DOE OSTI2022

Combinatorial Cu-Ni Alloy Thin-Film Catalysts for Layer Number Control in Chemical Vapor-Deposited Graphene

We synthesized a combinatorial library of CuxNi1−x alloy thin films via co-sputtering from Cu and Ni targets to catalyze graphene chemical vapor deposition. The alloy morphology, composition, and microstructure were characterized via scanning electron microscopy (SEM), energy dispersive x-ray spectroscopy (EDS), and X-ray diffraction (XRD), respectively. Subsequently, the CuxNi1−x alloy thin films were used to grow graphene in a CH4-Ar-H2 ambient at atmospheric pressure. The underlying rationale is to adjust the CuxNi1−x composition to control the graphene. Energy dispersive x-ray spectroscopy (EDS) analysis revealed that a continuous gradient of CuxNi1−x (25 at. % < x < 83 at.%) was initially achieved across the 100 mm diameter substrate (~0.9%/mm composition gradient). The XRD spectra confirmed a solid solution was realized and the face-centered cubic lattice parameter varied from ~3.52 to 3.58 A˙, consistent with the measured composition gradient, assuming Vegard’s law. Optical microscopy and Raman analysis of the graphene layers suggest single layer growth occurs with x > 69 at.%, bilayer growth dominates from 48 at.% < x < 69 at.%, and multilayer (≥3) growth occurs for x < 48 at.%, where x is the Cu concentration. Finally, a large area of bi-layer graphene was grown via a CuxNi1−x catalyst with optimized catalyst composition and growth temperature.

2D materials↗

DOE OSTI2021

Ultrafast and Controllable Phase Evolution by Flash Joule Heating

Flash Joule heating (FJH), an advanced material synthesis technique, has been used for the production of high-quality carbon materials. Direct current discharge through the precursors by large capacitors has successfully converted carbon-based starting materials into bulk quantities of turbostratic graphene by the FJH process. However, the formation of other carbon allotropes, such as nanodiamonds and concentric carbon materials, as well as the covalent functionalization of different carbon allotropes by the FJH process, remains challenging. Here, we report the solvent-free FJH synthesis of three different fluorinated carbon allotropes: fluorinated nanodiamonds, fluorinated turbostratic graphene and fluorinated concentric carbon. This is done by millisecond flashing of organic fluorine compounds and fluoride precursors. Spectroscopic analysis confirms the modification of the electronic states and the existence of various short-range and long-range orders in the different fluorinated carbon allotropes. As a result, the flash time-dependent relationship is further demonstrated to control the phase evolution and product compositions.

01 COAL, LIGNITE, AND PEAT↗

DOE OSTI2021

Millisecond Conversion of Metastable 2D Materials by Flash Joule Heating

Controllable phase engineering is vital for precisely tailoring material properties since different phase structures have various electronic states and atomic arrangements. Rapid synthesis of thermodynamically metastable materials, especially two-dimensional metastable materials, with high efficiency and low cost remains a large challenge. Here we report flash Joule heating (FJH) as an electrothermal method to achieve the bulk conversion of transition metal dichalcogenides, MoS 2 and WS 2 , from 2H phases to 1T phases in milliseconds. The conversions can reach up to 76% of flash MoS 2 using tungsten powder as conductive additive. Different degrees of phase conversion can be realized by controlling the FJH conditions, such as reaction duration and additives, which allows the study of ratio-dependent properties. First-principles calculations confirm that structural processes associated with the FJH, such as vacancy formation and charge accumulation, result in stabilization of the 1T phases. Furthermore, FJH offers rapid access to bulk quantities of the hitherto hard-to-access 1T phases, a promising method for further fundamental research and diverse applications of metastable phases.

2D materials↗

DOE OSTI2020

Flash Graphene Morphologies

Flash Joule heating (FJH) can convert almost any carbon-based precursor into bulk quantities of graphene. This work explores the morphologies and properties of flash graphene (FG) generated from carbon black. It is shown that FG is partially comprised of sheets of turbostratic FG (tFG) that have a rotational mismatch between neighboring layers. The remainder of the FG is wrinkled graphene sheets that resemble non-graphitizing carbon. To generate high quality tFG sheets, a FJH duration of 30 – 100 ms is employed. Beyond 100 ms, the turbostratic sheets have time to AB-stack and form bulk graphite. Atomistic simulations reveal that generic thermal annealing yields predominantly wrinkled graphene which displays minimal to no alignment of graphitic planes, as opposed to the high-quality tFG that might be formed under the direct influence of current conducted through the material. As a result, the tFG was easily exfoliated via shear, hence the FJH process has the potential for bulk production of tFG without the need for pre-exfoliation using chemicals or high energy mechanical shear.

01 COAL, LIGNITE, AND PEAT↗