5 records

DOE OSTI2024

Material characterization of seven photovoltaic backsheets using seven accelerated test conditions

A variety of polymeric backsheet materials can be found in fielded photovoltaic (PV) modules, mostly based on fluoropolymer and polyethylene terephthalate (PET) materials. Cost reduction and sustainability considerations drive the recent development of alternative backsheet materials and designs [1]. In some fielded PV installations, polymeric materials are susceptible to environmental degradation in the form of backsheet cracking. To prevent backsheet degradation that can result in a module failure, thorough laboratory reliability testing is needed. In this report we studied the durability of seven commercial and experimental PV backsheets through accelerated stress testing using seven photolytic, hygrometric, and custom tests with the goal to understand if novel fluoropolymer-free backsheets are sufficiently environmentally durable to be commercialized. We divided the mechanisms observed during aging into two categories: core degradation and surface degradation. Although core degradation due to hydrolysis was observed in all commercial PET-, and polyamide (PA)-based backsheets aged with 85 degrees C/85% relative humidity, this test is unlikely to be field relevant. Photo-oxidative reactions on the exposed surface during UV weathering affected all seven backsheets regardless of the outer layer polymer material and additives. This degradation was limited to the outermost micrometers of the surface, except for backsheets containing PA-12, which resulted in surface cracking. A custom test combining UV with water spray caused the most severe backsheet degradation, including surface erosion and loss of insulating properties in polyolefin (PO)- and PA-based backsheets. This highlights the importance of combined accelerated stress testing to screen for complex backsheet degradation mechanisms. We also showed that, with material and design optimization, coextruded experimental PO-based backsheets have the potential to be a durable alternative to commercial PET- and fluoropolymer-based PV backsheets.

14 SOLAR ENERGY↗

DOE OSTI2022

Arrhenius Analysis of the Degradation Modes in Emerging Photovoltaic Backsheets

With increasingly large-scale deployments of photovoltaic (PV) modules to meet global energy demands, interest in better establishing modules' lifespans is growing. We report on the performance of co-extruded polyolefin- (PO)-based backsheets as environmentally friendly alternatives to fluoropolymer-reinforced polyethylene-terephthalate (PET)-based backsheets using three hygrometric accelerated test conditions. After completing cumulative 4000 hours of aging, we analyzed data from electrical performance (I-V), surface roughness (gloss), and appearance (L, a*, b* color) characterizations to quantify degradation rates, quantify the corresponding activation energy, and cross-correlate between the characteristics examined, thereby providing insights into the relationship between physical characteristics and operating performance.

BackFLIP↗

DOE OSTI2022

Arrhenius Analysis of the Degradation Modes in BackFLIP Study of Emerging Photovoltaic Backsheets: Preprint

With increasingly large-scale deployments of photovoltaic (PV) modules to meet global energy demands, interest in better establishing module lifespans is growing. We report on the performance of co-extruded polyolefin- (PO) based backsheets as environmentally friendly alternatives to fluoropolymer-reinforced polyethylene-terephthalate- (PET)-based backsheets using three hygrometric accelerated test conditions. After completing 4000 cumulative hours of aging, we analyzed data from electrical performance (I-V), surface roughness (gloss), and appearance (L, a*, b* color) characterizations are analyzed to quantify degradation rates, quantify the corresponding activation energy, and cross-correlate between the characteristics examined, thereby providing insights into the relationship between physical characteristics and operating performance.

BackFLIP↗

DOE OSTI2021

Thermomechanical and sequential stress performance of photovoltaic backsheets

Photovoltaic backsheet technology is utilized to protect the interior components of solar modules from environmental stress as well as provide electrical insulation to the module. The growing demand for solar energy and longer module service life requirements have brought backsheet performance into focus. Despite being a protective packaging material, many backsheets have exhibited failure in the field, limiting the performance and service life of entire modules. Most backsheets consist of multiple polymeric layers laminated together using adhesives. A new backsheet, with a high performance polyamide structure, has been developed as the solution to module failure. Primarily, it contains a unique polyamide-ionomer alloy targeted at improved weather resistance. In this study, several photovoltaic industry standard backsheets, and the novel polyamide compositions of multilayered backsheets fabricated from the coextrusion process, were examined using thermomechanical analysis (TMA). The coefficient of thermal expansion (CTE) for entire backsheets and their constituent layers was used to model the thermomechanical behavior of various backsheet constructions. Subsequently, thermal cycling was performed in the TMA to examine the intrinsic thermal behavior of the backsheets. Thermal cycling in the TMA indicates the resilience and dimensional stability in the coextruded structures as opposed to the laminated structures. Lastly, results from a Module Accelerated Sequential Testing (MAST), are included to show the mechanical integrity of these backsheets after sequential exposure to stressors including damp heat, ultra-violet (UV) light radiation, and thermal cycling. The laminate backsheets deteriorated extensively after sequential exposure to these stressors, while the novel coextruded structures retained their physical properties.

14 SOLAR ENERGY↗

DOE OSTI2021

Evaluating Non-Fluoropolymer-Based Co-Extruded Backsheets Using Combined-Accelerated Stress Testing and Materials Forensics

Co-extruded, non-fluoropolymer backsheet films for photovoltaic (PV) modules have gained popularity in recent years based on their cost competitiveness. However, their viability has been thrown into question as a result of widespread, early-life field-failures of some materials, particularly the polyamide (PA)-based “AAA” backsheet product. Failure to detect weaknesses in those earlier products could be due, in part, to insufficient quality testing practices. New testing protocols have recently been developed to better evaluate such materials. Here we show the testing results for a non-fluoropolymer, co-extruded PA-based backsheet film, which demonstrates greater durability than AAA and some commercial fluoropolymers. Using material characterization techniques including Fourier-transform infrared spectroscopy (FTIR), wide-angle x-ray scattering (WAXS), differential scanning calorimetry (DSC), X-ray photoelectron spectroscopy (XPS), elongation-to-break (ETB), and optical microscopy we perform a comprehensive failure analysis to better understand the materials weaknesses. This analysis can ultimately inform how best to improve the material and extend its lifetime. This work serves as a demonstration that some materials should not be discounted due to a single poorly designed product and that more appropriate qualification testing with subsequent materials analysis can be used to develop better materials.

41 EE - Solar Energy Technologies Office (EE-4S)↗