Suzuki, Yuri

Publications and source records attributed to Suzuki, Yuri.

14 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

The role of magnetic anisotropy in the magnetoresistance of Cr 2 O 3 /Al 2 O 3 thin film antiferromagnets

The magnetic states of antiferromagnetic insulating thin films are a promising medium for information storage, but characterization of these states has proven to be challenging. One approach is via magnetotransport measurements in an adjacent heavy metal layer. To this end, we synthesized and characterized a series of Cr 2 O 3 films and bilayers on Al 2 O 3 substrates with three different orientations: m-plane, a-plane, and c-plane. X-ray diffraction results demonstrated orientation control of the Cr 2 O 3 thin film, with m-plane films displaying a higher degree of mosaic spread than the a- and c-plane films. Reciprocal space maps showed that the films are mostly relaxed, although there was a small and different degree of strain in each orientation. The m-plane films were under 2% compressive strain, the a-plane film was under 0.5% compressive strain, and the c-plane film was completely relaxed to bulk values. To probe the magnetic state of the films, we measured the angular dependent magnetoresistance of Cr 2 O 3 /Pt bilayers for each orientation. We found a nontrivial temperature dependence of the sign of the magnetoresistance, pointing to the complex interplay between the exchange and anisotropy energies that vary with orientation. We propose that strain and mosaic spread may contribute to a difference in magnetic anisotropies among the samples and the resulting temperature dependence of the magnetoresistance. This work demonstrates the importance of considering the competition between antiferromagnetic exchange and magnetic anisotropy when storing information in the spin state of an antiferromagnetic insulator.

42 ENGINEERING↗
DOE OSTI2024

Emergent Ferromagnetism in CaRuO 3 /CaMnO 3 (111)-Oriented Superlattices

The boundary between CaRuO 3 and CaMnO 3 is an ideal test bed for emergent magnetic ground states stabilized through interfacial electron interactions. In this system, nominally antiferromagnetic and paramagnetic materials combine to yield interfacial ferromagnetism in CaMnO 3 due to electron leakage across the interface. In this work, we show that the crystal symmetry at the surface is a critical factor determining the nature of the interfacial interactions. Specifically, by growing CaRuO 3 /CaMnO 3 heterostructures along the (111) instead of the (001) crystallographic axis, we achieve a 3-fold enhancement of the magnetization and involve the CaRuO 3 layers in the ferromagnetism, which now spans both constituent materials. Importantly, the stabilization of a net magnetic moment in CaRuO 3 through strain effects has been long-sought but never consistently achieved, and our observations demonstrate the importance of interface engineering in the development of new functional heterostructures.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Enhanced Ferromagnetism in Atomically Thin Oxides Achieved by Interfacial Reconstruction

Discoveries of ferromagnetic materials with ultrathin thickness are of great importance for both fundamental science and technological applications. Transition metal oxides (TMOs) provide promising candidates in the context of next‐generation spintronics, despite the severe decay of ferromagnetism as the thickness reduces to the nanometer regime. Here, in this work, an efficient strategy to eliminate the magnetic dead layer in atomically thin oxides is presented, by using the epitaxial interface of 3 d and 5 d oxide monolayers that reconciles both strong exchange interaction and large uniaxial magnetic anisotropy. Combining multiple experimental methods, a ferromagnetic transition in an ultrathin oxide heterostructure comprised of only one La 0.2 Sr 0.8 MnO 3 monolayer sandwiched by SrIrO 3 monolayer (total thickness of three unit‐cells) is unambiguously demonstrated. Remarkably, a largely enhanced saturation magnetization (2 µ B Mn −1 ) and Curie temperature (80 K) are observed for the single manganite monolayer, as compared to previously reported ferromagnetic monolayer oxides. The results demonstrate a general strategy for creating robust ferromagnetism in ultrathin TMOs, potentially enabling novel oxide spin‐orbitronic devices.

