alloys with a composition close to the stoichiometry of the Ni5Al3 phase were investigated using homogenized and quenched specimens aged at low temperatures for various times. Results of analyses of XRD data and electron microscopy observations were used for quantitative phase analysis, performed to calculate the (NiAl + Ni5Al3)/Ni5Al3 phase boundary locations. The measured lattice parameters of Ni5Al3 phase formed at 823, 873, and 923 K indicated an increase in tetragonality of the phase with increasing nickel content.

Khadkikar, P. S.↗

NASA NTRS1990

Preferred orientations in extruded nickel and iron aluminides

A plotting of inverse pole figures is used to characterize the preferred orientations in both powder-extruded and cast-and-extruded NiAl, FeAl, and Ni3Al; the preferred 111 orientation has been noted along the extrusion direction in both powder-extruded and cast-and-extruded NiAl. While powder-extruded FeAl also had a 111 preferred orientation in the as-extruded condition, 110 was observed upon casting and extrusion; this was in turn replaced by a 211 orientation preference upon annealing, although annealing did not change the preferred orientation in either NiAl or in powder-extruded FeAl.

Khadkikar, P. S.↗

NASA NTRS1989

Notch effects on room temperature tensile and bend properties of Ni3Al and Ni3Al+B

The notched mechanical properties of Ni3Al and Ni3Al+B prepared by powder metallurgy techniques have been determined in both tension and bending at room temperature. Tensile tests performed using double-notched specimens containing relatively blunt notches produced intergranular fracture in both Ni3Al and Ni3Al+B, with evidence of fracture initiating in an intergranular manner ahead of the blunt notch in both cases. Estimates of notched fracture toughness from bend tests and of local grain boundary fracture stress from the notched tensile tests suggest an increase in these values with boron addition.

Khadkikar, P. S.↗

NASA NTRS1989

Strength and toughness of composite materials based on nickel aluminide matrices

Several nickel aluminide matrix composites were prepared using vacuum hot pressing techniques. The matrix compositions, based on Ni3Al, Ni3Al+B, and NiAl, were reinforced with 10 vol pct TiB2 particles. Both smooth- and notched-bend tests were conducted at room temperature on the monolithic as well as the reinforced materials in order to determine the effects of TiB2 reinforcement on both the smooth-bend and notched-bend properties. TiB2 additions were shown to improve the smooth-bend strengths regardless of the matrix composition, while notched-bend tests, conducted to provide estimates of fracture toughness, revealed somewhat lower values for the composites in comparison to the monolithic materials. Fractographic analyses and in situ fracture observations of the composites revealed that preferential fracture in regions of clustered TiB2 particles may significantly affect the measured toughnesses.

Rigney, J. D.↗

NASA NTRS1988

Potential for NiAl based alloys for high temperature applications

The B2 nickel aluminide, NiAl, is of potential use for high temperature structural applications because of its high melting point, low density, and oxidation resistance. An overview of recent attempts to improve the low temperature ductility as well as the high temperature strength of this alloy is presented. Room temperature tensile ductility of 2.5 percent can be obtained in a stoichiometric binary alloy by careful control of the composition and processing conditions. Alloying additions to improve high temperature creep resistance are most effective when fine distributions of ternary intermetallic phases can be obtained. A promising direction for exploiting the advantages of this alloy may be as a matrix for composite materials.

Vedula, K.↗

NASA NTRS1987

Analysis of NiAlTa precipitates in beta-NiAl + 2 at. pct Ta alloy

Results are reported from experiments performed to identify the precipitates, and their orientation in the matrix, in a beta-NiAl alloy containing 2 at. pct. Ta after undergoing creep test at 1300 K. Test specimens formed by extruding hot powders were compressed at 1300 K for about 50 hr at a strain rate averaging 6/1 million per sec. The specimens were then thinned and examined under an electron microscope and by X-ray diffractometry. An intermetallic NiAlTa compound with a hexagonal Cl4 structure appeared as second phase precipitates in the samples, exhibiting plate-like shapes and a habit plane close to (012). The prism planes of the hexagonal NiAlTa precipitates paralleled the closest packed planes in the cubic beta-NiAl matrix.

Pathare, V.↗

NASA NTRS1987

The role of boron in ductilizing Ni3Al

Ductilization of Ni3Al at room temperature by microalloying with boron has been primarily attributed to the increased grain boundary cohesion in the presence of boron. However, another aspect of the role played by boron in ductilizing Ni3Al is revealed when the Hall-Petch relationships for Ni3Al and B-doped Ni3Al are compared. A shallower slope for the B-doped Ni3Al compared to that for Ni3Al indicates a reduced resistance to slip propagation across grain boundaries, and therefore reduced stress concentration at boundaries, in the presence of boron. This comparison of Hall-Petch relationships was carried out by generating data for powder processed B-doped Ni3Al at various grain sizes and by compiling data for Ni3Al from the literature. In addition, the room temperature fracture of B-doped Ni3Al has been shown to initiate along certain grain boundaries. The fracture eventually occurs by transgranular ductile tearing.

Vedula, K.↗

NASA NTRS1987

Compressive creep behavior of alloys based on B2 FeAl

Alloys based on FeAl are attractive alternative materials for environmental resistance at intermediate temperatures. Addition of small amounts of Nb, Hf, Ta, Mo, Zr, and B were shown to improve the compressive creep of this alloy at 1100 K. Boron, in particular, was found to have a synergistic effect along with Zr in providing properties substantially better than the binary alloy. This improvement seems to be related to the higher activation energy found for this alloy, suggesting a modification in the diffusion behavior due to the alloying additions.

