Area-based composition predictions of materials fabricated using simultaneous wire-powder-directed energy deposition

Functionally graded materials are an emergent method for designing components with programmable site-specific material properties. These materials are typically fabricated using metal additive manufacturing tools by simultaneously feeding multiple wire and/or powder feedstocks at various rates to achieve spatial composition change. The wire-powder-directed energy deposition (WP-DED) technique is of particular interest for many functionally graded material applications by balancing the low raw materials cost of wire with the high resolution of powder. However, feeding wire and powder are inherently different processes since all extruded wire enters the melt pool, while much of the blown powder is scattered, which makes determining the composition of the build challenging. In this study, we devise a simple area-based measurement method for estimating the composition of WP-DED structures. WP-DED single beads are printed using 309L stainless steel wire and commercially pure Fe powder at five wire feed rates (0.5, 0.75, 1.00, 1.25, 1.50 mm/mm) and five powder feed rates (2, 4, 6, 8, 10 rpm). Characteristic defects including interface gaps and macrosegregation (lack of mixing) tendencies are examined. High powder feed rates (8, 10 rpm) result in interface gaps at all wire feed rates, but smooth deposition and complete mixing is achieved at low powder feed rates, particularly with lower wire feed rates as well. The area-based composition measurement method is within ±20% of energy dispersive x-ray spectroscopy measurements for all samples, showing its effectiveness as a rapid composition estimate for WP-DED materials development.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Measurement of G-phase volume fraction and number density in duplex stainless steels using transmission electron microscopy

Duplex stainless steels (DSS) have a high toughness and strength due the presence of both austenitic and ferritic phases. These alloys have had limited use in power production applications due to thermal embrittlement caused by spinodal decomposition and development of G-phase precipitates in the ferrite. Lean grade DSS alloys (e.g., 2101, 2003) may offer improved thermal stability due to the reduction of Cr- and Ni-equivalent elements when compared to standard grade compositions (e.g., 2205, 2209). The abundance of the G-phase was measured in five duplex stainless steels, three wrought alloys (2101, 2003, 2205) and their matching filler metals (2101-w, 2209-w), after aging at 427 °C for 1000 h and 10,000 h. The G-phase volume fraction, number density, size, and precipitate spacing were found using quantitative analysis of transmission electron microscopy dark field images and the composition of G-phase precipitates on other clusters were characterized with atom probe tomography (APT). In the welded alloys, the G-phase was found to develop rapidly, relative to the wrought material. A positive correlation was found between the nickel equivalent composition of the alloy and the G-phase volume fraction. The alloys 2205, 2209, and 2101-w, which are higher in Cr and Ni, all showed significant G-phase precipitation, further strengthening the hypothesis that lean grade DSS alloys are more thermally stable against precipitation in the ferrite. Electron diffraction showed a secondary phase present in the 2101 wrought alloy at 10,000 h, but it was not crystallographically consistent with the G-phase; APT showed the presence of nanoclusters rich in both nickel and copper for this alloy. In conclusion, no secondary phases or clusters were found in 2003 after 10,000 h of aging, so it may be a candidate alloy for applications that require long-life times at high operating temperatures.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Corrosion Resistance of 309L Stainless Steel Claddings on Carbon Steel Produced with Wire-Fed Directed Energy Deposition

Additive manufacturing (AM) tools are capable of applying overlay austenitic stainless steel (SS) claddings to carbon steel components. The benefits of this approach over arc welding include a smaller heat-affected zone, residual stress reduction, and material savings. In particular, wire-directed energy deposition is a suitable technique because of its low material cost and high rate of production compared to other AM methods. However, metallurgical variations in composition, phase fraction, and microsegregation can potentially influence the corrosion behavior of such claddings. In this work, 309L SS is clad on carbon steel substrates and electrochemical methods are used to measure their general and pitting corrosion resistance in simulated marine environments (3.5 wt% NaCl solutions). Two-layer claddings are fabricated with four laser powers to understand the effects of bulk chemical composition, austenite/δ-ferrite phase fractions, and individual phase compositions on corrosion behavior. The two-layer claddings are compared to a single-layer cladding, wrought 304 SS, and the carbon steel substrate for a comprehensive assessment of corrosion performance. The two-layer claddings are remarkably resistant to general corrosion in the 3.5 wt% NaCl environment because of their high Cr content (21.6 wt% to 23.3 wt% Cr). The single-layer cladding exhibits localized corrosion at unmixed Fe-rich peninsulas that originate at the dissimilar metal boundary and protrude into the first cladding layer. All two-layer claddings possess higher pitting corrosion resistance than wrought 304 SS, demonstrating their effectiveness as a corrosion-resistant barrier. Here, the pitting corrosion resistance is superior for claddings made with lower laser powers, due to low dilution and greater δ-ferrite contents.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Bulk Diffusion of Cl through O Vacancies in α-Cr 2 O 3 : A Density Functional Theory Study

Many metals form passive oxides which are broken or weakened by anionic-induced degradation leading to material failure and anionic diffusion is an important step of this degradation process. The diffusion of anionic species through oxides involves a combination of diffusion along grain boundaries, cracks, and channels, as well as bulk diffusion via point defects which is the focus of this study. Using density functional theory, we study bulk diffusion of Cl through O vacancies in α -Cr 2 O 3 as a model system for passive metal oxides. Little is known about Cl diffusion and bonding characteristics, so we benchmark our work through comparison to numerous studies on O diffusion in α -Cr 2 O 3 to analyze similarities and differences between the O and Cl diffusion in the passivation and degradation process of α -Cr 2 O 3 respectively. Unlike O diffusion, the lowest diffusion barrier for Cl is cross-plane diffusion between two (0001) planes through a vacant cation site but the much shorter in-plane diffusion path within the same coordination polyhedron has 35% higher barrier. This work provides the basis for considering the contributions of Cl bulk-diffusion in the overall diffusion kinetics of Cl through α -Cr 2 O 3 .

Oware Sarfo, Kofi↗