NASA NTRS1992

Elevated temperature crack growth

The purpose of this program was to extend the work performed in the base program (CR 182247) into the regime of time-dependent crack growth under isothermal and thermal mechanical fatigue (TMF) loading, where creep deformation also influences the crack growth behavior. The investigation was performed in a two-year, six-task, combined experimental and analytical program. The path-independent integrals for application to time-dependent crack growth were critically reviewed. The crack growth was simulated using a finite element method. The path-independent integrals were computed from the results of finite-element analyses. The ability of these integrals to correlate experimental crack growth data were evaluated under various loading and temperature conditions. The results indicate that some of these integrals are viable parameters for crack growth prediction at elevated temperatures.

Kim, K. S.↗

NASA NTRS1989

Elevated temperature crack growth

Alloy 718 crack growth experiments were conducted to assess the ability of the selected path-independent (P-I) integrals to describe the elevated temperature crack growth behavior. These tests were performed on single edge notch (SEN) specimens under displacement control with multiple extensometers to monitor the specimen and crack mouth opening displacement (CMOD). The displacements in these tests were sufficiently high to induce bulk cyclic inelastic deformation of the specimen. Under these conditions, the linear elastic fracture mechanics (LEFM) parameter K does not correlate the crack growth data. The experimentally measured displacement gradients at the end of specimen gage length were used as the boundary conditions in elastic-plastic finite element method (FEM) analyses. These analyses were performed with a node release approach using CYANIDE, a GEAE FEM code, which included a gap element which is capable of efficiently simulating crack closure. Excellent correlation was obtained between the experimentally measured and predicted variation of stress and CMOD with crack length and the stress-CMOD loops for Alloy 718 tests conducted at 538 C. This confirmed the accuracy of the FEM crack growth simulation approach. The experimentally measured crack growth rate data correlated well the selected P-I integrals. These investigations have produced significant progress in developing P-I integrals as non-linear fracture mechanics parameters. The results suggest that this methodology has the potential of accurately describing elevated temperature crack growth behavior under the combined influence of thermal cycling and bulk elastic-inelastic deformation states.

Kim, K. S.↗

NASA NTRS1988

Elevated temperature crack growth

A study was performed to examine the applicability of path-independent (P-I) integrals to crack growth problems in hot section components of gas turbine aircraft engines. Alloy 718 was used and the experimental parameters included combined temperature and strain cycling, thermal gradients, elastic-plastic strain levels, and mean strains. A literature review was conducted of proposed P-I integrals, and those capable of analyzing hot section component problems were selected and programmed into the postprocessor of a finite element code. Detailed elastic-plastic finite element analyses were conducted to simulate crack growth and crack closure of the test specimen, and to evaluate the P-I integrals. It was shown that the selected P-I integrals are very effective for predicting crack growth for isothermal conditions.

Kim, K. S.↗

NASA NTRS1988

Elevated temperature crack growth

The problem of crack growth in hot path components such as combustor liners is complicated by several practical and theoretical considerations. The loading environment of such components involves high temperature levels and gradients that lead to considerations such as thermal stresses, crack closure, hold time, inelastic strains (both time dependent and independent), and Thermal Mechanical Fatigue (TMF). In general, a good understanding of the influence of these factors on crack growth was not obtained. At the same time, several nonlinear fracture mechanics parameters were suggested for such applications; however, most of the proposed methods were not tested for broad applications such as required for hot section components. It was the purpose of this program to evaluate proposed nonlinear methods by performing a thorough experimental and analytical study. The results illustrated that much progress was made in developing nonlinear methods.

Kim, K. S.↗

NASA NTRS1988

Development of a unified constitutive model for an isotropic nickel base superalloy Rene 80

Accurate analysis of stress-strain behavior is of critical importance in the evaluation of life capabilities of hot section turbine engine components such as turbine blades and vanes. The constitutive equations used in the finite element analysis of such components must be capable of modeling a variety of complex behavior exhibited at high temperatures by cast superalloys. The classical separation of plasticity and creep employed in most of the finite element codes in use today is known to be deficient in modeling elevated temperature time dependent phenomena. Rate dependent, unified constitutive theories can overcome many of these difficulties. A new unified constitutive theory was developed to model the high temperature, time dependent behavior of Rene' 80 which is a cast turbine blade and vane nickel base superalloy. Considerations in model development included the cyclic softening behavior of Rene' 80, rate independence at lower temperatures and the development of a new model for static recovery.

