High gradient off-axis coupled C-band Cu and CuAg accelerating structures

Here, we report the high gradient testing results of two single-cell off-axis coupled standing wave accelerating structures. Two brazed standing wave off-axis coupled structures with the same geometry were tested: one made of pure copper (Cu) and one made of a copper–silver (CuAg) alloy with a silver concentration of 0.08%. A peak surface electric field of 450 MV/m was achieved in the CuAg structure for a klystron input power of 14.5 MW and a 1 μs pulse length, which was 25% higher than the peak surface electric field achieved in the Cu structure. The superb high gradient performance was achieved because of the two major optimizations in the cavity's geometry: (1) the shunt impedance of the cavity was maximized for a peak surface electric field to accelerating gradient ratio of ~2 for a fully relativistic particle, and (2) the peak magnetic field enhancement due to the input coupler was minimized to limit pulse heating. These tests allow us to conclude that C-band accelerating structures can operate at peak fields similar to those at higher frequencies while providing a larger beam iris for improved beam transport.

71 CLASSICAL AND QUANTUM MECHANICS, GENERAL PHYSIC↗

DOE OSTI2020

Shaped Beams from Diamond Field-Emitter Array Cathodes

Diamond field-emitter arrays (DFEAs) are arrays of diamond pyramids with exquisitely sharp tips and micrometer-scale bases that produce high current densities. These arrays can be fabricated in arbitrary shapes, ranging from single tips to many millions of tips, so that they produce an inherently shaped electron beam. Each tip emits a modest current, but the large dense array can produce many Amps. We are investigating these cathodes for use in dielectric wakefield accelerators; however, they may also be applicable to vacuum microwave tubes. Recently, shaped beam production and transport have been demonstrated in the 1.3-GHz RF gun at the Argonne Cathode Test Stand at the Argonne National Laboratory. The charge was measured on a Faraday cup and the beam imaged on a YAG screen with peak electric field gradients on the cathode ranging from 12 to 35 MV/m. Three cathode geometries were tested: one 1-mm equilateral triangle with 7-mu m base pyramids and 10-mu m pitch, one 1-mm equilateral triangle with 10-mu m base and 25-mu m pitch, and one sparse 5 x 5 square array with 20-mu m base and 400-mu m pitch. The two triangular arrays emitted 35 nC in an RF macropulse at 35 MV/m and 13-nC charge at 27 MV/m, respectively, while the sparse array emitted 0.060-nC charge at 15 MV/m. This article presents the results of the triangular array experiments, including damage due to breakdown in the RF gun and initial models of tip-to-tip shielding.

Cathodes↗