2D ferromagnetism↗
DOE OSTI2023

Ultra-thin lithium aluminate spinel ferrite films with perpendicular magnetic anisotropy and low damping

Ultra-thin films of low damping ferromagnetic insulators with perpendicular magnetic anisotropy have been identified as critical to advancing spin-based electronics by significantly reducing the threshold for current-induced magnetization switching while enabling new types of hybrid structures or devices. Here, we have developed a new class of ultra-thin spinel structure Li 0.5 Al 1.0 Fe 1.5 O 4 (LAFO) films on MgGa 2 O 4 (MGO) substrates with: 1) perpendicular magnetic anisotropy; 2) low magnetic damping and 3) the absence of degraded or magnetic dead layers. These films have been integrated with epitaxial Pt spin source layers to demonstrate record low magnetization switching currents and high spin-orbit torque efficiencies. These LAFO films on MGO thus combine all of the desirable properties of ferromagnetic insulators with perpendicular magnetic anisotropy, opening new possibilities for spin based electronics.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Large Spin-Orbit-Torque Efficiency and Room-Temperature Magnetization Switching in Sr Ir O 3 / Co-Fe-B Heterostructures

Spin-orbit-torque (SOT) switching is a potentially energy-efficient mechanism by which electrical current can control magnetization. We demonstrate room-temperature SOT switching in nanometer-thick Co⁢Fe⁢B/Sr⁢Ir⁢O 3 bilayers despite the amorphous nature of CoFeB and the interface. This behavior is attributed to the large spin Hall angle in Sr⁢Ir⁢O 3 as well as high spin transmission at the interface that contribute to the SOT efficiency ξ SOT . Our bilayers exhibit large ξ SOT of up to 1.4 and effective spin Hall conductivity of 0.9 ×10 5 (ℏ/2e)Ω –1 ⁢m –1 . In our bilayers, we observe unidirectional magnetoresistance and current-induced magnetization switching with a low critical current density of 1.38 ×10 10 A/m 2 at room temperature. Finally, our results are promising for heterostructures combining technologically relevant CoFeB with high spin-orbit-coupling oxides.

72 PHYSICS OF ELEMENTARY PARTICLES AND FIELDS↗
DOE OSTI2021

Ferromagnetic resonances in single-crystal yttrium iron garnet nanofilms fabricated by metal-organic decomposition

Tunable microwave and millimeter wave oscillators and bandpass filters with ultra-low phase noise play a critical role in electronic devices, including wireless communication, microelectronics, and quantum computing. Magnetic materials, such as yttrium iron garnet (YIG), possess ultra-low phase noise and a ferromagnetic resonance tunable up to tens of gigahertz. Here, we report structural and magnetic properties of single-crystal 60 and 130 nm-thick YIG films prepared by metal-organic decomposition epitaxy. These films, consisting of multiple homoepitaxially grown monolayers, are atomically flat and possess magnetic properties similar to those grown with liquid-phase epitaxy, pulsed laser deposition, and sputtering. Our approach does not involve expensive high-vacuum deposition systems and is a true low-cost alternative to current commercial techniques that have the potential to transform the industry.

Wang, Szu-Fan (Paul)↗
DOE OSTI2021

Emergent long-range magnetic order in ultrathin (111)-oriented LaNiO3 films

Abstract The emergence of ferromagnetism in materials where the bulk phase does not show any magnetic order demonstrates that atomically precise films can stabilize distinct ground states and expands the phase space for the discovery of materials. Here, the emergence of long-range magnetic order is reported in ultrathin (111) LaNiO 3 (LNO) films, where bulk LNO is paramagnetic, and the origins of this phase are explained. Transport and structural studies of LNO(111) films indicate that NiO 6 octahedral distortions stabilize a magnetic insulating phase at the film/substrate interface and result in a thickness-dependent metal–insulator transition at t = 8 unit cells. Away from this interface, distortions relax and bulk-like conduction is regained. Synchrotron x-ray diffraction and dynamical x-ray diffraction simulations confirm a corresponding out-of-plane unit-cell expansion at the interface of all films. X-ray absorption spectroscopy reveals that distortion stabilizes an increased concentration of Ni 2+ ions. Evidence of long-range magnetic order is found in anomalous Hall effect and magnetoresistance measurements, likely due to ferromagnetic superexchange interactions among Ni 2+ –Ni 3+ ions. Together, these results indicate that long-range magnetic ordering and metallicity in LNO(111) films emerges from a balance among the spin, charge, lattice, and orbital degrees of freedom.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Magnetic anisotropy and spin scattering in (La 2/3 Sr 1/3 )MnO 3 /CaRuO 3 bilayers

