Engineering topics

Truong, Thien

Publications and source records attributed to Truong, Thien.

4 records

DOE OSTI2025

Microwave Annealing for Fast and Effective Hydrogen Activation in Polycrystalline Silicon Passivating Contacts

Hydrogenation is a crucial step in the fabrication of high-efficiency silicon solar cells. In this study, the effectiveness of hydrogen activation is demonstrated via microwave annealing of hydrogen-rich dielectrics coated on poly-Si passivating contacts. This method is compared with conventional hydrogenation techniques, such as annealing in N2 in the presence of a hydrogen-rich source (such as hydrogenated aluminum oxide (AlOx:H), hydrogenated silicon nitride (SiNy:H), or a AlOx:H/SiNy:H stack). Key improvements observed include a reduction in J0 from 30 to <5 fA cm-2, an increase in iVoc from 690 to >730 mV, and an enhancement in effective lifetime (teff) from 0.6 to ~3.5 milliseconds on phosphorus-doped poly-Si/SiO2 passivating contact samples. With a very short annealing time of ~1-2 min, the samples passivated by AlOx:H, SiNy:H, or the stack show similar performance to samples subjected to 30 min of nitrogen annealing. Photoluminescence (PL) spectra corroborate the findings regarding the hydrogenation of the poly-Si layer and the c-Si substrate, with an increase in PL intensity after microwave annealing. Ultimately, this work suggests that microwave annealing could be a promising addition, offering flexibility to traditional firing hydrogenation processes.

hydrogenation↗

DOE OSTI2024

Effect of Iron Contamination and Polysilicon Gettering on the Performance of Polysilicon‐Based Passivating Contact Solar Cells

Over the past decade, silicon solar cells with carrier-selective passivating contacts based on polysilicon capping an ultra-thin silicon oxide (commonly known as TOPCon or POLO) have demonstrated promising efficiency potentials and are regarded as an evolutionary upgrade to the PERC (passivated emitter and rear contact) cells in manufacturing. The polysilicon-based passivating contacts also exhibit excellent gettering effects that relax the wafer and cleanroom requirements to some extent. Here, in this work, we experimentally explore the impact of bulk iron contamination and polysilicon gettering on the passivation quality of the polysilicon/oxide structure and the resulting solar cells performance. Results show that both n- and p-type polysilicon/oxide passivating contacts are not affected by iron gettering, demonstrating robust and stable passivation quality. However, for a very high bulk iron contamination (1 × 10 13 cm −3 ), the accumulated iron in the p-type lightly boron-doped emitter in crystalline silicon would degrade the emitter saturation current density. This can cause a reduction in both open-circuit voltage and short-circuit current. Meanwhile, this very high iron content (1 × 10 13 cm −3 ) can further degrade the fill factor and temperature coefficient of the cells. On the other hand, for an initial iron content of 2 × 10 12 cm −3 , which should be well above the iron level in the current industrial Czochralski silicon wafers, the resulting cells demonstrate similar performance as the control group with no intentional iron contamination. This work brings attention to both the benefits of polysilicon gettering effects as well as the potential degradation due to the accumulation of metal impurities in the p-type emitter region.

14 SOLAR ENERGY↗

DOE OSTI2024

Ultraviolet Laser Activation of Phosphorus-Doped Polysilicon Layers for Crystalline Silicon Solar Cells

In crystalline silicon photovoltaics (c-Si PV), a pulsed laser can be used as a substitute for a high-temperature furnace dopant diffusion/activation step. In contrast to furnace-based activation, lasers can be used to achieve highly localized doping with controlled dopant concentrations, useful in advanced architectures such as the interdigitated back contact (IBC) solar cell. In this study, a pulsed ultraviolet (UV) laser is utilized for phosphorus dopant activation within a low-pressure chemical vapor deposited (LPCVD) polycrystalline silicon (poly-Si) passivated contact layer. The highest implied open-circuit voltage iV oc values achieved using this approach reach 726 mV. However, this comes at the expense of high specific contact resistivities ρ c , which is attributed to a lower dopant concentration across the poly-Si(n + )/SiO x /c-Si interface. Regardless, the optimum iV oc , ρ c combination is measured at a laser fluence of 0.78 J cm -2 producing values of 712 mV and 89 mΩ-cm 2 , respectively. These values are still compatible with high-efficiency solar cell designs, underscoring the feasibility and effectiveness of this approach.

14 SOLAR ENERGY↗

DOE OSTI2024

Screen-Printed Complex Ag Inks for Si HJT Metallization

Metallization using reactive metal inks has recently attracted significant research interest due to its advantages in cost of materials and manufacturing, while still achieving performance comparable to traditional fire-through particle pastes. Here, we present for the first time the use of reactive silver (Ag) inks via industrial screen-printing and inkjet printing methods for the metallization of different Si surfaces used in tunneling oxide passivating contacts (TOPCon) and Silicon heterojunction (SHJ) solar cells. Printed Ag lines exhibit a conductivity of ~5 Mu O·cm, which is approximately 3 times that of bulk Ag (1.59 µO·cm). The printed metal has a thickness of ~0.5-1.5 Mu m, an order of magnitude smaller than the current fire-through metal finger thickness (~15 Mu m). Contact resistivity measurements of the screen-printed and inkjet-printed samples on a transparent conducting oxide (TCO) surface show a very low value of ~0.2-12 mO·cm 2. Photoluminescence images of the metallized samples demonstrate minimal surface passivation degradation compared to the non-metallized areas (?iVoc <3.5 mV). Scanning electron microscopy images (SEM) reveal the structure of the printed metals on the Si surfaces as porous but much denser than fire-through Ag by nanoparticle paste. In the final presentation, we will showcase our results of printing these reactive Ag inks on high-efficiency heterojunction and TOPCon solar cells with full-area M6 wafers. Additionally, the adhesion of these reactive Ag inks on different Si surfaces according to ASTM D3359-17, as well as the performance of solar cells after standard IEC 61215 freeze/thaw and damp heat tests, will be presented. These new metal inks show promising potential as an alternative to the currently dominant particle-based pastes, offering lower Ag consumption and lower processing temperatures without compromising performance.

heterojunction solar cells↗