Mantravadi, N.↗

NASA NTRS1987

Two-phase nickel aluminides

The as-extruded microstructures of two alloys in the two phase field consisting of Ni3Al and NiAl in the Ni-Al phase diagram exhibit fibrous morphology and consist of Ll(2) Ni3Al and B2 NiAl. These as-extruded microstructures can be modified dramatically by suitable heat treatments. Martensite plus NiAl or martensite plus Ni3Al microstructures are obtained upon quenching from 1523 K. Aging of martensite at 873 K results in the recently identified phase Ni5Al, whereas aging at 1123 K reverts the microstructures to Ni3Al plus NiAl. The microstructures with predominantly martensite of Ni5Al3 phases are brittle in tension at room temperature. The latter microstructure does not deform plastically even in compression at room temperature. However, some promise of room temperature tensile ductility is indicated by the Ni3Al plus NiAl phase mixtures.

Khadkikar, P. S.↗

NASA NTRS1987

B2 aluminides for high temperature applications

The structure, phase composition, and mechanical properties of B2 FeAl and NiAl aluminides are investigated. It is noted that, in both alloys, the room temperature brittleness is of primary concern. In the case of FeAl, significant tensile ductilities of up to 8 percent have been obtained at room temperature in iron-rich alloys. In the case of polycrystalline NiAl, attempts to improve ductility have not so far been successfull. Possible solutions to this problem are examined.

Vedula, K.↗

NASA NTRS1987

Powder processing of nickel and other aluminides by hot consolidation

Alloys based on FeAl, NiAl, and Ni3Al have been processed by extrusion of powders over a range of compositions, powder characteristics, and extrusion parameters. It is found that extrusion leads to dynamic recrystallization and that the grain size of the extrusions depends on the powder size, extrusion temperature, and extrusion ratio. Prior particle boundary oxides play an important role in controlling the grain size and uniformity by acting as obstacles to grain growth. Hot isostatic pressing and vacuum hot pressing can be used for powder densification, but prior particle oxides are not effectively broken up due to insufficient shearing deformation.

Vedula, K.↗

NASA NTRS1987

Hot extrusion of B2 iron aluminide powders

The objective of the study was to investigate the effect of powder and processing variables on the microstructure and resultant tensile properties of an extruded FeAlZrB alloy. For a given powder particle size, increasing the extrusion temperature from 1250 to 1450 K is found to increase the grain size and produce a more uniform microstructure. At high extrusion temperatures, where grain boundary mobility is high, powder size is not critical in determining the grain size. The addition of Y2O3 dispersion (1 vol pct) by mechanical alloying makes it possible to obtain very fine-grained materials at low and high extrusion temperatures.

Strothers, S.↗

NASA NTRS1986

High temperature dispersion strengthening of NiAl

A potential high temperature strengthening mechanism for alloys based on the intermetallic compound NiAl was investigated. This study forms part of an overall program at NASA Lewis Research Center for exploring the potential of alloys based on NiAl for high temperature applications. An alloy containing 2.26 at% Nb and produced by hot extrusion of blended powders was examined in detail using optical and electron microscopy. Interdiffusion between the blended Nb and NiAl powders results in the formation of intermediate phases. A fine dispersion of precipitates of a hexagonal, ordered NiAlNb phases in a matrix of NiAl can be produced and this results in strengthening of the alloy by interfering with dislocation motion at high temperature. These precipitates are, however, found to coarsen during the high temperature (1300 K) deformation at slow strain rates and this may impose some limitatioins on the use of this strengthening mechanism.

Sherman, M.↗

NASA NTRS1986

Effect of boron on tensile properties of B2 BeAl

Small additions of boron were shown to improve the room temperature ductility of the intermetallic compound Ni3Al. Boron is believed to segregate to the gain boundaries and strengthen them, allowing the inheret ductility of the grains to be achieved. The present study was undertaken to see if boron has a similar effect on the low temperature tensile properties of the equiatomic intermetallic compound FeAl. A binary alloy without boron is compared with an alloy containing 0.78 at % B (0.2 wt %) B, by tensile testing over the temperature range of 300 K to 640 K. Both alloys were processed by powder metallurgy. Results showed that 0.78 at % B addition to FeAl does indeed change the room temperature fracture mode from intergranular to transgranular, suggesting a strengthening of grain boundaries. The alloy containing boron is, however, still brittle at room temperature. A slight decrease in the ductile to brittle transition temperature is, nevertheless, observed. In addition a significant increase in strength of the alloy is observed with boron addition.

Crimp, M.↗

NASA NTRS1986

Compressive creep behavior of alloys based on B2 FeAl

Alloys based on FeAl are attractive alternate materials for environmental resistance at intermediate temperatures. Addition of small amounts of Nb, Hf, Ta, Mo, Zr, and B were shown to improve the compressive creep of this alloy at 1100 K. Boron, in particular, was found to have a synergistic effect along with Zr in providing properties substantially better than the binary alloy. This improvement seems to be related to the higher activation energy found for this alloy, suggesting a modification in the diffusion behavior due to the alloying additions.

Mantravadi, N.↗

NASA NTRS1985

Alloys based on NiAl for high temperature applications

The NiAl alloys for potential high temperature applications were studied. Alloys were prepared by powder metallurgy techniques. Flow stress values at slow strain rates and high temperatures were measured. Some ternary alloying additions (Hf, Ta and Nb) were identified. The mechanism of strengthening in alloys containing these additions appears to be a form of particle dislocation interaction. The effects of grain size and stoichiometry in binary alloys are also presented.

Vedula, K.↗