Publications and source records attributed to Sindelar, Robert L..

34 records · Page 2

DOE OSTI2022

Nondestructive Evaluation of Stress Corrosion Cracking in a Welded Steel Plate Using Guided Ultrasonic Waves

Stress corrosion cracking (SCC) had occurred in early-generation high-level nuclear waste tanks constructed by welding carbon steel. This paper describes an ultrasonic inspection system and its fundamental ability to detect and quantify the length of SCC on thick welded steel plates. The finite element method (FEM) was applied to simulate the welding process to estimate the welding residual stress field. Growth of stress corrosion cracks is driven by crack stress intensities exceeding the subcritical cracking threshold intensity. The subject plate was experimentally inspected with ultrasonic nondestructive evaluation (NDE) techniques to characterize the extent of SCC. The NDE system uses a piezoelectric transducer to generate guided waves in the thick steel plate, and a scanning laser Doppler vibrometer (SLDV) to measure multidimensional time–space wavefield data over a user-defined scanning area in the plate surface. The measured wavefield data can show wave interactions in a localized area in the plate due to the presence of the discontinuities of the SCC. To generate an inspection image that can precisely show the crack’s location and/or the dimension, the wavefield data are further processed to generate inspection image that maps the entire sample plate so the crack can be clearly identified in the plate while its length can be readily estimated. In conclusion, the ultrasonic test results for crack length agree well with the visually estimated length and are close to that predicted by the FEM for cracks in the weld residual stress field.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Large Plate Experiment of Chloride-induced Stress Corrosion Cracking in Spent Nuclear Fuel Storage Canisters

This report is the comprehensive description of the completed experiment to evaluate the corrosion behavior of a large section of welded plate material harvested from the Sandia National Laboratories’ (SNL) full-size mockup of a spent nuclear fuel (SNF) dry storage canister. The plate was subjected to conditions aggressive to chloride-induced stress corrosion cracking for a total time of 2 years. The details of the establishment of this experiment, and the corrosion results are reported. This work is intended to inform aging management programs for SNF canisters under conditions of extended dry storage.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2021

Crack Stability in Breached Fuel

This report describes the fracture mechanics formalism to evaluate the stability of cracks in a fuel cladding. Recognized consensus-body linear elastic fracture mechanics (LEFM) was applied to identify the crack instability length, or the length at which unstable mechanical crack extension would occur, as a function of pellet swelling loading (radial strain and fraction conversion from UO 2 to U 3 O 8 ) at the local cracked cladding region for two postulated fracture toughness (K IC ) values of the cladding. The crack opening displacement (COD) and the crack opening area (COA) were also identified. This analysis informs evaluations for crack extension and the potential for pellet debris loss from the fuel rod for cases of pellet oxidation in dry storage canisters where inadvertent residual water may undergo radiolysis causing oxidizing conditions to pellets exposed to the canister environment through breached cladding.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2021

Test Plan for Investigation of Hydrogen Generation in SNF Canisters

This report presents a test plan to investigate radiolytic hydrogen generation in spent nuclear fuel (SNF) canisters containing Zr-based cladding materials. The initial primary contributor to the generation of radiolytic hydrogen is estimated to be the residual physisorbed water on the ZrO 2 film, post-dry out. Over the longer term the primary hydrogen source is associated with the aluminum hydroxides and water vapor. The proposed testing to be conducted in FY22 would consist of lab-scale testing on non-radioactive surrogates of oxidized ZIRLO tubing and unalloyed zirconium using a miniature steel canister (“mini-canister") designed to allow intermittent, in-situ sampling of the canister gas during irradiation. The mini-canister approach for irradiation with in-situ monitoring system was used in a recent and on-going study [McNamara and Verst, 2020a & 2020b; Verst et al., 2021] to measure radiolytic hydrogen generation from aluminum SNF cladding surrogate materials. This proposed testing will form part of the overall materials performance evaluation of the commercial SNF-in-canister system and is part of the technical bases for their continued safe dry storage

08 HYDROGEN↗

DOE OSTI2021

Crack Stability in Breached Fuel

22 GENERAL STUDIES OF NUCLEAR REACTORS↗

DOE OSTI2020

Technology Development for Aluminum-clad Spent Nuclear Fuel for Extended Dry Storage (Status Report)