Complex ferromagnetic oxides have been identified as possible candidate materials for sources of spin currents. Here we study bilayers of ferromagnetic (La 2/3 Sr 1/3 )MnO 3 (LSMO) and metallic CaRuO 3 (CRO) on LSAT substrates as a model system for spin pumping. Ferromagnetic resonance (FMR) measurements of these bilayers show evidence of spin pumping across the interface in the form of an increase in Gilbert damping with the addition of CRO. FMR indicates that the presence of CRO modifies the magnetic anisotropy of the LSMO. By increasing CRO thickness, we find a reduction of the out-of-plane anisotropy and simultaneous rotation of the easy axis within the plane, from the $\langle$110$\rangle$ to $\langle$100$\rangle$ axis. The evolution of magnetic anisotropy determined by FMR disagrees with that measured by bulk SQUID magnetometry and is accompanied by structural distortions in the LSMO layer as measured by x-ray diffraction, thus suggesting a change in magnetic anisotropy attributed to structural distortions imposed on LSMO by CRO. These results suggest that while LSMO and CRO remain promising candidates for efficient pure spin current generation and detection, respectively, epitaxial integration of perovskites will cause additional changes which must be accounted for in spintronics applications.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Enhanced Interface-Driven Perpendicular Magnetic Anisotropy by Symmetry Control in Oxide Superlattices

Perpendicular magnetic anisotropy (PMA) has recently been shown to emerge at interfaces of 3d and 5d transition-metal oxides (TMOs). However, strategies to systematically stabilize such interface-driven PMA still remains elusive, hindering further applications of this design approach. Here, tuning crystal symmetry is shown to be an effective means to engineer this interfacial phenomenon. The evolution of PMA strength as a function of ferromagnetic oxide thickness quantitatively reveals the competition between volume- and interface-specific contributions that determine the magnetic anisotropy. By applying different degrees of epitaxial strain, the relative contributions to PMA are modulated, clearly revealing their correlations with crystal symmetries. To be more specific, the volume anisotropy energy is found to be correlated with the tetragonal distortion of the ferromagnetic layer, while the interface anisotropy energy is mainly modulated by the octahedral tilting at the interface. With these insights, superlattices with enhanced interface-driven PMA and higher Curie temperature are realized. These findings reveal a route to engineering interface-driven PMA and associated magnetic phenomena in TMO heterostructures for future spintronic applications.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗
DOE OSTI2021

Growth and characterization of La 0.67 Sr 0.33 MnO 3 /YBa 2 Cu 3 O 7- δ bilayers

Understanding the interplay of ferromagnets and superconductors requires high quality interfaces. To this end, we have fabricated heterostructures of the cuprate superconductor YBa2Cu3O7-δ (YBCO) with the metallic ferromagnet La0.67Sr0.33MnO3 (LSMO) via pulsed laser deposition on SrTiO3 (STO) (001) and (LaAlO3)0.3(Sr2TaAlO6)0.7 (LSAT) (001) substrates. By varying the YBCO thickness from 1.7-13.6 nm while keeping the LSMO thickness at 12 nm, we have studied the interplay between ferromagnetism and superconductivity in the in-plane transport and magnetic properties of the bilayers. X-ray reflectivity data indicate the presence of a 2-3 nm thick interfacial layer between the LSMO and YBCO layers in all heterostructures. In-plane transport measurements exhibit suppression of the superconducting transition temperature from bulk YBCO values. Magnetometry measurements indicate high LSMO saturation magnetization values for samples grown on STO substrates and even higher (bulk-like) magnetization for bilayers grown on LSAT substrates. Together these results indicate that the interdiffused layer is largely attributed to a modified YBCO layer.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Ultra-low magnetic damping in epitaxial Li 0.5 Fe 2.5 O 4 thin films

