Composites From in-Situ Consolidation Automated Fiber Placement of Thermoplastics for High-Rate Aircraft Manufacturing

The National Aeronautics and Space Administration (NASA) project Hi-Rate Composites Aircraft Manufacturing (HiCAM) aims to significantly increase commercial aircraft composite structures manufacturing rate. Thermoplastic composites offer attractive solutions to rapid manufacturing due to their ability to be formed and consolidated quickly. NASA has a particular interest in assessing composite structure manufacturing utilizing an in-situ consolidation automated fiber placement (AFP) of thermoplastics (ICAT) process employing current state-of-the-art laser heating systems. Three semi-crystalline polyaryletherketone (PAEK) thermoplastic tape materials were characterized to ascertain the ICAT process parameters. The required laser power settings were determined at Electroimpact, Inc., measuring material temperatures utilizing a forward looking infrared (FLIR) thermal imaging camera and thermocouples. The material temperature, tool temperature, and placement speed were varied for resulting consolidation quality assessment. The resulting temperature data were also utilized to calibrate thermal analysis models under development at NASA. The experimental temperature data confirmed analytical results. The quality of the resulting test panels was evaluated by both non-destructive evaluation as well as destructively by photo-microscopy. The effect on interlaminar strength was determined by short beam strength testing. Test results of carbon fiber laminates fabricated by ICAT using polyetheretherketone (PEEK), polyetherketoneketone (PEKK), and low-melt polyaryletherketone (LM-PAEK) at various placement temperatures and placement speeds are presented.

thermoplastic composites↗

NASA NTRSDate not supplied

Laser Angle of Incidence Effects on in-Situ Consolidation of Automated Fiber Placement of Polyaryletherketone Composites

NASA and Electroimpact, Inc. ® in conjunction with other U.S. industry partners are performing research as a part of the NASA High-rate Composites for Aircraft Manufacturing (HiCAM) Project to fabricate thermoplastic panels using automated fiber placement (AFP) to increase manufacturing rates of aircraft structural composites. This work focuses on evaluating the in-situ consolidation AFP of thermoplastics (ICAT) process. Previous studies of the ICAT process using semi-crystalline, polyaryletherketone (PAEK) slit-tape have resulted in an adequate degree of intimate contact between plies; however, the resulting interlaminar strength have been less than laminates fabricated in an autoclave. To improve these properties, the effect of reducing the laser angle of incidence (AoI) during placement to increase the degree of auto-hesion was evaluated. The AoI of the laser assisted AFP head was varied between 12° and 16° to fabricate multiple quasi-isotropic and unidirectional test panels. Physics-based thermal models developed at the NASA Langley Research Center were utilized to predict the temperature profile. Laminate processing temperature was measured experimentally, and panel quality was evaluated by both non-destructive evaluation (NDE) as well as destructively by photo-microscopy. The effect on interlaminar strength was determined by short beam strength testing. Test results of carbon fiber laminates fabricated by ICAT using polyetheretherketone (PEEK), polyetherketoneketone (PEKK), and low-melt polyaryletherketone (LM-PAEK) at various laser angles of incidence, placement temperatures and placement speeds are presented.

Thermoplastic Composites↗

NASA NTRSDate not supplied

Detection and Localization of a Fold, Twist, and Overlaps within Tow-Steered Composite Panels During Autoclave Cure

Because of the anisotropic properties of carbon fiber reinforced polymer (CRFP) composites, novel layup architectures, such as tow-steering, can be used to tailor mechanical properties of the composite structure to the loading condition during use. In this work, a tow-steered composite panel was de-signed, laid up using the Integrated Structural Assembly of Advanced Com-posites (ISAAC) automated fiber placement (AFP) machine located at the NASA Langley Research Center (LaRC), and cured while simultaneously be-ing inspected using an ultrasonic inspection system operating inside the auto-clave. The composite panel contained overlaps that are intrinsic to the tow-steered design and had intentionally introduced layup defects including folds, wrinkles, splices, tow twists, foreign object debris (FOD), gaps, and additional overlaps. The inspections during the cure cycle focused on the ar-ea within the laminate containing a fold, a twist, and intrinsic overlaps. The ultrasonic inspections performed during the cure cycle were analyzed and compared to post-cure ultrasonic inspections of the entire laminate.

Composites↗

NASA NTRSDate not supplied

Detection and Localization of a Fold, Twist, and Overlaps within Tow-Steered Composite Panels During Autoclave Cure

Because of the anisotropic properties of carbon fiber reinforced polymer (CRFP) composites, novel layup architectures, such as tow-steering, can be used to tailor mechanical properties of the composite structure to the loading condition during use. In this work, a tow-steered composite panel was de-signed, laid up using the Integrated Structural Assembly of Advanced Com-posites (ISAAC) automated fiber placement (AFP) machine located at the NASA Langley Research Center (LaRC), and cured while simultaneously be-ing inspected using an ultrasonic inspection system operating inside the auto-clave. The composite panel contained overlaps that are intrinsic to the tow-steered design and had intentionally introduced layup defects including folds, wrinkles, splices, tow twists, foreign object debris (FOD), gaps, and additional overlaps. The inspections during the cure cycle focused on the ar-ea within the laminate containing a fold, a twist, and intrinsic overlaps. The ultrasonic inspections performed during the cure cycle were analyzed and compared to post-cure ultrasonic inspections of the entire laminate.

Composites↗