Ramaswamy, V. G.↗

NASA NTRS1987

Elevated temperature crack growth

The purpose is to determine the ability of currently available P-I integrals to correlate fatigue crack propagation under conditions that simulate the turbojet engine combustor liner environment. The utility of advanced fracture mechanics measurements will also be evaluated. Research showed that the experimentally measured displacements and loads can be accurately predicted by finite element analyses that consider the growth of the fatigue crack. These results are being used to evaluate nonlinear fracture mechanics parameters for correlating the observed fatigue crack growth rates for different strain ranges.

Kim, K. S.↗

NASA NTRS1987

Elevated temperature crack growth

The objective of the Elevated Temperature Crack Growth Program is to evaluate proposed nonlinear fracture mechanics methods for application to hot section components of aircraft gas turbine engines. Progress during the past year included linear-elastic fracture mechanics data reduction on nonlinear crack growth rate data on Alloy 718. The bulk of the analytical work centered on thermal gradient problems and proposed fracture mechanics parameters. Good correlation of thermal gradient experimental displacement data and finite element prediction was obtained.

Malik, S. N.↗

NASA NTRS1986

Elevated temperature crack growth

It is necessary to relate the processes that control crack growth in the immediate vicinity of the crack tip to parameters that can be calculated from remote quantities, such as forces, stresses, or displacements. The most likely parameters appear to be certain path-independent (PI) integrals, several of which have already been proposed for application to high temperature inelastic problems. The ability of currently available PI-integrals to correlate fatigue crack propagation under conditions that simulate the engine combustor liner environment was determined. The utility of advanced fracture mechanics measurements will also be evaluated and determined during the course of the program.

Malik, S. N.↗

NASA NTRS1985

Constitutive modeling for isotropic materials

Constitutive theories were evaluated against a large uniaxial and multiaxial data base that was generated as part of this work. The experimental approach was to determine the constitutive behavior of Rene 80 under a multitude of conditions that are important in the design of gas turbine blades and vanes. The experimental and analytical goals of this program were successfully accomplished. A new multiaxial constitutive model which can represent the complex nonlinear high temperature behavior of Rene 80 was developed. The model was extensively verified on data at several temperatures.

Ramaswamy, V. G.↗

NASA NTRS1985

Elevated temperature crack growth

The purpose is to determine the ability of currently available P-I integrals to correlate fatigue crack propagation under conditions that simulate the turbojet engine combustor liner environment. The utility of advanced fracture mechanics measurements will also be evaluated during the course of the program. To date, an appropriate specimen design, a crack displacement measurement method, and boundary condition simulation in the computational model of the specimen were achieved. Alloy 718 was selected as an analog material based on its ability to simulate high temperature behavior at lower temperatures. Tensile and cyclic tests were run at several strain rates so that an appropriate constitutive model could be developed. Suitable P-I integrals were programmed into a finite element post-processor for eventual comparison with experimental data.

Malik, S. N.↗

NASA NTRS1985

Elevated temperature crack growth

The objective of the Elevated Temperature Crack Growth Project is to evaluate proposed nonlinear fracture mechanics methods for application to combustor liners of aircraft gas turbine engines. During the first year of this program, proposed path-independent (P-I) integrals were reviewed for such applications. Several P-I integrals were implemented into a finite-element postprocessor which was developed and verified as part of the work. Alloy 718 was selected as the analog material for use in the forthcoming experimental work. A buttonhead, single-edge notch specimen was designed and verified for use in elevated-temperature strain control testing with significant inelastic strains. A crack mouth opening displacement measurement device was developed for further use.

Yau, J. F.↗

NASA NTRS1985

Constitutive modeling for isotropic materials

The first year of progress on a NASA-Lewis contract with the General Electric Co is documented. The purpose of this contract (NAS3-23927) is to develop and evaluate unified constitutive equations for applications to hot-path components of aircraft gas turbine engines such as high pressure turbine blades and vanes. To accomplish this goal, uniaxial, notched, and multiaxial specimens made of conventionally cast Rene 80 are being tested under conditions that simulate engine operating conditions. To reduce the raw data, automated data reduction techniques are being developed that produce computer files containing the information needed to analyze proposed constitutive theories. Described are the analytical methods being developed to determine the parameters for these nonlinear unified theories by using the reduced data files. In another activity, a dedicated finite-element computer code is being developed to use unified theories in the structural analysis of hot-section components. This code was extensively verified for one such theory by successfully predicting the strain histories measured experimentally at the notch root of complex specimens taken from complex laboratory specimens.

