Steady-shear rheology showing evolution of the microstructure of iridium oxide catalyst inks of PEM water electrolyzers with aging time.
A major factor driving fuel cell costs is the quantity of precious metal required. Therefore, it is important to understand a timeframe where inks can be reused. Here, in this work, we explore differences between a freshly prepared catalyst ink and one that has been stored for over a year – comparing ink properties, cathode catalyst layer microstructure, and their respective fuel cell performance. Ink studies revealed smaller agglomerate sizes and a decrease in shear viscosity for the aged ink. Longer storage time also results in fewer cracks and a more uniform ionomer distribution, as evidenced by microscopy characterization of rod-coated electrodes. Lastly, polarization curves show improved performance at higher current densities for the electrode prepared from the aged ink. We rationalize such effect in terms of enhanced ionomer adsorption onto the catalyst over time.
Image processing is a powerful tool that allows for rapid and automated data parsing in settings that occupy large variable spaces and require large data sets. Feature detection on difficultly discerned backgrounds is a subset of image processing that facilitates the extraction of quantitative metrics from otherwise subjective data. Crack detection and quantification is an important capability in polymer electrolyte membrane fuel cell quality control, failure analysis, and optimization. This work presents a technique to perform crack detection and quantification which overcomes challenges faced by commonly used image segmentation techniques. We demonstrate the use of a geometrically filtered noise‐level detection technique to select a binary threshold value from which we then quantify how cracked a sample is. Furthermore, we demonstrate the accuracy of our technique using programmatically generated test images of known crack amounts and their performance on real‐world fuel cell catalyst layer samples.
This work investigates the influence of ballmilling (sometimes also referred to as jar roller milling) time on cathode catalyst layer (CL) inks and electrode properties using formulations and coating methods relevant for industrial manufacturing. Four CL inks with the same composition were milled for 24, 48, 72, or 96 h. Rheological investigation of these inks showed a reduction of elastic moduli and steady-shear viscosity with continuous ink milling, which is correlated to a decrease in particle-particle interactions as well as formation of smaller agglomerates. Optical microscopy (OM) analysis of the fabricated electrodes revealed a trend in surface crack formation; formulations milled for 24 h contained the lowest average surface crack area percentages of 0.370% at heavy-duty loadings of ~0.300 mg Pt cm -2 , compared to 2.418% for the ink milled for 96 h. Further characterization of the CL through transmission electron microscopy (TEM) imaging showed a decrease in the mean agglomerate and pore size with milling time. Furthermore, these smaller electrode features were consistent with reduced fracture resistance and, hence, development of larger stresses during drying. Our results highlight the need to consider ink processing as an important component in defect-free CL manufacturing.
Not Available
Abstract We investigate the effect of alcohol fraction (isopropanol, IPA) in a binary water‐alcohol solvent mixture on the shear and extensional rheological properties, as well as the role of viscoelasticity on fiber formation of poly(acrylic acid) (PAA) in electrospinning. Comparison of the scaling of both specific viscosities η sp and extensional relaxation times λ E of PAA in water–IPA mixtures, showed stronger scaling compared to salt‐free aqueous polyelectrolyte solutions, except for the η sp in the unentangled regime displaying a polyelectrolyte‐like scaling η sp ~ c 0.5 for all IPA%. Such deviation suggested IPA induces association/aggregation of PAA. However, the trends between η sp and λ E magnitudes as a function of IPA% differ for concentrations compared in the entangled regime. The η sp as well as their elastic moduli exhibit a maximum, whereas λ E increases monotonically with IPA%, suggesting a complex interplay of various interactions are dictating their structure in water‐IPA mixtures, affecting their shear and extensional response differently. Electrospinning experiments showed increasing IPA% reduces the onset of both beaded and uniform fibers. Analysis using dimensionless numbers indicated the enhancement of their elasticity by IPA, and the consequent stabilizing effect on their jets/filaments against break‐up during electrospinning, plays a role in the improvement of their fiber formation.
Here this work reports the characterization of catalyst layer (CL) structure and composition for a set of gas-diffusion electrodes (GDEs) fabricated by different coating methods with the goal of developing a better understanding of CL processing-structure-property-performance relationships. The CL coating techniques used in this study were ultrasonic spray coating, and two roll-to-roll (R2R) methods - gravure and slot die. Scanning transmission electron microscopy (STEM) coupled with X-ray energy dispersive spectroscopy (EDS) analysis of GDE cross-sections provided bulk information, while scanning electron microscopy (SEM) with EDS and X-ray photoelectron spectroscopy (XPS) were used to investigate the near surface and surface composition of the CLs that will be in direct contact with the membrane once the membrane electrode assembly (MEA) is constructed. This study demonstrates that common quantification parameters, namely the F:Pt ratio extracted from cross-sectional STEM-EDS maps and top-down CL measurements with SEM and XPS, along with roughness parameters quantified from SEM micrographs are useful parameters in explaining and potentially predicting performance trends. Additionally, it highlights the importance of understanding key CL surface properties for advancing the manufacturability of high-performance components for polymer electrolyte membrane (PEM) technologies.
