DOE OSTI2023

A comprehensive material study of CdSeTe films deposited with differing selenium compositions

The addition of selenium into CdTe to create the ternary alloy CdSeTe has been one of the most impactful advancements to CdTe-based photovoltaics in the last decade. CdSeTe/CdTe bilayer device structures have enabled a gain in short-circuit current due to the narrower bandgap of the alloy, with minimal to no loss in voltage. Intensity of photoluminescence and time-resolved photoluminescence measurements suggest this is due to an increase in carrier lifetime and concomitant greater fraction of radiative vs non-radiative recombination events which allows for a reduction in the voltage deficit. Here, in this work, we study the properties of as-deposited and CdCl 2 -treated CdSeTe films deposited by close-space sublimation under varying conditions from CdSeTe source charges with both 20 and 40 mol% CdSe. We find that the selenium content in the deposited films are substantially reduced from that of the source material. Additionally, deposition temperature, particularly that of the substrate, considerably affects the grain size, crystallinity, and photoluminescence of the material, illustrating the importance of source material selection and process optimization. Finally, we present evidence that the source material, and therefore the properties of the deposited films, change over time as the source material is used.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Te/CdTe and Al/CdTe Interfacial Energy Band Alignment by Atomistic Modeling

A synergistic approach that incorporates first-principles atomistic modeling with numerical device simulations is used to systematically evaluate the role of heterointerfaces within metal-chalcogenide-based photovoltaic technologies. Two interfaces involving either a tellurium back contact or aluminum back electrode combined with a cadmium telluride absorber layer within cadmium-telluride-based thin-film solar cells are investigated on an atomic scale to determine the mechanisms contributing to variations in device performance. Electronic structures and predicted charge transport behavior with respect to cadmium and tellurium termination of the absorber layer are studied along the polar oriented CdTe{111} facets. The computational methodology reveals a noticeable contrast between the Schottky barrier forming Al/CdTe interface versus the Type I Te/CdTe heterojunction. Greater band bending features are exhibited by the cadmium termination as opposed to the tellurium termination for each interface case. Subsequent device modeling suggests that 3.6% higher photovoltaic conversion efficiency is achievable for the cadmium termination relative to the tellurium termination of the Te/CdTe interface. Based strictly on an idealistic representation, both interface models show the importance of atomic-scale interfacial properties for cadmium telluride solar cell device performance with their bulk properties being validated in comparison to published experimental data. Here, the synergistic approach offers a suitable method to analyze solar cell interfaces through a predictive computational framework for the engineering and optimization of metal-chalcogenide-based thin-film photovoltaic technologies.

Green’s function↗

DOE OSTI2021

Transparent MgO for Back-Contact Passivation of CdTe-Based Solar Cells

The passivating effects of MgO have been studied by integrating into an existing superstrate CdTe thin film solar cell device architecture. When implemented as an emitter to replace the typical MZO, the device performance was below par, but improved PL and TRPL was detected with significant carrier lifetimes in comparison to the MZO devices. However, when integrated at the back, the PL signal was detected upon the illumination of excitation laser from the back. This has opened the possibility of probing the back of the CdTe thin film solar cells with transparent back contact with improved back passivation and a bifacial device structure. Further, the TRPL measurements suggests that the MgO shows passivating effects to a CdTe surface irrespective of method of deposition implemented.

bifacial↗

DOE OSTI2021

Simulating the Effect of p-n Junction Fields on TRPL Transients of Thin-Film CdTe Solar Cells

Bias-dependent time-resolved photoluminescence (TRPL) transients of thin CdTe solar cells were simulated with the goal of characterizing the effect of p-n junction fields on photoluminescence decays. It was found that, although bulk lifetime could be accurately determined in field-free samples, electric field effects in solar cells lead to systematic underestimation of bulk lifetime. Modulating field strength with the application of external bias was found to have a major impact, a result corroborated by experimental data. In particular, p-n junction fields effects were found to be effectively suppressed when a cell is put far into forward bias, enabling accurate measurement of bulk lifetime in p-n junction structures.

CdTe↗

DOE OSTI2021

Submicron Thickness Characterization of Poly-Si Thin Films on Textured Surfaces by X-Ray Diffraction for Minimizing Parasitic Absorption in Poly-Si/SiO2 Passivating Contact Cells

Poly-Si/SiO2 passivating contacts have shown great potential for industry-relevant next-generation solar cells. Previous work has demonstrated an improved Jsc from dry reactive ion etching in an SF6 environment, using front metal grids as a self-aligned mask. Here, we show an effective method to measure the front poly-Si thickness on an alkaline textured surface using X-ray diffraction. The calculated thicknesses are compared with cross-section SEM analysis and Quokka simulation. We show that by thinning the front poly-Si from 200 nm to 60 nm, Jsc increases by 2.4 mA/cm2, leading to an absolute efficiency gain of 1.73%. Finally, we discuss possible reasons for the premature loss of passivation before the removal of all poly-Si.

41 EE - Solar Energy Technologies Office (EE-4S)↗

DOE OSTI2020

Field Effect in CdSeTe/CdTe Solar Cells with Biased Spectroscopy

Steady-state and time-resolved photoluminescence measurements were performed under external electrical bias on thin polycrystalline CdSeTe/CdTe solar cells. The results indicate that internal field effects which can go unnoticed during traditional, unbiased spectroscopy measurements may be more consequential than generally realized. In addition, probing the field behavior with bias may allow investigation of defect states and the determination of transport characteristics, such as mobility.

14 SOLAR ENERGY↗