A task group under the Spent Nuclear Fuel Working Group of the U.S. Department of Energy (DOE), Offices of Environmental Management (EM) and Nuclear Energy (NE) identified technical challenges (“information gaps"’) to the ability to provide for safe extended (>50 years) dry storage of Aluminum-Clad Spent Nuclear Fuel (ASNF) in a report issued in 2017, An Action Plan was developed, and a task- based program was launched under the sponsorship of DOE-EM, Office of Technology Development (EMTD) in October 2018 to close the gaps and complete the technical information set needed to implement extended dry storage with confidence. This interim status report summarizes the work to date of this EMTD program to complete the technical bases and demonstrate that extended dry storage is safe and viable.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Effects of Residual Water on Storage Canister Internal Components

This report describes an evaluation of the spent nuclear fuel cladding and canister internal materials’ corrosion/oxidation due to (inadvertent) residual free water inside a dry storage canister post-dryout. Drying of spent nuclear fuel (SNF) and the impact of (inadvertent) residual water in a SNF canister is being addressed under the DOE-NE Spent Fuel and Waste Science and Technology (SFWST) program to ensure the safe extended dry storage and transportation of commercial SNF. A long-standing understanding has been that the amount of residual water in a storage canister after vacuum drying is not expected to be much more than trace amounts of 0.43 gram mole. However, recent findings from the High Burnup Demonstration project, and an Integrated Research Project show that residual free water well above the amount of approximately 0.43 gm-moles that had been assumed for a 3 torr rebound pressure, may remain within an SNF canister following prototypic drying. In fact, an NRC-NMSS sponsored study considered residual water amount as high as 55 moles. Considering the recent findings and the NRC-sponsored work, this present work was conducted to study the effects of unspecified amount of residual water on oxidation and corrosion of canister internals, i.e., it was assumed that the residual water amount is not limiting. It was assumed that the spent nuclear fuel content in the canister is not exposed to the internal environment, i.e., the packaged canister does not contain any damaged (breached) fuel.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Large Plate Experiment of Chloride-induced Stress Corrosion Cracking in Spent Nuclear Fuel Storage Canisters

This report provides a description of the testing (in progress at the Savannah River National Laboratory) to evaluate the corrosion behavior of a large section of welded plate material harvested from the Sandia National Laboratories’ full-size mockup of a spent nuclear fuel (SNF) dry storage canister. The details of the establishment of this plate test, the interim corrosion results (from visual examination), and the general plan for examination of the plate in CY21 to evaluate crack growth behavior (if any) are provided. This work is intended to inform aging management programs for SNF canisters under conditions of extended dry storage. A “large plate” (approximately 51 x 46 cm with thickness 16 mm and weight about 30 kg) and containing a circumferential weldment from the mockup is the test specimen. The knowledge of the salt, temperature, humidity conditions for chloride-induced stress corrosion cracking (CISCC) including the threshold stress intensity factor, K iscc , were used to setup the large plate test in which a set of part-through-wall and through-wall electrical discharge machined (EDM) defects were positioned in the weld residual stress field of the welded plate material from the mockup canister. A marine salt solution was applied to this plate specimen with an air-brush spray, then dried, and then exposed to a sustained 71-73% RH condition at an ambient room temperature of 22 °C. The salt loading and environmental condition is expected to be aggressive to cause CISCC

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Evaluation of Hydrogen Generation in High Burnup Demonstration Dry Storage Cask

