A correlation-based approach for evaluating mechanical properties of nuclear fuel cladding tubes

The present work offers and evaluates a correlation-based approach to determine the tensile properties of nuclear fuel cladding tubes. A set of model materials with known properties (i.e., austenitic and ferritic steels, fcc- and hcp-alloys) were tested to build a correlation between conventional tensile tests and ring (hoop) and tube (axial) tests. It was shown that close-to-linear relationships exist for the basic mechanical properties (i.e., yield and ultimate stress, uniform and total elongation) between the uniaxial tensile test data and the ring and tube test data. Using the ring and tube specimen geometries, the feasibility of the approach was demonstrated via manufacturing and testing specimens from irradiated Zr and FeCrAl nuclear fuel cladding tubes. Limitations caused by specific deformation mechanisms (e.g., high ductility of 304L steel) were discussed in detail. The approach can be extended to other tubular products with different geometry and dimensions.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Conceptual Design of the Transformational Challenge Reactor

The Transformational Challenge Reactor is a 3-MW(thermal) helium-cooled experimental nuclear reactor designed using an additive manufacturing–informed agile design process. This design process leverages rapid prototyping and advanced materials from emerging additive manufacturing technologies, key characteristics that enable rapid design maturation. The resulting core design incorporates a blend of advanced reactor technologies into an intermediate-spectrum microreactor, including conventionally manufactured tristructural isotropic (TRISO) fuel particles in an advanced manufactured SiC fuel element and a solid yttrium hydride moderator encapsulated in steel. Matured during the design effort, these technologies are incorporated with additively manufactured steel support and fluidic structures to form a 75-cm-outer-diameter cylindrical active core region. Below and above the active core region are axial SiC reflectors, which are housed inside the reactor pressure vessel. The reactor is controlled with an annular shroud actuated external to the pressure vessel in the gap between the pressure vessel and a steel radial reflector. A safety rod is at the center of the core to shut down the reactor when necessary. Helium pressurized at 5 MPa is forced into the pressure vessel below the core and around the core to the top plenum before it is forced down through the axial reflectors and the active core region. The primary pressurized helium loop is operated up to 500°C and includes the pressure vessel, the circulator, and the hot side of a helium-to-air heat exchanger. The secondary loop rejects all heat from the primary loop to ambient air through a heat exchanger. A vented temporary confinement building contains the entire primary loop, with penetrations for a stack, cooling, and the secondary ambient air loop. Finally, this is the first advanced nuclear microreactor designed using additive manufacturing technologies, demonstrating their applicability in an accelerated advanced design process.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗

DOE OSTI2021

Mechanical behavior of additively manufactured and wrought 316L stainless steels before and after neutron irradiation

Fabrication of nuclear reactor components using additive manufacturing (AM) methods is now a practical option since the AM technologies have advanced to allow for building of complex parts with high quality materials. To assess the mechanical performance of printed components in reactor-relevant conditions and to build a property database for the AM 316L stainless steel (SS), mechanical testing and characterization were performed before and after neutron irradiation. In this work, miniature tensile specimens were irradiated at the High Flux Isotope Reactor (HFIR) to 0.2 and 2 displacements per atom (dpa) at 300 and 600°C. The AM 316L SS was tested in the as-built, stress-relieved, and solution-annealed conditions, and the wrought (WT) 316L SS in solution-annealed condition as a reference alloy. The baseline test result showed that the AM 316L SS, regardless of the post-build heat treatment, had higher strength than the WT 316L SS, but similar ductility. Post-irradiation tensile testing was conducted at RT, 300°C, and 500°C for selected irradiation conditions. Neutron irradiation induced significant changes in the mechanical behavior of the AM stainless steels, including both hardening and softening. Although the as-built 316L steel after 300°C irradiation showed necking just after yielding, the overall property changes of the as-printed alloy became less significant after 600°C irradiation. Irradiation-induced ductilization was also observed after the higher temperature irradiation. In general, the strength change was smaller in the relatively stronger as-built and stress-relieved AM SSs than in the solution-annealed AM and WT SSs. These relatively lower strength 316L SSs overall retained higher ductility in the irradiation conditions tested, but the stronger 316L SSs demonstrated a similar level of ductility after the higher temperature (600°C) irradiation. It is a positive assessment for the AM 316L materials that no embrittlement was observed within the test and irradiation conditions of the experiment.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Transformational Challenge Reactor preconceptual core design studies

In the nuclear industry, a manufacturing-informed design approach has the potential to yield the most benefit from advanced manufacturing. By leveraging advanced materials, data science, and rapid testing and deployment, manufacturing-informed design can drive down costs and development times, ultimately improving future commercial viability. This approach is being demonstrated in the US Department of Energy Office of Nuclear Energy (DOE-NE) Transformational Challenge Reactor (TCR) program. Preconceptual design activities for TCR have been focused on analyzing and maturing four reactor core design concepts: two fast-spectrum and two thermal-spectrum systems. Furthermore, the designs were iteratively modified and analyzed, and subcomponents were manufactured in parallel over weeks instead of months or years. To meet key program initiatives (e.g., timeline and material use), several constraints—including fissile material availability, component availability, materials compatibility, and additive manufacturing capabilities—were factored into the design effort, yielding small cores less than one cubic meter in volume with near-term viability. Additionally, the TCR program has made significant progress on development of advanced moderator materials such as yttrium hydride, advancing the feasibility of gas-cooled thermal spectrum systems using less than 250 kg of high-assay low enriched uranium (HALEU) and occupying less than 1 m3. Each of the two resulting thermal designs uses a different fuel form: traditional UO2 ceramic fuel and tristructural isotropic (advanced TRISO) fuel particles embedded inside a SiC matrix. Core neutronics and thermal performance for these systems were assessed and summarized. Evaluation of the performance metrics for these two moderated designs has yielded the downselected TCR design: a TRISO-fueled and yttrium hydride moderated gas-cooled reactor.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