Engineering Microstructure in Dry-Processed Cathodes Via Calendering

Calendering serves as a multifunctional step in dry electrode processing that not only densifies the electrode but also induces polytetrafluoroethylene (PTFE) fibrillation and reorganizes the microstructure. These coupled effects are essential for achieving electrical connectivity and sufficient cohesion, yet they also introduce trade-offs, such as active material particle fracture, pore collapse, and excessive porosity loss, that can hinder ionic transport. This research systematically maps the calendering parameter space for LiNi0.6Mn0.2Co0.2O2 (NMC622) dry cathodes with a target thickness of ∼100 µm and porosity of ∼30% by varying roll gaps, roll temperature, roll speed, and the number of passes. A practical processing window for this formulation and electrode architecture is identified that achieves sufficient PTFE fibrillation and strong interfacial contact while minimizing particle fracture and preserving the porosity required for efficient ionic transport. In particular, gradual-gap calendering with moderate per-pass compression mitigates fracture and pore collapse while still reaching the target thickness with reasonable throughput, and slower roll speeds with modest roll temperatures further reduce mechanical damage. These results provide actionable guidance for scaling NMC622-based thick dry-processed cathodes.

Park, Hyunji↗

DOE OSTI2026

High Purity and Reduced Defects Hard Carbon Synthesis for Sodium-Ion Batteries

Hard carbon (HC) is the state-of-the-art anode material for sodium-ion batteries; however, the high-temperature carbonization of precursors (>1100 °C) often introduces inorganic impurities, an issue that remains largely underexplored. Here, we report a simple synthesis strategy for producing high purity HC by carbonizing a cellulose-derived precursor at 1400 °C under a slightly reducing Ar–H2 atmosphere on a graphite substrate, thereby eliminating the aluminum contamination observed during conventional carbonization on an alumina substrate under Ar. In addition, the modified synthetic condition reduces surface defects and the concentration of oxygen-containing functional groups, thereby altering the interphase formation on the HC surface. At a current density of 20 mA g−1, the impurity-rich HC exhibited an initial coulombic efficiency (ICE) of 74.1% and a reversible capacity of 248.8 mAh g−1. In sharp contrast, the high purity HC delivered a significantly improved ICE of 90.1% and a reversible capacity of 345.1 mAh g−1. These results underscore the critical importance of impurity and defect control during HC synthesis and highlight the clear electrochemical advantages of high purity HC with reduced defects for sodium-ion battery anodes.

Harshita, Lohanni↗