Sykes, G. F.

Publications and source records attributed to Sykes, G. F..

At least 19 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1988

Degradation of graphite-epoxy due to electron radiation

Experimental results are presented showing that electron irradiation has a variable effect on the properties of graphite-epoxy depending upon the test temperature and the property of interest. In general, compression properties are improved at cold temperature and degraded at elevated temperature. With the exception of some moduli, tensile and shear properties are degraded at both cold and elevated temperatures. Electron irradiation lowers the glass transition temperature of graphite/epoxy significantly. Property degradation of irradiated materials at the elevated temperature is associated with the reduction in Tg. It is shown that a (0) compression-strength test is the most sensitive test for exhibiting the effects of electron irradiation. Results from tests on neat resin also show that the bulk matrix is degraded after irradiation, and that the correlation between resin and composite response is good.

Herakovich, C. T.↗
NASA NTRS1986

The effects of space radiation on a chemically modified graphite-epoxy composite material

The effects of the space environment on the engineering properties and chemistry of a chemically modified T300/934 graphite-epoxy composite system are characterized. The material was subjected to 1.0 x 10 to the 10th power rads of 1.0 MeV electron irradiation under vacuum to simulate 30 years in geosynchronous earth orbit. Monotonic tension tests were performed at room temperature (75 F/24 C) and elevated temperature (250 F/121 C) on 4-ply unidirectional laminates. From these tests, inplane engineering and strength properties (E sub 1, E sub 2, Nu sub 12, G sub 12, X sub T, Y sub T) were determined. Cyclic tests were also performed to characterize energy dissipation changes due to irradiation and elevated temperature. Large diameter graphite fibers were tested to determine the effects of radiation on their stiffness and strength. No significant changes were observed. Dynamic-mechanical analysis demonstrated that the glass transition temperature was reduced by 50 F(28 C) after irradiation. Thermomechanical analysis showed the occurrence of volatile products generated upon heating of the irradiated material. The chemical modification of the epoxy did not aid in producing a material which was more radiation resistant than the standard T300/934 graphite-epoxy system. Irradiation was found to cause crosslinking and chain scission in the polymer. The latter produced low molecular weight products which plasticize the material at elevated temperatures and cause apparent material stiffening at low stresses at room temperature.

Reed, S. M.↗
NASA NTRS1986

Space radiation effects on the dimensional stability of a toughened epoxy graphite composite

The effects of a simulated space radiation environment on the dimensional stability of an elastomer-toughened epoxy-graphite composite were determined. The response of the material was characterized following exposure to radiation doses equivalent to geosynchronous orbit lifetimes ranging from 6 months to 30 years. The results show that radiation interacts with the epoxy matrix to embrittle the composite, beginning at relatively low total doses (10 to the 7th power rads). The embrittlement results in thermal expansion changes and significant laminate microcracking during thermal cycling. These property changes could limit the service life of this material in some spacecraft applications.

Sykes, G. F.↗
NASA NTRS1986

The effects of radiation on the interlaminar fracture toughness of a graphite/epoxy composite

An experimental study is made of the effect of electron irradiation (10 to the 10th rad), simulating a 30-year geosynchronous orbit exposure, on the fracture toughness of a graphite/epoxy composite, T300/934. The double cantilever beam (DBC) test is used to determine Mode I (peel) critical strain energy release rate and the edge delamination tension (EDT) test is used to determine mixed Mode I and II (peel and shear) critical strain energy release rate. It is found that the electron interaction of the epoxy matrix material enhances the fracture toughness properties of the composite and that the test temperature has a significant effect on the fracture toughness of both baseline and irradiated material.

Funk, J. G.↗
NASA NTRS1985

The thermal and mechanical stability of composite materials for space structures

A continuing research objective of the National Aeronautical and Space Administration (NASA) is to develop advanced composite materials for space structures. The thrust of this research is to gain fundamental understanding of the performance of advanced composites in the space environment. The emphasis has been to identify and model changes in the thermal-physical properties due to induced damage and develop improved materials.

Tompkins, S. S.↗
NASA NTRS1985

NASA space materials research

The effect of the space environment on: (1) thermal control coatings and thin polymer films; (2) radiation stability of 250 F and 350 F cured graphite/epoxy composites; and (3) the thermal mechanical stability of graphite/epoxy, graphite/glass composites are considered. Degradation in mechanical properties due to combined radiation and thermal cycling is highlighted. Damage mechanisms are presented and chemistry modifications to improve stability are suggested. The dimensional instabilities in graphite/epoxy composites associated with microcracking during thermal cycling is examined as well as the thermal strain hysteresis found in metal-matrix composites.

Tenney, D. R.↗
NASA NTRS1985

Space radiation effects on an elastomer-toughened epoxy-graphite composite

An elastomer-toughened epoxy-graphite composite system (CE339/T300) was evaluated for its potential durability in the space radiation environment. The physical and chemical response of this system was characterized following exposure to radiation doses equivalent to 20 to 30 years in geosynchronous orbit using 1 MeV electrons. The results show that electrons generate extensive crosslinking and embrittlement of the matrix. This embrittlement results in chemical and mechanical property changes that would limit the service life of this epoxy system in some space structure applications.

Sykes, G. F.↗
NASA NTRS1984

Electron radiation effects on the thermal expansion of graphite/resin composites

The effects of 1 MeV electron radiation on the thermal expansion characteristics of two graphite reinforced resin matrix composite systems were studied. Specimens of both graphite/epoxy (T300/5208) and graphite/polyimide (C6000/PMR15) were irradiated to a total dose of 6 x 10 to the 9th rads at two different rates. Dynamic mechanical analyses (DMA) were performed to study changes in resin chemistry. Thermal expansion results indicate that radiation did produce permanent residual strains of up to -70 x 10 to the -6th for the graphite/epoxy when exposed to temperatures up to +280 F. However, no permaanent changes in the coefficient of thermal expansion (CTE) were observed. No permanent residual strains or changes in the CTE attributable to radiation were observed for the graphite/polyimide specimens. DMA results indicate that electron radiation caused chemical changes in the epoxy matrix. These changes resulted in a lower glass transition temperature and broader 'rubbery region' which extended into the temperature range of the thermal expansion tests.