This report provides a best-estimate evaluation of residual water content (post-dry out) in the High Burnup (HBU) LWR Spent Fuel Demonstration project TN-32 cask, and evaluates the radiolysis of the residual free water, and the physisorbed and chemisorbed waters on the surfaces of the fuel and cask internal contents. The evaluation of radiolytic breakdown of those waters with gamma radiation causing the generation of hydrogen gas (H 2 ) is made using available literature data and models. This evaluation is part of the overall materials performance evaluation of the SNF-in-canister system, and is part of the technical bases for their continued safe dry storage. The TN-32 cask contents included 32 HBU LWR spent fuel assemblies each with 264 fuel rods clad in zirconium alloys, aluminum neutron absorber components, and aluminum and stainless steel structural components. The residual free and surface (physisorbed/chemisorbed) waters are ascribed to water vapor in the free volume and to components’ surfaces, respectively. The total potential radiolytic hydrogen inventory from the water vapor and from waters ascribed to surfaces has been calculated assuming all the water produced molecular H 2 . The residual water that is chemically incorporated into the bulk of a hydrated oxide, i.e., chemisorbed water, and its total potential hydrogen inventory has been calculated. These calculations are at the physical limit of material available and are used for a bounding assessment purpose only.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

Augmented Monitoring and Condition Assessment Program (AMCAP) Material Test Reactor (MTR) (Fuel Inspection Program Report)

The AMCAP MTR Fuel Inspection Program, a special inspection program comprised of four inspection campaigns, examined a total of ten (10) pre-selected aluminum-clad, aluminum-based fuel core spent nuclear fuel assemblies (ASNF) stored in the L Area Disassembly Basin (L Basin) at the Savannah River Site. A full description of the inspections and the results are reported. The fuel had been stored in bundled-tube storage (Vertical Tube Storage) for periods of 18 to 21 years. The prior service experience of the individual 10 assemblies varies, but all included irradiation followed by wet storage at international research reactor sites prior to shipment to the US and storage in L Basin. The 10 assemblies were expected to be among the “worst"’ in terms of prior corrosion damage of the entire inventory of the direct-bundle-stored ASNF in L Basin. The inventory of MTR ASNF in L Basin will continue to be stored in the bundled-tube configuration or in slug-storage buckets with inserts pending retrieval for ultimate disposition. The MTR fuel inspections focused on collecting information for characterization of the material condition of the ASNF considering various types of aluminum fuel corrosion degradation of its assembled materials in water storage. A custom-designed Fuel Inspection Table was used to stage the fuel for remote, enhanced visual examination (close-up video imaging & recording) with controlled lighting and positioning that enables reproducibility of imaging conditions. The inspections were conducted by fuel subject matter expert staff from Spent Fuel Project Engineering (SFPE) and the Savannah River National Laboratory (SRNL). Stills captured from the video records were used to compare the corrosion evolution from previous records, as available. This evaluation of the inspection results including the comparison to the previous inspection results demonstrate that the water quality and the storage configuration of ASNF in L Basin do not cause aggressive corrosion degradation of the fuel; mitigation of the prior corrosion degradation of the fuel also appears to have been achieved with the good water quality conditions of L Basin. Recommendations are made for future inspection of the fuel to trend corrosion degradation and demonstrate continued safe wet storage of the ASNF in L Basin. The next fuel examination is recommended to be performed in 5 years.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Thermal Dehydration of Aluminum (Oxy)hydroxides on Fuel Cladding Material - 20200

