Nanoscale clustering and fission product segregation in irradiated annular U-10Zr fuel

Zirconium (Zr) is added to uranium (U) to improve the performance of metallic fuel for fast reactor applications. This study employs transmission electron microscopy (TEM) and atom probe tomography (APT) to investigate nanoscale clustering of U and Zr, as well as segregation of fission products (FPs), in annular U-10Zr (in weight) metallic fuel irradiated at the Advanced Test Reactor (ATR). The results reveal variations in the shape, size, and chemical composition of clusters at different radial locations within the irradiated fuel cross-section. Zr-rich clusters exhibit higher concentration of FPs compared to U-rich clusters, potentially due to the co-precipitation of Zr and FPs in the fuel matrix during cooling at the end-of-life. In conclusion, this work complements the study of fuel constituents and fission product distribution across multiple length scales in irradiated U-10Zr metallic fuel.

Atom probe tomography↗

DOE OSTI2025

Irradiation-induced formation of G-phase precipitates and M 2 X carbides in self-ion irradiated HT-9

Ferritic-martensitic steels with high chromium content are a promising material group for advanced nuclear systems due to their high temperature strength and good irradiation tolerance. HT-9 is an optimized and often-studied alloy in this group, but additional studies are required on its radiation response under extreme conditions to be experienced in various types of nuclear reactors, especially with respect to phase stability under irradiation. Self-ion irradiation of HT-9 by 5 MeV Fe ions was used to simulate neutron-induced behavior reaching peak doses of 100 and 300 dpa at temperatures ranging from 450 to 550 °C. M 23 C 6 carbides that existed prior to irradiation were found to remain stable under all examined irradiation conditions. As irradiation progressed at 450 and 500 °C, however, formation of spherical-like G-phase precipitates and needle-like M 2 X carbides was observed. G-phase precipitates were found to be enriched in Ni, Si, and Mn, and show no interface segregation, whereas needle-like M 2 X carbides were rich in Cr and Mo and clearly displayed interface segregation of Ni and Si. M 2 X carbide formation is believed to be assisted by vacancies, while G-phase precipitation is thought to be assisted by interstitials. Finally, this difference in defect-mediated formation leads to a difference in distribution with depth. M 2 X carbides are distributed over shallower depths than that of G-phase precipitates, consistent with defect imbalance predictions that consider the influence of the injected interstitial effect.

atom probe tomography↗

DOE OSTI2025

Local chemical ordering of a neutron-irradiated CrFeMnNi compositionally complex alloy

While ion-irradiation studies are a critical first step in studying compositionally complex alloys (CCAs) for nuclear applications, they do not capture all the microstructural changes occurring under the low irradiation dose rates and different particles’ scattering patterns experienced in a nuclear reactor setting. To explore these phenomena in reactor-relevant conditions for the first time in CCA, the single-phase solid-solution Cr 10 Fe 30 Mn 30 Ni 30 was neutron irradiated up to 6.61 displacements per atom at 395 and 579 °C. Irradiation-enhanced local chemical ordering (LCO) well beyond the range of short range ordering was observed, and is predicted to be the precursor to the precipitation of a coherent Ni-Mn L1 0 phase and a Cr-rich α’ phase, though TEM analysis did not indicate the presence of either in any irradiation condition. The line density of faulted dislocation loops decreased from 6.47 to 1.69 ∙ 10 15 m -2 from 3.43 to 6.61 dpa at 579 °C despite no appreciable faulted loop content in the unirradiated material. LCO is expected to increase the complexity of the energy landscape within this alloy, restricting interstitial point defect mobility and creating local regions of greater stacking fault energy. These contribute to the negative correlation between irradiation dose and faulted dislocation loop density in this study, as well as the lack of void swelling observed.