The realization of more energy efficient nanomagnetic information devices relies on the existence of magnetic insulators capable of supporting pure spin currents in the absence of a dissipative charge current. Currently, there is a limited number of thin-film magnetic insulators with low magnetic damping. Li 0.5 Fe 2.5 O 4 (LFO) is well known to possess the lowest damping among the bulk spinel structure oxides, but, thus far, LFO thin films have not lived up to these expectations. Here, we demonstrate low magnetic damping (even lower than typical bulk values) and bulk magnetization in 3 nm thick epitaxial LFO thin films. At room temperature, SQUID magnetometry shows a high saturation magnetization of 320 kA/m, and broadband ferromagnetic resonance measurements yield an effective Gilbert damping parameter of 1.3×10 -3 , which is among the lowest reported for ferro-/ferrimagnetic films of comparable thickness. Our results show the promise of LFO as a candidate material for spin current-based spintronics.

36 MATERIALS SCIENCE↗
DOE OSTI2020

The role of iron in magnetic damping of Mg(Al,Fe) 2 O 4 spinel ferrite thin films

© 2020 Author(s). We have investigated magnesium aluminum ferrite thin films with a range of iron concentrations and identified the optimal iron content to obtain high crystalline quality thin films with the low magnetic damping required for spin current-based applications. Epitaxial MgAl 2-x FexO4 films with 0.8 < x < 2.0 were grown by pulsed laser deposition on single crystal MgAl2O4 substrates and were characterized structurally and magnetically. We find that the x = 1.5 composition minimizes the room-temperature magnetic damping with a typical Gilbert damping parameter of α eff = 1.8 × 10-3. This minimized damping is governed by a competition between the more robust magnetic ordering with increased iron content, x, and the more defective structure due to larger film-substrate lattice mismatch with increased iron content. The temperature-dependent magnetization curves indicate that Tc is suppressed below room temperature for iron content x ≤ 1.2 and eventually suppressed entirely for x = 0.8. X-ray magnetic circular dichroism results indicate that for all x the magnetic moment is dominated by Fe 3 + cations distributed in a 60:40 ratio on the octahedral and tetrahedral sites, with minimal contribution from Fe 2 + cations. Films with x = 1.4-1.6 exhibit very strong ferromagnetic resonance and low Gilbert damping with α eff = (1.8-6) × 10-3, making them ideal candidates for microwave and spintronic applications.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Emergent electric field control of phase transformation in oxide superlattices

Electric fields can transform materials with respect to their structure and properties, enabling various applications ranging from batteries to spintronics. Recently electrolytic gating, which can generate large electric fields and voltage-driven ion transfer, has been identified as a powerful means to achieve electric-field-controlled phase transformations. The class of transition metal oxides provide many potential candidates that present a strong response under electrolytic gating. However, very few show a reversible structural transformation at room-temperature. Here, we report the realization of a digitally synthesized transition metal oxide that shows a reversible, electric-field-controlled transformation between distinct crystalline phases at room-temperature. In superlattices comprised of alternating one-unit-cell of SrIrO 3 and La 0.2 Sr 0.8 MnO 3 , we find a reversible phase transformation with a 7% lattice change and dramatic modulation in chemical, electronic, magnetic and optical properties, mediated by the reversible transfer of oxygen and hydrogen ions. Strikingly, this phase transformation is absent in the constituent oxides, solid solutions and larger period superlattices. Our findings open up this class of materials for voltage-controlled functionality.

36 MATERIALS SCIENCE↗