All sourcesNASA NTRSDOE OSTI
NASA NTRS1982

JT90 Ceramic Outer Air Seal System Refinement Program, Phase 2

The sprayed ceramic gas turbine outer air seal system was tested in two JT9D engines to substantiate the abradability and durability of the seals. Of particular significance was that one of the tests, a 150 hour 1000 cycle endurance program at nominal JT9D operating conditions, was completed with minimal effect on the seals and received Federal Aviation Administration cognizance with respect to potential field service use by the airlines. The other engine test completed 1825 endurance cycles at severe operating conditions and no burn through or other serious defects in the structural integrity of a seal segment was observed. These test results combined with other Pratt and Whitney Aircraft engine tests substantiate the potential of the ceramic outer air seal system to attain the durability goal of 50000 hour engine operating capability. Both engine tests subjected the seals to intentional blade rubs and demonstrated good abradability with volume wear ratios greater than 100, far exceeding the design goal of 10. The improved volume wear ratio will allow the turbine tip clearance to be reduced, thereby resulting in an estimated thrust specific fuel consumption improvement of 0.3 percent.

Shiembob, L. T.↗
NASA NTRS1980

Some considerations of the performance of two honeycomb gas path seal material systems

A standard Hastelloy-X honeycomb material and a pack aluminide coated honeycomb material were evaluated as to their performance as labyrinth seal materials for aircraft gas turbine engines. Consideration from published literature was given to the fluid sealing characteristics of two honeycomb materials in labyrinth seal applications, and their rub characteristics, erosion resistance, and oxidation resistance were evaluated. The increased temperature potential of the coated honeycomb material compared to the uncoated standard could be achieved without compromising the honeycomb material's rub tolerance, although there was some penalty in terms of reduced erosion resistance.

Bill, R. C.↗
NASA NTRS1980

Development of improved high pressure turbine outer gas path seal components

A plasma sprayed graded layered ceramic/metallic (ZrO2/CoCrAlY) seal was evaluated for JT9D turbine application by rig and engine tests. Four cyclic thermal shock rig tests were conducted during the program. Three completed 1000 simulated engine thermal cycle tests and the fourth completed 500 cycles without severe cracking or spalling. Three ceramic seals were installed in a JT9D experimental engine to evaluate the effect of the engine thermal environment on the seals. All three seals completed the test successfully without severe cracking or spalling. The three seals did have slight laminar cracks at the 85/15-40/60 ZrO2/CoCrAlY interface. The second engine test evaluated the rub capabilities of the seal. Six ceramic seals were installed in the engine with fourteen abrasive tip blades. Three of the six seals rubbed to a depth of 24 mils. Eight of the fourteen abrasive tip blades showed evidence of wear. Three of the eight blades wore a maximum of five mils. Engine rub test results demonstrated the potential of reducing turbine clearances and thereby improving engine performance by use of sprayed ceramic seals.

Shiembob, L. T.↗
NASA NTRS1979

Development of a plasma sprayed ceramic gas path seal for high pressure turbine applications

Development of the plasma sprayed graded, layered ZrO2/CoCrAlY seal system for gas turbine engine blade tip seal application up to 1589 K (2400 F) surface temperature was continued. Methods of improvement of the cyclic thermal shock resistance of the sprayed zirconia seal system were investigated. The most promising method, reduction of the ceramic thickness and metallic substrate stiffness were selected based upon potential and feasibility. Specimens were fabricated and experimentally evaluated to: (1) substantiate the capacity of the geometry changes to reduce operating stresses in the sprayed structure; and (2) define the abradability, erosion, thermal shock and physical property characteristic for the sprayed ceramic seal system. Thermal stress analysis was performed and correlated with thermal shock test results.

Shiembob, L. T.↗
NASA NTRS1978

Development of a plasma sprayed ceramic gas path seal for high pressure turbine application

Development of the plasma sprayed graded, layered ZRO2/CoCrAlY seal system for gas turbine engine blade tip seal applications up to 1589 K (2400 F) surface temperature was continued. The effect of changing ZRO2/CoCrAlY ratios in the intermediate layers on thermal stresses was evaluated analytically with the goal of identifying the materials combinations which would minimize thermal stresses in the seal system. Three methods of inducing compressive residual stresses in the sprayed seal materials to offset tensile thermal stresses were analyzed. The most promising method, thermal prestraining, was selected based upon potential, feasibility and complexity considerations. The plasma spray equipment was modified to heat, control and monitor the substrate temperature during spraying. Specimens were fabricated and experimentally evaluated to: (1) substantiate the capability of the thermal prestrain method to develop compressive residual stresses in the sprayed structure and (2) define the effect of spraying on a heated substate on abradability, erosion and thermal shock characteristics of the seal system. Thermal stress analysis, including residual stresses and material properties variations, was performed and correlated with thermal shock test results. Seal system performance was assessed and recommendations for further development were made.