The aluminum cladding of research-reactor fuel undergoes general corrosion with resulting formation of adherent aluminum (oxy)hydroxide films during in-reactor and post-discharge exposure to water under various conditions and temperatures. These (oxy)hydroxides contain chemically-bound water that poses challenges for extended dry storage due to the risk of thermal or radiolytic decomposition releasing free water and/or hydrogen and oxygen gases. This study comprised laboratory experiments of thermal drying behavior of aluminum (oxy)hydroxides to identify approaches for reducing bound water on fuel cladding prior to sealed dry storage. Effective drying strategies for adherent (oxy)hydroxides on fuel cladding will improve the safety of dry storage by mitigating potential avenues for additional corrosion and/or generation of flammable gases inside the storage canister. This work is part of a broader investigation to address knowledge gaps and technical data needs for dry storage of aluminum-clad spent nuclear fuel (ASNF), which included investigation of (oxy)hydroxide formation on aluminum alloy substrates immersed in water, characterization of service-grown films from ASNF, and radiolytic yield of hydrogen from (oxy)hydroxide powders and films. The current work comprises experimental thermal dehydration of aluminum trihydroxides (bayerite and gibbsite) characteristic of low-temperature (<80 deg. C) corrosion in water and aluminum oxyhydroxide (boehmite) characteristic of high temperature (>80 deg. C) corrosion in water. First, commercially produced (oxy)hydroxide powders (boehmite and gibbsite) were tested via thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The effort aimed to identify or confirm key temperature ranges/thresholds for the thermal decomposition reactions, as well as impacts of ramp rate and hold times, for drying of isolated, high-surface-area (oxy)hydroxides. The information gleaned from powder tests was used to guide subsequent drying tests on adherent (oxy)hydroxide films grown on aluminum alloy substrates. TGA was used to analyze small samples of the aluminum coupons with adherent (oxy)hydroxide films. Specimens were characterized both pre- and post-drying using X-ray diffraction (XRD) to determine the film composition and scanning electron microscopy (SEM) to determine its morphology. Drying of adherent (oxy)hydroxide films was anticipated to pose additional complications relative to drying of (oxy)hydroxide powders. Anticipated challenges include achieving sufficient drying of the (oxy)hydroxide at low-enough temperature to avoid melting or other undesirable phase changes in the aluminum substrate and overcoming transport limitations of water through the thickness of a dense film or through a tortuous pore structure to reach the outer surface of the film. Inn addition, dehydration of (oxy)hydroxides significantly changes the film density, which may lead to substantial alterations in the morphology, including potential cracking and spalling of the film. TGA/DSC tests of gibbsite powders resulted in successful conversion to boehmite or alumina, depending on the maximum temperature reached. At low ramp rates (≤5 deg. C/min), the conversion to boehmite occurred around 300 deg. C (210-340 deg. C). XRD confirmed that boehmite was the only phase detected after tests reaching 450 deg. C. The transition to alumina occurred around 510 deg. C (470-550 deg. C), with XRD detecting only alumina after tests reaching at least 600 deg. C. Boehmite powders dehydrated to alumina at about 400 deg. C (330-460 deg. C) for coarse (77-μm particle diameter) powder and about 490 deg. C (420-520 deg. C) for fine (0.7-μm particle diameter) powder. For all powders tested, the maximum percent mass loss after drying to high temperature slightly exceeded the theoretical mass loss for complete dehydration of the stoichiometric (oxy)hydroxide to alumina, which is likely attributable to physisorbed water in the powder. Drying of a thick (∼8.6 μm), predominantly bayerite adherent film displayed a dramatic change in film morphology, with the initially continuous trihydroxide film cracking into sections on the order of 50 μm square and partially delaminating. The outermost layer of the film completely faked of in some regions. The layer exposed under the spalled oxide also displayed prominent cracking, with spacing on the order of 10 μm, but this surface layer appeared to remain completely adhered to the aluminum substrate. TGA showed mass losses per unit surface area up to ∼1.0 mg/cm{sup 2}. XRD characterization of the remaining oxide was inconclusive, with no crystalline phases detected. (authors)

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2020

(Oxy)hydroxides Formed on Aluminum Fuel Materials After Irradiation and Long-Term Wet Storage - 20354

