Modeling creep behavior in ceramic matrix composites

Here, in this work, a three-dimensional viscoplasticity formulation with progressive damage is developed and used to investigate the complex time-dependent constituent load transfer and progressive damage behavior in ceramic matrix composites (CMCs) subjected to creep. The viscoplasticity formulation is based on Hill's orthotropic plastic potential, an associative flow rule, and the Norton-Bailey creep power law with Arrhenius temperature dependence. A fracture mechanics-informed isotropic matrix damage model is used to account for CMC brittle matrix damage initiation and propagation, in which two scalar damage variables capture the effects of matrix porosity as well as matrix property degradation due to matrix crack initiation and propagation. The Curtin progressive fiber damage model is utilized to simulate progressive fiber failure. The creep-damage formulation is subsequently implemented as a constitutive model in the generalized method of cells (GMC) micromechanics formulation to simulate time-dependent deformation and material damage under creep loading conditions. The developed framework is used to simulate creep of single fiber SiC/SiC microcomposites. Simulation results are in excellent agreement with experimental and numerical data available in the literature.

36 MATERIALS SCIENCE↗

NASA NTRS2019

Through-Thickness Tensile Properties of Triaxial Braided Composites

The through-thickness strength of triaxial braided composites was measured using thin specimens bonded to metallic tabs. Despite providing reasonable engineering estimates of the bulk properties, some test specimen limitations were noted: For strong epoxies, significant shear and tensile stresses occur and induce failure between the first layer and bond-line; the strains over much of the exterior are ~10% lower than interior strains, which are representative of the nominal state; and failure often occurred near or along the adhesive bond line. These interference were partially overcome by adding a large radius to the gage section. Based on the finite element analysis and experimental measurements, the nominal elastic modulus and Poisson's ratio are E(sub 33) = 10.7 GPa and v(sub 31) = 0.08 for the three triaxial braided composites tested. Strengths vary from 14 to 40 MPa depending on the resin. Relative to the in-plane properties, the through thickness modulus, fracture strength, failure strain, and Poisson's ratio are 1/5th, 1/30th, 1/6th, and 1/4th. Interlaminar failure occurred with varying degrees of fiber tear out along with little damage to axial tows, resulting is a smooth undulating fracture surface. Post cure temperature excursions to 177 deg C (350 deg F) had little effect on elastic constants but reduced the strength E862 based composites severely. The strength of PR520 and 5208 based composites increased.

composite↗