Engineering topics
Publications and source records attributed to Vannorman, John D..
A catalyst for the combination of CO and O2 to form CO2 which includes a platinum group metal, e.g., platinum; a reducible metal oxide having mulitple valence states, e.g., SnO2; and a compound which can bind water to its structure, e.g., silica gel. This catalyst is ideally suited for application to high powered, pulsed, CO2 lasers operating in a sealed or closed cycle condition.
Noble-metal/tin-oxide based catalysts such as Pt/SnO2 have been shown to be good catalysts for the efficient oxidation of CO at or near room temperature. These catalysts require a reductive pretreatment and traces of hydrogen or water to exhibit their full activity. Addition of Palladium enhances the activity of these catalysts with about 15 to 20 percent Pt, 4 percent Pd, and the balance SnO2 being an optimum composition. Unfortunately, these catalysts presently exhibit significant decay due in part to CO2 retention, probably as a bicarbonate. Research on minimizing the decay in activity of these catalysts is currently in progress. A proposed mechanism of CO oxidation on Pt/SnO2-based catalysts has been developed and is discussed.
CO oxidation catalysts with high activity at 25 C to 100 C are important for long-life, closed-cycle operation of pulsed CO2 lasers. A reductive pretreatment with either CO or H2 has been shown to significantly enhance the activity of a commercially available platinum on tin (IV) oxide (Pt/SnO2) catalyst relative to an oxidative or inert pretreatment or no pretreatment. Pretreatment at temperatures of 175 C and above causes an initial dip in the observed CO2 yield before the steady-state yield is attained. This dip has been found to be caused by dehydration of the catalyst during pretreatment and is readily eliminated by humidifying the catalyst or the reaction gas mixture. It is hypothesized that the effect of humidification is to increase the concentration of OH groups on the catalyst surface which play a role in the reaction mechanism.
The low temperature CO oxidation catalysts that are being developed and tested at NASA-Langley are fairly unique in their ability to efficiently oxidize CO at low temperatures (approx. 303 K). The bulk of the reaction data that has been collected in the laboratory has been determined using plug flow reactors with a low mass of Pt/SnO2/SiO2 catalyst (approx. 0.1 g) and a modest flow rate (5 to 10 sc sm). The researchers have previously characterized the surface solely in terms of N2 BET surface areas. These surface areas have not been that indicative of reaction rate. Indeed, some of the formulations with high BET surface area have yielded lower reaction rates than those with lower BET surface areas. As a result researchers began a program of determining the chemisorption of the various species involved in the reaction; CO, O2 and CO2. Such a determination of will lead to a better understanding of the mechanism and overall kinetics of the reaction. The pulsed-reactor technique, initially described by Freel, is used to determine the amount of a particular molecule that is adsorbed on the catalyst. Since there is some reaction of CO with the surface to produce CO2, the pulsed reactor had to be coupled with a gas chromatograph in order to distinguish between the loss of CO that is due to adsorption by the surface and the loss that is due to reaction with the surface.
A catalyst is disclosed for the combination of CO and O2 to form CO2, which includes a platinum group metal (e.g., platinum); a reducable metal oxide having multiple valence states (e.g., SnO2); and a compound which can bind water to its structure (e.g., silica gel). This catalyst is ideally suited for application to high-powered pulsed, CO2 lasers operating in a sealed or closed-cycle condition.
CO oxidation catalysts with high activity at 25 to 100 C are important for long life, closed cycle operation of pulsed CO2 lasers. A reductive pretreatment with either CO or H2 was shown to significantly enhance the activity of a commercially available platinum on tin (IV) oxide (Pt/SnO2) catalyst relative to an oxidative or inert pretreatment of no pretreatment. Pretreatment at temperatures of 175 C and above causes an initial dip in the observed CO2 yield before the steady state yield is attained. This dip was found to be caused by dehydration of the catalyst during pretreatment and is readily eliminated by humidifying the catalyst or the reaction gas mixture. It is hypothesized that the effect of humidification is to increase the concentration of OH groups on the catalyst surface which play a role in the reaction mechanism.
CO oxidation catalysts with high activity in the range of 25 C to 100 C are important for long-life, closed-cycle operation of pulsed carbon dioxide 2 lasers. A reductive pretreatment with either CO or H sub 2 was shown to significantly enhance the activity of a commerically-available platinum on tin (IV) oxide (Pt/SnO2) catalyst relative to an oxidative or inert pretreatment or no pretreatment. Pretreatment at temperatures of 175 C and above caused an initial dip in observed CO or O sub 2 loss or CO sub 2 formation in a test gas mixture of 1 percent CO and 0.5 percent O sub 2 in a He gas matrix before a steady-state yield was obtained. This dip was found to be caused by dehydration of the surface of the catalyst and was readily eliminated by humidifying the catalyst or the test gas mixture. It was also found that too much moisture resulted in a lower overall yield of CO sub 2. Under similar conditions, it is hypothesized that the effect of the humidification is to increase the concentration of OH groups on the surface of the catalyst. The effect of having high concentration of CO sub 2 in the test gas mixture upon the loss of CO and O sub 2 as well as the effect of periods of relaxation of the catalyst under non-test gas conditions was studied. The purpose of these studies was to gain an insight into the mechanism of CO oxidation on this type of catalyst.
Mass spectrometry was used to measure oxygen and nitrogen permeabilities while polarography was used to measure oxygen permeabilities for several contact lens materials. Applicable sample holders were designed and fabricated to accommodate curved and flat specimens. A prepared standard was used to calibrate the mass spectrometric analyses. The oxygen permeability values determined by mass spectrometry were significantly greater than those determined by polarography. This was attributed to the phase boundary phenomena and the limiting oxygen permeance of water inherent in the polarographic technique. Polarographic values determined were in good agreement with proprietary values obtained by polarography, with the exception of one material.