The aluminum cladding of research-reactor fuel experiences general corrosion when in contact with water during in-reactor service and post-discharge wet storage, resulting in the formation of adherent aluminum (oxy)hydroxide films. These (oxy)hydroxides contain chemically-bound water that poses challenges for extended dry storage due to the risk of thermal or radiolytic decomposition releasing free water and/or hydrogen and oxygen gases. This study describes characterization of the (oxy)hydroxides present on several aluminum materials used in reactor operation and subsequently stored wet in the L-Basin storage facility at the Savannah River Site (SRS) for an extended period. Characterization data providing insight into the loading, composition, and morphology of (oxy)hydroxides to be expected on service-exposed aluminum cladding provides valuable benchmarks for designing adequate drying and dry-storage approaches. This work is part of a broader investigation to address knowledge gaps and technical data needs for dry storage of aluminum-clad spent nuclear fuel (ASNF), which included in-lab growth of (oxy)hydroxide films on aluminum alloy substrates to investigate formation behavior, investigation of drying methods to remove existing (oxy)hydroxides from ASNF cladding, and measurement of radiolytic yield of hydrogen from (oxy)hydroxide powders and films. In this study, (oxy)hydroxide films were characterized for three aluminum-alloy materials used in reactors and subsequently stored wet for up to approximately 40 years in L-Basin at SRS: one cropping from a Missouri University Research Reactor (MURR) fuel element (Al-6061 alloy), one cropping from a Universal Sleeve Housing (USH) (Al-6063 alloy), and one Mark-16B fuel assembly (either Al-6061 or Al- 6063). The USH and Mark-16B were used in SRS production reactors. Characterization of the as-received (oxy)hydroxides included scanning electron microscopy (SEM) in both plan-view and cross-section to characterize the (oxy)hydroxide layer's morphology, thickness, and structure. X-ray diffraction (XRD) was used to identify the chemical composition and distinguish between the various aluminum (oxy)hydroxides known to form under reactor and storage conditions. XRD analysis revealed both bayerite (Al(OH)3) and boehmite (AlOOH) on the surface of the MURR and USH samples, as well as bayerite, boehmite, and gibbsite (another Al(OH)3 polymorph) on the surface of the Mark-16B sample. The aluminum trihydroxides, bayerite and gibbsite, are typically associated with corrosion in low-temperature (<80 deg. C) water, while boehmite is expected to form at higher water temperature (>80 deg. C). The presence of bayerite on the USH, which is believed to have operated close to 90 deg. C, suggests that boehmite formed during in-reactor exposure was not protective against further hydroxide growth in low-temperature wet storage. Cross-section scanning electron microscopy (SEM) showed total (oxy)hydroxide layer thicknesses of ∼5- 10 μm for the MURR and ∼5-15 μm for the Mark-16B. The thickness of the USH's (oxy)hydroxide layer was indiscernible by the current mounting and imaging method, despite plan-view SEM and XRD confirming the presence of an (oxy)hydroxide layer. (authors)

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Consequence Analysis of Residual Water in a Storage Canister - 20484

Recent observations from projects sponsored under the DOE-Nuclear Energy Spent Fuel and Waste Disposition campaign show that residual free water, well above the 0.4 gm-moles that correspond to a 3 torr rebound pressure after a 30-minute hold following prototypic drying, may remain within SNF canisters used for long-term dry storage. Specifically, experimental observations in an Integrated Research Project showed subzero temperatures and a local pocket of frozen water in a mockup fuel assembly subjected to an industry practiced drying process. In gas sampling and analysis from the High Burnup (HBU) Demonstration project, using a fully loaded and dried SNF canister, indicated presence of 100 g of residual water had remained in the canister. The effects of residual water in terms of potential adverse impacts on the condition of the SNF and the canister internals during long-term dry storage has been rigorously evaluated to address inadvertent residual water contents. The impact of residual water on the fuel and canister internals, with a focus on the oxidation of the cladding and of postulated exposed (breached-clad) fuel, were evaluated using an integrated set of time-dependent environmental conditions with semi-empirical materials oxidation models. An 'integration model,' with coupled sub-models, developed and previously used by the Center for Nuclear Waste Regulatory Analysis (CNWRA), was applied and expanded with improved sub-models for water radiolysis, and for cladding and fuel oxidations. Cladding oxidation models for various alloys were developed using the rate constants for various cladding alloys in the dry storage temperature range. A burnup-dependent fuel oxidation model was developed; it accounted for inhibition effect of fission products on fuel oxidation rates. The potential for extension of the initial breach flaw (1 mm hole) was evaluated by two separate mechanics criteria. In the first case, a critical cladding strain criterion was used. In the second case, a critical stress intensity was used to evaluate stability of a planar axial flaw postulate. A failure condition exists when a sufficient amount of fuel oxidation (at the postulated breached-clad location) causes fuel pellet swelling to load the cladding to meet a mechanics criterion for flaw extension. The integration model's results provide the following insights. The radiolysis-generated oxygen is consumed with a partitioning between the cladding and the fuel. The extent of cladding oxidation is no more than 2 μm additional consumption of the cladding metal even with 10 moles of residual water, indicating that changes in cladding conditions due to water are expected to be negligible. The conditions for cladding failure (breach opening size extension) directly correlates with the extent of fuel oxidation. Fuel oxidation significant to extend the breach could occur even with 5.5 moles of residual water. The results indicate that fuel oxidation vis-a-vis cladding oxidation is more likely under a higher radiation field, i.e., when radiolytic decomposition of the residual water occurs in few years compared to several decades, and that the conditions to cause failure are increased with fuel and cladding temperatures approaching the peak storage temperature limit of 400 deg. C. (authors)

