Smith, Rebecca E. | Engineering Papers

DOE OSTI2023

Determining the oxidation behavior of matrix graphite

This work presents the oxidation behavior of matrix graphite in air. Matrix graphite, graphite powder/flakes bonded by a small amount of non-graphitic carbon, surrounds coated fuel particles in order to form cylindrical fuel compacts (in prismatic core designs) or spheres (in pebble-bed reactor designs). This work focuses on oxidation tests conducted on two matrix graphite materials, one provided by Kairos Power and the other A3 matrix graphite. Some of the tests followed American Society for Testing and Materials (ASTM) oxidation testing standards using a vertical furnace system and others were performed in a thermogravimetric analyzer (TGA). It was determined that, at temperatures of 450 °C–700 °C, the oxidation rate of the Kairos matrix graphite follows the Arrhenius equation. In comparison with A3 matrix graphite, the Kairos matrix graphite shows better oxidation resistance at high temperatures (≥550 °C), but also a higher oxidation rate at low temperatures. Both the A3 matrix graphite and the Kairos matrix graphite materials may experience preferential oxidation of the partially graphitized binder. An oxygen penetration gradient was also observed when using the three characterization methods (i.e., optical microscope, x-ray tomography [XCT], and density profile by the lathe) enlisted in this research. In conclusion, the oxygen penetration depth increases with decreasing isothermal oxidation temperature, while the center of the oxidized samples (10% weight loss) remains almost untouched even at 500 °C.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2023

Drying of Spent Nuclear Fuel: Considerations and Examples

A recently revised American Society for Testing and Materials consensus standard guide for drying of spent nuclear fuel (SNF) provides considerations and guidance for preparing SNF for its safe storage in a sealed dry storage system. The standard discusses (1) needs for drying, (2) techniques to dry, and (3) demonstration of adequate dryness. No specific approach is prescribed since the effective techniques and needs for drying depend on the specifics of the fuel and dry storage system. Here, this paper discusses these topics using examples for both Zr-alloy-clad commercial SNF and for aluminum-alloy-clad research reactor SNF. Residual water can include free water (liquid and/or vapor), physisorbed water bound to internal surfaces, and chemisorbed water incorporated into surface films, such as (oxy)hydroxides. The potential impacts of these residual waters are corrosion/oxidation, radiolytic breakdown into gaseous and/or reactive species, and canister pressurization. For commercial SNF, inadvertent free water, even up to large amounts (e.g., 10+ mol), is not predicted to cause adverse corrosion degradation, except possible fuel oxidation for breached SNF. For aluminum-clad SNF, the production of radiolytic hydrogen with contribution from the chemisorbed water in its hydrated oxides is a primary consideration. For both SNF systems, canister pressurization is predicted to be well within the canister design, and flammability would not pose a safety concern using an oxygen limit of 5 vol % criterion. (Flammability control can be achieved by limiting either hydrogen or oxygen, and an oxygen limit is expected to be easier to meet in the presence of radiolytic H 2 generation.) The two primary technologies for SNF drying, vacuum drying and forced-gas dehydration, are described herein, and drying tests and campaigns using these methods are cited. Dryness criteria and the methods used to detect and measure residual (free) water are also discussed.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