Reconfigurable Grating Diffraction Structural Color in Self-Assembled Colloidal Crystals

Self-assembled colloidal crystals display structural colors due to light diffracted from their microscale, ordered structure. This color arises due to Bragg reflection (BR) or grating diffraction (GD); the latter mechanism is much less explored than the former. Here the design space for generating GD structural color is identified and its relative advantages are demonstrated. Electrophoretic deposition is used to self-assemble crystals with fine crystal grains from colloids of diameter 1.0 µm. The structural color in transmission is tunable across the full visible spectrum. The optimum optical response—represented by both color intensity and saturation—is observed at low layer number (≤5 layers). The spectral response is well predicted by Mie scattering of the crystals. Taken together, the experimental and theoretical results demonstrate that vivid grating colors with high color saturation can be produced from thin layers of micron-sized colloids. These colloidal crystals extend the potential of artificial structural color materials.

42 ENGINEERING↗

DOE OSTI2023

Microdynamics of active particles in defect-rich colloidal crystals

Hypothesis. Because they are self-propulsive, active colloidal particles can interact with their environment in ways that differ from passive, Brownian particles. Here, we explore how interactions in different microstructural regions may contribute to colloidal crystal annealing. Experiments. We investigate active particles propagating in a quasi-2D colloidal crystal monolayer produced by alternating current electric fields (active-to-passive particle ratio ~ 1:720). The active particle is a platinum Janus sphere propelled by asymmetric decomposition of hydrogen peroxide. Crystals are characterized for changes in void properties. The mean-squared-displacement of Janus particles are measured to determine how active microdynamics depend on the local microstructure, which is comprised of void regions, void-adjacent regions (defined as within three particle diameters of a void), and interstitial regions. Findings. At active particle energy E A = 2.55 k B T, the average void size increases as much as three times and the average void anisotropy increases about 40% relative to the passive case. Further, the average microdynamical enhancement, <δ(t)>, of Janus particles in the crystal relative to an equivalent passive Janus particle is reduced compared to that of a free, active particle (<δ(t) > is 1.88 ± 0.04 and 2.66 ± 0.08, respectively). The concentration of active particles is enriched in void and void-adjacent regions. Active particles exhibit the greatest change in dynamics relative to the passive control in void-adjacent regions (<δ(t)> = 2.58 ± 0.06). The results support the conjecture that active particle microdynamical enhancement in crystal lattices is affected by local defect structure.

36 MATERIALS SCIENCE↗