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Augmented Monitoring and Condition Assessment Program for SNF Wet Storage Life Extension - 20489

Approximately 27 MTHM of spent nuclear fuel (SNF) owned and managed by the U.S. Department of Energy, Office of Environmental Management is stored in the L Basin at the Savannah River Site (SRS). This 'DOE SNF' is comprised of approximately 12,000 aluminum-clad, aluminum-based fuel assemblies (∼7 MTHM), and approximately 2000 non-aluminum fuel assemblies (∼20 MTHM). A program is in progress to perform Non-Destructive Examination (NDE) of the fuel and their storage containers to characterize the materials' condition, and to evaluate the effects of service to enable continued safe wet storage of the SNF. The Augmented Monitoring and Condition Assessment Program (AMCAP), a two-part program to develop and implement remote underwater Non-Destructive Examination of the aluminum SNF, and of the containers of the non-aluminum SNF, respectively, is aimed at the characterization and evaluation of corrosion degradation of aluminum fuel and container materials. The predominant design of the aluminum SNF (ASNF) stored in L Basin is the Materials Test Reactor (MTR) equivalent design, a plate fuel design. These SNF are stored in 5'' diameter tubes or 5'' x 5'' squares (called bundles) that are nominally 12' or up to 14' long. The SNF is de-bundled and inspected using a custom-designed MTR Fuel Inspection Table. The inspection table provides for indexed fuel positioning for a video camera examination with controlled lighting. A total of 10 of the SNF originating from foreign research and test reactors were selected for examination based on burnup, enrichment, and prior damage caused by service/storage history. A special inspection campaign of these 10 assemblies is in progress. The observed corrosion damage included minor to moderate attack from general corrosion, pitting, crevice, end grain and galvanic corrosion. Example results from the completed inspections are shown and discussed. The focus is a comparison of the as-received condition versus the as-found current storage condition that will serve to validate Water Chemistry and Corrosion Monitoring Programs. The non-aluminum SNF (NASNF) stored in L Basin are of diverse design that includes various geometries with claddings of stainless steel, Zircaloy, and Hastelloy. The fuel core materials include uranium alloys, oxides/mixed oxides, and carbides. These SNF materials, originating from early experimental and test reactors, are in various physical forms including single fuel elements and cut pieces. The fuel is stored in L Basin in various configurations including in direct bundled storage in aluminum tubes and in isolation cans that are in the bundles or in a larger over-size storage container (OSC). Concern with inside-out corrosion and the potential loss of configuration control and ability to handle the storage containers prompted the development of remote NDE methods that include visual and UT technologies to assess the condition of the containers. Candidate stored materials were selected for a special inspection campaign; the development of the NDE methods for the inspection for galvanic, crevice and sediment-induced corrosion (inside-out) are discussed. A summary of the SNF storage in L Basin at the SRS, and an overview of the AMCAP to enable continued safe storage of DOE SNF are described. (authors)

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Technology Development for Dry Storage of Aluminum-Clad Spent Nuclear Fuel - 20490