Shiembob, L. T.↗
NASA NTRS1978

Development of sprayed ceramic seal systems for turbine gas path sealing

A ceramic seal system is reported that employs plasma-sprayed graded metal/ceramic yttria stabilized zirconium oxide (YSZ). The performance characteristics of several YSZ configurations were determined through rig testing for thermal shock resistance, abradability, and erosion resistance. Results indicate that this type of sealing system offers the potential to meet operating requirements of future gas turbine engines.

Bill, R. C.↗
NASA NTRS1977

Development of a plasma sprayed ceramic gas path seal for high pressure turbine applications

The plasma sprayed graded layered yittria stabilized zirconia (ZrO2)/metal(CoCrAlY) seal system for gas turbine blade tip applications up to 1589 K (2400 F) seal temperatures was studied. Abradability, erosion, and thermal fatigue characteristics of the graded layered system were evaluated by rig tests. Satisfactory abradability and erosion resistance was demonstrated. Encouraging thermal fatigue tolerance was shown. Initial properties for the plasma sprayed materials in the graded, layered seal system was obtained, and thermal stress analyses were performed. Sprayed residual stresses were determined. Thermal stability of the sprayed layer materials was evaluated at estimated maximum operating temperatures in each layer. Anisotropic behavior in the layer thickness direction was demonstrated by all layers. Residual stresses and thermal stability effects were not included in the analyses. Analytical results correlated reasonably well with results of the thermal fatigue tests. Analytical application of the seal system to a typical gas turbine engine application predicted performance similar to rig specimen thermal fatigue performance. A model for predicting crack propagation in the sprayed ZrO2/CoCrAlY seal system was proposed, and recommendations for improving thermal fatigue resistance were made. Seal system layer thicknesses were analytically optimized to minimize thermal stresses in the abradability specimen during thermal fatigue testing. Rig tests on the optimized seal configuration demonstrated some improvement in thermal fatigue characteristics.

Shiembob, L. T.↗
NASA NTRS1977

Friction and wear of sintered fibermetal abradable seal materials

Three abradable gas-path seal-material systems based on a sintered NiCrAlY fiber metal structure were evaluated under a range of wear conditions representative of those likely to be encountered in various knife-edge seal (labyrinth or shrouded turbine) applications. Conditions leading to undesirable wear of the rotating knife were identified, and a model proposed based on thermal effects arising under different rub conditions. It was found, and predicted by the model, that low incursion (plunge) rates tended to promote smearing of the low-density sintered material with consequent wear to the knife edge. Tradeoff benefits between baseline 19 percent dense material, a similar material of increased density, and a self-lubricating coating applied to the 19 percent dense material were identified on the basis of relative rub tolerance and erosion resistance.

Bill, R. C.↗
NASA NTRS1977

Friction and wear of sintered fiber-metal abradable seal materials

Three abradable gas path seal material systems based on a sintered NiCrAlY fibermetal structure were evaluated under a range of wear conditions representative of those likely to be encountered in various knife-edge seal (labyrinth or shrouded turbine) applications. Conditions leading to undesirable wear of the rotating knife were identified and a model was proposed based on thermal effects arising under different rub conditions. It was found, and predicted by the model, that low incursion (plunge) rates tended to promote smearing of the low density sintered material with consequent wear to the knife-edge. Tradeoffs benefits between baseline 19 percent dense material, a similar material of increased density, and a self lubricating coating applied to the 19 percent material were identified based on relative rub tolerance and erosion resistance.

Bill, R. C.↗
NASA NTRS1975

Continued development of abradable gas path seals

Major program objectives were the continued development of NiCrAlY feltmetal and honeycomb systems for knife edge seal applications in the 1144 to 1366 K temperature range, and to initiate abradable seal material evaluation for blade tip seal applications in the 1366 to 1589 K temperature range. Larger fiber size, higher density feltmetal showed greatly improved erosion resistance with a slight reduction in abradability compared to the baseline feltmetal. Pack aluminide coating of the honeycomb extended the oxidation resistance and slightly improved the abradability of this material. Evaluation through selected abradability, erosion and oxidation testing, and pertinent metallography led to selection of a plasma sprayed yttria stabilized zirconia (ZrO2)/CoCrAlY layered system as the system with the most potential to meet the 1589 K requirement for blade tip seals. This system demonstrated structural integrity, erosion resistance, and some degree of abradability.

Shiembob, L. T.↗