Here, we present a study of mid-infrared (mid-IR) transmission through typical proton-exchange fuel cell and water electrolyzer catalyst-coated membrane materials, and the determination of membrane layer thickness, and catalyst layer loading, from the power of the transmitted beam. Measured membrane thicknesses lay in the range of 25-125 um, and catalyst areal loadings range from 0.05 to 0.35 mg/cm 2 . We show that the transmission spectrum correlated to membrane thickness and catalyst loading values separately, and also used a mathematical model to calculate both quantities simultaneously, from a single measurement of transmission. Measurements were carried out using a Fourier-transform infrared (FTIR) spectrometer, in specular transmission mode, in the wavelength range of 3-13 um (3333-770 cm -1 ). We discuss the potential application of this method to the development of roll-to-roll manufacturing full-area-scanning quality inspection of catalyst-coated membrane (CCM) materials.
R2R processing is used to manufacture a wide range of products for various applications which span many industrial business sectors. The overall R2R methodology has been in use for decades and this continuous technique traditionally involves deposition of material(s) onto substrates or membranes that are on moving webs, carriers or other continuous belt-fed or conveyor-based processes that enable successive steps to build a final product. Established methods that typify R2R processing include tape casting, silk-screen printing, reel-to-reel vacuum deposition/coating, and R2R lithography. Products supported by R2R manufacturing include micro-electronics, electro-chromic window films, PVs, fuel cells for energy conversion, battery electrodes and electrolytes for energy storage, and barrier and membrane materials for decarbonization and air and water filtration. Due to innovation in materials and process equipment, high-quality yet very low-cost multilayer technologies have the potential to be manufactured on a very cost-competitive basis. To move energy-related products from high-cost niche applications to the commercial sector, the means must be available to enable manufacture of these products in a cost-competitive manner. Fortunately, products such as fuel cells, thin- and mid-film PVs, batteries, electrochromic and piezoelectric films, water separation membranes, and other energy saving technologies readily lend themselves to manufacture using R2R approaches. However, more early-stage research is needed to solve the challenge of linking the materials (particles, polymers, solvents, additives) used in ink and slurry formulations and the coating and heated drying processes to the ultimate performance of the final R2R product, especially for a process that uses multiple layers of deposition to achieve the end product.
As the production of polymer electrolyte fuel cells expands, novel quality control methods must be invented or adapted in order to support expected rates of production. Ensuring the quality of deposited catalyst layers is an essential step in the fuel cell manufacturing process, as the efficiency of a fuel cell is reliant on the catalyst layer being uniform at both the target platinum loading and the target ionomer content. Implementing a quality control method that is sensitive to these aspects is imperative, as wasting precious metals and other catalyst materials is expensive, and represents a potential barrier to entry into the field for manufacturers experimenting with novel deposition processes. In this work, we analyzed catalyst inks to determine if their ionomer content could be quantized spectroscopically. Attenuated total reflection (ATR) Fourier transform infrared spectroscopic technique was investigated producing a signal proportional to the ionomer content. ATR spectroscopy was able to quantitatively differentiate samples in which the ionomer to carbon mass ratio (I/C) varied between 0.9 and 3.0. The I/C ratio was correlated to the measured ATR signal near the CF 2 vibrational bands located between 1100 cm −1 and 1400 cm −1 . The experimental results obtained constitute a step toward the development of novel quality control methodologies for catalyst inks utilized by the fuel cell industry.
Quality control (QC) for both polymer electrolyte membrane fuel cell and electrolysis membrane electrode assembly (MEA) materials is a key challenge for scale-up and cost reduction. Developing methods for detecting defects, as well as measuring critical material properties and understanding the impact of as-manufactured variations in these materials on cell performance and lifetime, are critical barriers. To help address these needs, the National Research Council Canada (NRC), Fraunhofer Institute for Solar Energy Systems (ISE), and the National Renewable Energy Laboratory (NREL) have organized and facilitated a series of workshops on the topic, bringing together industry, academia, and research institutions from North America and Europe. Prior workshops in Canada and Germany have focused on the status of quality tool capabilities and identification of needed developments for fuel cells. These meetings have garnered an excellent response and follow-on attendance, with over 100 unique attendees.
Explore the source record for details and available documents.
This project was focused on developing the durable, high-performance materials and interfaces for advanced water splitting, enabling a clear pathway for achieving <$2/Kg H2 (on scale) with efficiency of 43 kWh/kg H 2 via anion exchange membrane (AEM)-based electrolysis. We aimed to advance these final goals via an improved fundamental understanding of both hydrogen and oxygen evolution reactions (HER/OER) leading to novel platinum group metal (PGM)-free catalyst materials in conjunction with critical improvements in membrane and ionomers and gas evolution electrodes with corresponding characterization and testing. Northeastern University (NU) lead this effort focusing on catalyst development and characterization (both in situ and ex situ) while project partners lead improvements in ionomer and membrane materials and will aid in the development of specialized electrode and membrane electrode assemblies. In addition, close collaboration occured with the HydroGEN Energy Materials Network (EMN) National Laboratory consortium including efforts related to use of advanced ionomers, durability protocols and validation of electrolyzer materials (e.g. NREL), multiscale modeling and computation (e.g. LBNL), and molecular dynamics (MD) simulations of the membrane catalyst interface (e.g. SNL). The interactions with HydroGEN included exchange of data and materials as needed to facilitate project success.