Engineering topics
Publications and source records attributed to Vanaphuti, Panawan.
A novel precursor phase (Mn, Fe) 5 (PO 4 ) 2 (HPO 4 ) 2 ·4H 2 O is introduced with a co-precipitation reaction, enabling a low-cost, sustainable, scalable production of LMFP cathodes exhibiting excellent cycling stability with good tap density.
Solid-state sodium-metal batteries assembled with a composite solid-electrolyte separator and Na 0.72 Li 0.24 Mn 0.75 Si 0.01 O 2 cathode, utilizing reversible cationic (Mn) and anionic (O) redox, achieve high initial specific capacity of 180 mA h g −1 .
A recycling and synthesis of charge material for secondary batteries generates single-crystal charge materials for producing batteries with greater charge cycle longevity. Charge material particles undergo a heating for fusing or enhancing grain boundaries between polycrystalline particles. The resulting, more well-defined grain boundaries are easily etched by a relatively weak mineral acid solution. The acid solution removes material at the grain boundaries to separate secondary particles into primary particles along the grain boundaries. The resulting single crystal (monocrystalline) charge material particles are washed and filtered, and typically re-sintered to accommodate any needed lithium (lithium carbonate), and result in a charge material with larger surface area, higher lithium diffusivity and lower cation ordering.
The ever-growing demand for low-cost, high-energy-density lithium-ion batteries (LIBs) makes high-nickel layered oxide cathodes, especially LiNiO 2 (LNO), one of the most appealing candidates. However, poor structural and surface instability that leads to a short cycle life remains a formidable challenge. Herein, a systematic investigation of LNO performance in two different electrolytes (a conventional carbonate-based LP57 electrolyte and an ether-based localized high-concentration electrolyte (LHCE)) with different charge cut-off voltages is presented. These findings show that the cathode-electrolyte reactivity is the main factor dictating the performance degradation of LNO at high voltages rather than bulk integrity. While LHCE can provide good stability beyond 4.2 V with a robust, uniform solid–electrolyte interphase (SEI) layer on the Li-metal anode, there is no significant difference in cyclability at 4.15 V (96% capacity retention after 200 cycles) for both LP57 and LHCE. From LNO symmetric cells, carbonate-based electrolyte is found to be good for LNO stability while ether-based electrolyte is beneficial toward Li-metal anode. Furthermore, a suitable electrolyte or a low cut-off voltage is necessary to maintain a decent cycle life. Altogether, this work highlights the impact of electrolyte and cut-off voltage on LNO and Li-metal, which can help guide the development of cells based on LNO.
Here, with the limited resources and high cost of lithium-ion batteries (LIBs) and the ever-increasing market demands, sodium-ion batteries (SIBs) gain much interest due to their economical sustainability, and similar chemistry and manufacturing processes to LIBs. As cathodes play a vital role in determining the energy density of SIBs, Mn-based layered oxides are promising cathodes due to their low cost, environmental friendliness, and high theoretical capacity. However, the main challenge is structural instability upon cycling at high voltage. Herein, Mg is introduced into the P2-type Na 0.62 Ni 0.25 Mn 0.75 O 2 cathode to enhance electrochemical stability. By combining electrochemical testing and material characterizations, it is found that substituting 10 mol% Mg can effectively alleviate the P2–O2 phase transition, Jahn-Teller distortion, and irreversible oxygen redox. Moreover, structural integrity is greatly improved. These lead to enhanced electrochemical performances. With the optimized sample, a remarkable capacity retention of 92% in the half cell after 100 cycles and 95% in the full cell after 170 cycles can be achieved. Altogether, this work provides an alternative way to stabilize P2-type Mn-based layer oxide cathodes, which in turn, put forward the development of this material for the next-generation SIBs.