Ramaswamy, V. G.↗

NASA NTRS1984

Constitutive modeling for isotropic materials

The unified constitutive theories for application to typical isotropic cast nickel base supperalloys used for air-cooled turbine blades were evaluated. The specific modeling aspects evaluated were: uniaxial, monotonic, cyclic, creep, relaxation, multiaxial, notch, and thermomechanical behavior. Further development of the constitutive theories to model thermal history effects, refinement of the material test procedures, evaluation of coating effects, and verification of the models in an alternate material will be accomplished in a follow-on for this base program.

Ramaswamy, V. G.↗

NASA NTRS1984

Elevated temperature crack growth

Critical gas turbine engine hot section components such as blades, vanes, and combustor liners tend to develop minute cracks during early stages of operations. The ability of currently available path-independent (P-I) integrals to correlate fatigue crack propagation under conditions that simulate the turbojet engine combustor liner environment was determined. To date, an appropriate specimen design and a crack displacement measurement method were determined. Alloy 718 was selected as the analog material based on its ability to simulate high temperature behavior at lower temperatures in order to facilitate experimental measurements. Available P-I integrals were reviewed and the best approaches are being programmed into a finite element post processor for eventual comparison with experimental data. The experimental data will include cyclic crack growth tests under thermomechanical conditions, and, additionally, thermal gradients.

Kim, K. S.↗

NASA NTRS1977

The influence of composition, annealing treatment, and texture on the fracture toughness of Ti-5Al-2.5Sn plate at cryogenic temperatures

The plane strain fracture toughness K sub Ic and conventional tensile properties of two commercially produced one-inch thick Ti-5Al-2.5Sn plates were determined at cryogenic temperatures. One plate was extra-low interstitial (ELI) grade, the other normal interstitial. Portions of each plate were mill annealed at 1088 K (1500 F) followed by either air cooling or furnace cooling. The tensile properties, flow curves, and K sub Ic of these plates were determined at 295 K (room temperature), 77 K (liquid nitrogen temperature), and 20 K (liquid hydrogen temperature).

Vanstone, R. H.↗

NASA NTRS1977

Investigation of the fracture mechanism in Ti-5Al-2.5Sn at cryogenic temperatures

The influence of microstructure on the fracture mechanism and plane-strain fracture toughness of Ti-5Al-2.5Sn was studied through the use of fractography and metallographic sectioning techniques. One-inch thick plates of extra low interstitial (ELI) and normal interstitial Ti-5Al-2.5Sn were mill annealed at 815 C followed by either air or furnace cooling. These variations in composition and cooling rate resulted in differences in the volume fraction and internal structure of the iron-stabilized phase, and in the crystallographic texture and ordering of the alpha matrix. The tensile properties of these plates were determined at 20 K, 77 K, and 295 K. The air-cooled ELI plate was the toughest material evaluated.

Vanstone, R. H.↗

NASA NTRS1974

The effect of microstructure on the fracture toughness of titanium alloys

The microstructure of the alpha titanium alloy Ti-5Al-2.5Sn and the metastable beta titanium alloy Beta 3 was examined. The material was from normal and extra low interstitial grade plates which were either air-cooled or furnace-cooled from an annealing treatment. Beta 3 was studied in alpha-aged and omega-aged plates which were heat treated to similar strength levels. Tensile and plane strain fracture toughness tests were conducted at room temperature on the alpha-aged material. The microstructure and fracture mechanisms of alloys were studied using optical metallography, electron microscopy, microprobe analyses, and texture pole figures. Future experiments are described.

Vanstone, R. H.↗

NASA NTRS1973

The effect of microstructure on the fracture toughness of titanium alloys

The high-strength titanium alloys are widely used in aircraft and aerospace structures due to their high strength to density ratios. In such applications, the fracture toughness rather than the strength is often the factor which requires larger size sections and lower useful payloads. The response of the strength and toughness of titanium alloys was analyzed generally without regard to the fracture mode or the effect of microstructure on the fracture mechanisms. Research on the fracture mechanisms in aluminum alloys and steels showed that the toughness may be improved by decreasing the sizes of inclusions and sub-micron precipitates. An investigation was conducted to study the fracture mechanisms in titanium alloys which may lead to suggestions for the improvement of the fracture toughness without a corresponding loss in strength.

Vanstone, R. H.↗