Bowles, D. E.↗
NASA NTRS1983

Space environmental effects on materials

Research efforts at NASA-Langley to characterize the durability of composite materials which are candidates or use as components on various space hardware systems are reviewed. The material applications include large space structures, antennas, cables, thermal control coatings, solar reflectors, and satellite power systems. Simulation facilities have been built to study radiation effects on polymer matrix composites, and the dimensional stability of the matrix composites and tension stabilized.

Tenny, D. R.↗
NASA NTRS1982

Space environmental effects on materials

Research efforts at NASA-Langley to characterize the durability of composite materials which are candidates for use as components on various space hardware systems are reviewed. The material applications include large space structures, antennas, cables, thermal control coatings, solar reflectors, and satellite power systems. Simulation facilities have been built to study radiation effects on polymer matrix composites, and the dimensional stability of the matrix composites and tension stabilized cables. Numerical models are being developed for radiation effects on the mechanical, physical, and optical properties. Additionally, chemical and microstructural analyses are performed to identify damage mechanisms and the limits of effectiveness of accelerating life tests. It is noted that no residual strength reduction has been detected in polymer films after dosages of 5 billion rads of electron radiation.

Tenney, D. R.↗
NASA NTRS1981

Radiation effects on four polysulfone films

The response of polysulfones to proton and electron radiation is evaluated by assessing the radiation durability of four selected sulfones, establishing radiation interaction mechanisms with the polymer chain, and determining the dependence of radiation durability on chemical structure. Chain scission appears to predominate at lower doses up to about 10 to the 9th rad, and past this threshold the second mechanism, crosslinking, seems to predominate. This is evidenced by the increase in modulus, glass transition temperature, and increased quantity of thermally stable residue at high temperatures. The variations of chemical structure of the polysulfones appear to have little effect on the response to radiation.

Santos, B.↗
NASA NTRS1980

Advanced materials for space

The principal thrust of the LSST program is to develop the materials technology required for confident design of large space systems such as antennas and platforms. Areas of research in the FY-79 program include evaluation of polysulfones, measurement of the coefficient of thermal expansion of low expansion composite laminates, thermal cycling effects, and cable technology. The development of new long thermal control coatings and adhesives for use in space is discussed. The determination of radiation damage mechanisms of resin matrix composites and the formulation of new polymer matrices that are inherently more stable in the space environment are examined.

Tenney, D. R.↗
NASA NTRS1980

Characterization of aging effects of LARC-160

Specimens of freshly prepared polyimide precursor resin LARC-160 and resin aged at room temperature up to 45 days were characterized by high-pressure liquid chromatography and several different thermal analyses. Graphite reinforced composites were then fabricated from fresh and aged resin and tested to determine if changes observed by these techniques were significant. It was found that resin aging resulted in greater flow during processing and poorer composite isothermal stability. However, aging did not affect the room-temperature flexural or short-beam-shear strengths of the composites.

Young, P. R.↗
NASA NTRS1980

Impact penetration studies of graphite/epoxy laminates

A study was conducted to provide an initial insight into the role of the matrix in impact energy absorption of graphite/epoxy laminates. A single epoxy system, NARMCO 5208, in both composite and cured neat-resin form was studied with a constant velocity impact test apparatus. The parameters investigated include resin cure temperature, fiber type, ply thickness and orientation, and impact velocity. The results from the study show that matrix chemistry, as obtained by cure temperature changes, has a significant effect upon the failure mode and energy absorption during impact.

Sykes, G. F.↗
NASA NTRS1980

Analysis of aromatic polyamine mixtures for formulation of LARC-160 resin

An investigation was conducted to identify a potential substitute for the aromatic polyamine mixture, Jeffamine AP-22, currently used to formulate LARC-160 polyimide precursor resin. Jeffamine AP-22 was characterized by high pressure liquid chromatography and mass spectrometry. Eleven different aromatic amines in the mixture were isolated and identified. Subsequent liquid chromatographic analysis of nine additional commercially available aromatic polyamine mixtures identified three candidates that are similar in composition to AP-22.

Young, P. R.↗
NASA NTRS1979

HPLC for quality control of polyimides

High Pressure Liquid Chromatography (HPLC) as a quality control tool for polyimide resins and prepregs are presented. A data base to help establish accept/reject criteria for these materials was developed. This work is intended to supplement, not replace, standard quality control tests normally conducted on incoming resins and prepregs. To help achieve these objectives, the HPLC separation of LARC-160 polyimide precursor resin was characterized. Room temperature resin aging effects were studied. Graphite reinforced composites made from fresh and aged resin were fabricated and tested to determine if changes observed by HPLC were significant.

Young, P. R.↗
NASA NTRS1977

The effect of moisture on the dynamic thermomechanical properties of a graphite/epoxy composite

A study has been made of the effect of moisture absorption on the dynamic thermomechanical properties of a graphite/epoxy composite recently considered for building primary aircraft structures. Torsional braid analysis (TBA) and thermomechanical analysis (TMA) techniques were used to measure changes in the glass transition temperature (Tg) and the initial softening temperature (heat distortion temperature, HDT) of T-300/5209 graphite/epoxy composites exposed to room temperature water soak.

Sykes, G. F.↗