Method of manufacturing proton selective membranes based on two dimensional materials

Proton conductive membrane includes a proton selective layer of 80-100% carbon with sp2 hybridization having a thickness of 0.3-100 nm, with 0-20% of hydrogen, oxygen, nitrogen and sp3 carbon; wherein the sp2 carbon is in a form of graphene-like material; the proton selective layer having a plurality of pores formed by any of 7, 8, 9 or 10 sp2 carbon cycles or a combination thereof, with the pores having an effective diameter of up to 0.6 nm; an ionomeric polymer layer on the proton selective layer. Total thickness of the proton conductive membrane is less than 50 microns. The ionomeric polymer is PFSA (perfluorinated sulfonic acid), PVP (polyvinylpyrrolidone) or PVA (poly vinyl alcohol) with iodide or bromide counterion dissolved inside. The graphene-like material is CVD graphene or reduced graphene oxide (rGO). A D to G Raman band ratio of the membrane is more than 0.1.

Smirnov, Sergei↗

DOE OSTI2023

Armor for Steel: Facile Synthesis of Hexagonal Boron Nitride Films on Various Substrates

Abstract While hexagonal boron nitride (hBN) has been widely used as a buffer or encapsulation layer for emerging electronic devices, interest in utilizing it for large‐area chemical barrier coating has somewhat faded. A chemical vapor deposition process is reported here for the conformal growth of hBN on large surfaces of various alloys and steels, regardless of their complex shapes. In contrast to the previously reported very limited protection by hBN against corrosion and oxidation, protection of steels against 10% HCl and oxidation resistance at 850 °C in air is demonstrated. Furthermore, an order of magnitude reduction in the friction coefficient of the hBN coated steels is shown. The growth mechanism is revealed in experiments on thin metal films, where the tunable growth of single‐crystal hBN with a selected number of layers is demonstrated. The key distinction of the process is the use of N 2 gas, which gets activated exclusively on the catalyst's surface and eliminates adverse gas‐phase reactions. This rate‐limiting step allowed independent control of activated nitrogen along with boron coming from a solid source (like elemental boron). Using abundant and benign precursors, this approach can be readily adopted for large‐scale hBN synthesis in applications where cost, production volume, and process safety are essential.

2D materials↗

DOE OSTI2022

Experimental Studies of Graphene-Coated Polymer Electrolyte Membranes for Direct Methanol Fuel Cells

The two main technical limitations of direct methanol fuel cells (DMFCs) are the slow kinetic reactions of the methanol oxidation reaction (MOR) in the anode and the crossing over of unreacted methanol through the proton exchange membrane (PEM). It is a common practice to use Nafion membranes as PEMs, which have high ion exchange capacity. However, Nafion-based membranes also have high fuel permeability, decreasing fuel utilization, and reducing the potential power density. This article focuses on using graphene-coated (Gr-coated) PEMs to reduce fuel crossover. Protons can permeate across graphene, and thus, it can be employed in various devices as a proton conductive membrane. Here, we report the efficiency of Gr-coated Nafions. We tested performance and crossover at three different temperatures with four different fuel concentrations and compared it to a Nafion PEM that underwent the same test conditions. We found that the adhesion of Gr on to PEMs is insufficient for prolonging fuel cell operation, resulting in Gr delamination at high temperatures and higher fuel crossover values compared to lower temperature testing. Furthermore, the results for 7.5M methanol fuel show a reduction of up to 25% in methanol crossover, translating to a peak power density that increases from 3.9 to 9.5 mW/cm 2 when using a Gr-coated PEM compared to a Nafion PEM at 30 °C.

25 ENERGY STORAGE↗

DOE OSTI2022

Proton selective membranes based on two dimensional materials

Proton conductive membrane includes a proton selective layer of 80-100% carbon with sp2 hybridization having a thickness of 0.3-100 nm, with 0-20% of hydrogen, oxygen, nitrogen and sp3 carbon; wherein the sp2 carbon is in a form of graphene-like material; the proton selective layer having a plurality of pores formed by any of 7, 8, 9 or 10 sp2 carbon cycles or a combination thereof, with the pores having an effective diameter of up to 0.6 nm; an ionomeric polymer layer on the proton selective layer. Total thickness of the proton conductive membrane is less than 50 microns. The ionomeric polymer is PFSA (perfluorinated sulfonic acid), PVP (polyvinylpyrrolidone) or PVA (poly vinyl alcohol) with iodide or bromide counterion dissolved inside. The graphene-like material is CVD graphene or reduced graphene oxide (rGO). A D to G Raman band ratio of the membrane is more than 0.1.

Smirnov, Sergei↗

DOE OSTI2022

Innovative Proton Conductive Membranes Based on Two-Dimensional Materials

The team of Oak Ridge National Laboratory, New Mexico State University, and General Graphene Corporation staff will develop and commercialize paradigm-shifting low-cost, high-performing, proton-conductive membranes made from abundant and durable 2D materials. Proposed membranes are expected to be an order of magnitude better in performance and cost compared with the current state-of-the-art formulation, Nafion, and thus are expected to eliminate huge roadblocks in proliferation of fuel cells and flow batteries. The major goal for this work is to develop a fundamentally new learning curve for novel proton exchange membranes needed for various applications. The new technology will overcome the shortcomings of the current state-of-the-art membranes that are based upon Nafion polymer by offering higher proton conductivities, the ability to operate at much lower external humidity levels and higher temperatures (>120°C), and negligible fuel and oxidant crossover through the membrane.

36 MATERIALS SCIENCE↗