A candidate disposition pathway for the > 13 MTHM of aluminum-clad spent nuclear fuel (ASNF), owned and managed by the U.S. Department of Energy, is the drying and placement of the SNF into sealed-canister dry storage, with the ASNF-in- canisters 'road-ready' for transportation to and final direct disposal in a repository waste package. Technical information gaps in fuel drying, and fuel dry storage behavior, have previously challenged the declaration of technology readiness for drying and placement of this fuel into the DOE Standard Canister design for > 50 years of safe dry storage. The principal technical information gaps included: i) characterization and thermal dehydration behavior of aluminum (oxy)hydroxide films attendant on the cladding due to film formation during reactor operation and during post-discharge up to long-term wet storage histories; and ii) G-value data to enable estimation of the radiolytic gas generation from the cladding with its (oxy)hydroxide films. Thus, the oxide films on the ASNF challenged the safety of a sealed storage canister with thermal and radiolytic decomposition of the waters on the films that can lead to corrosion, pressurization, and flammability issues. These gaps in the technical information base have largely been closed. This paper discusses the investigations at the Idaho National Laboratory (INL) and the Savannah River National laboratory (SRNL), and outlines the pending technology development work for input to an engineering design to enable a road-ready dry storage system for ASNF. The ASNF inventory considered for road-ready dry storage is stored at the Savannah River Site (SRS) and at the Idaho Nuclear Technology and Engineering Center (INTEC) at the INL. The ASNF inventory in the SRS L Basin is from foreign and domestic research reactors (FRR and DRR), and is diverse in terms of design, irradiation, and post-reactor-discharge storage conditions; these factors yield a range of characteristics of cladding oxide films on ASNF. Mixed aluminum (oxy)hydroxide (boehmite and bayerite/gibbsite) films, non-uniform in thicknesses up to a maximum local thickness bounded by 25 μm, were observed on ASNF materials removed from wet storage in the L Basin and in non-sealed dry storage at the SRS following reactor service and a long-term (up to 40+ years) interim storage history. The ASNF inventory at INTEC, in both wet and vented dry storage, is predominantly from the Advanced Test Reactor (ATR), but it also includes DRR and FRR fuel. To address a profound behavior of these films, radiolysis testing of aluminum specimens with mixed type boehmite/bayerite oxide films was performed to develop basic data on G-values for production of radiolytic hydrogen under dry storage conditions with nominal relative humidity, temperature, and cover gas. Modeling and simulation of canister internal environments with postulated inventories of oxide films provides estimation of the evolution of the conditions of the canister loaded with ASNF. Simultaneous Thermal Analysis (TGA/DSC) of hydrated oxide powders, and laboratory-scale aluminum specimens with a bayerite film (∼10 μm) using TGA methods, inform drying time/temperature conditions to be used for the ASNF. A demonstration project is recommended for Verification and Validation of the drying and storage of the ASNF. Remaining major tasks leading up to the hot demonstration include scale-up radiolysis testing and scale-up drying testing. Engineering design with the information from the technology program will establish the safety basis and enable long-term (> 50 years) dry storage compatibility with ASNF in the DOE Standard Canister pending its transportation to and disposal in a repository. This full capability would show the ASNF-in-canister storage system to be road-ready. (authors)

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗

DOE OSTI2020

Evaluation of Radiolysis Data for Hydrogen Gas Generation During Gamma Irradiation of Pre-Corroded and Pristine Aluminum Samples - An Aluminum SNF Dry Storage Study Interim Report

Information and data from radiolysis testing to measure hydrogen (H₂) generated from hydrated oxides on aluminum exposed to ⁶⁰Co radiation were reviewed to evaluate hydrogen generation with radiation dose. Hydrogen generation rate is a primary input to the coupled thermal-chemical system model of the performance of aluminum-clad spent nuclear fuel in a dry storage canister (ASNF-in-canister) over its storage life. Hydrogen generation data and hydrogen generation rate (hydrogen generated per absorbed radiation dose, $\Delta$(H₂)/$\Delta$(dose)) were reported in two reports for radiolysis testing [1, 2]. The testing involved first-time data¹ for radiolytic yield of hydrogen from hydrated-oxides-on-aluminum substrates, and from pristine (non-corroded) aluminum substrates. The laboratory-grown hydrated-oxides-on-aluminum substrates contained a ~ 5 μm film consisting of the trihydroxide bayerite (Al(OH)₃) with amounts of the oxyhydroxide boehmite (AlOOH). These specimens were assumed to also contain physisorbed water (unquantified). The pristine substrates were flat coupons of aluminum that were ground to a 600-grit finish but were not immersed in water to grow a hydrated oxide. The pristine substrates were tested as companion specimens to provide information on hydrogen generation from material without chemisorbed water and were assumed to contain physisorbed water (unquantified).

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