NASA NTRS2019

Characterizing Damage Accumulation in CMCs

Silicon carbide / silicon carbide ceramic matrix composites (SiC/SiC CMCs) are structural ceramics that are well-suited for the extreme environment conditions of aerospace applications largely due to their low weight, creep resistance, damage tolerance, and high specific strength. In CMCs, the initiation and evolution of damage is influenced by a number of factors including characteristics of the constituent landscape (porosity, interfacial properties, and geometric distribution of CMC constituents), thermo-mechanical loading parameters, and environmental conditions. However, much is still unknown about these factors and the interactions between them. In order to accurately predict the lifetimes of these advanced composites, it is critical to understand the evolution of damage and to characterize which early damage mechanisms (and their relationship to key microstructural features) subsequently lead to crack coalescence and macroscopic failure. This research focuses on the use of a multi-modal, experimental approach to examine the relative activity of surface and subsurface damage mechanisms in CMCs. The impact of fabrication choices on the evolution of damage to final failure, and the influence of constituent architecture on early damage mechanisms, are investigated. This approach combines acoustic emission (AE) with microscale deformation tracking via digital image correlation inside a scanning electron microscope (SEM-DIC). The potential application of this combined approach towards characterization of damage in SiC/SiC CMCs under more complex testing conditions is explored.

Swaminathan, Bhavana↗

NASA NTRS2017

Crack Opening Displacement Behavior in Ceramic Matrix Composites

Ceramic Matrix Composites (CMC) modeling and life prediction strongly depend on oxidation, and therefore require a thorough understanding of when matrix cracks occur, the extent of cracking for given conditions (time-temperature-environment-stress), and the interactions of matrix cracks with fibers and interfaces. In this work, the evolution of matrix cracks in a melt-infiltrated Silicon Carbide/Silicon Carbide (SiC/SiC) CMC under uniaxial tension was examined using scanning electron microscopy (SEM) combined with digital image correlation (DIC) and manual crack opening displacement (COD) measurements. Strain relaxation due to matrix cracking, the relationship between COD's and applied stress, and damage evolution at stresses below the proportional limit were assessed. Direct experimental observation of strain relaxation adjacent to regions of matrix cracking is presented and discussed. Additionally, crack openings were found to increase linearly with increasing applied stress, and no crack was found to pass fully through the gage cross-section. This observation is discussed in the context of the assumption of through-cracks for all loading conditions and fiber architectures in oxidation modeling. Finally, the combination of SEM with DIC is demonstrated throughout to be a powerful means for damage identification and quantification in CMC's at stresses well below the proportional limit.

acoustic emission↗

NASA NTRS2016

InSitu SEM Investigation of Microstructural Damage Evolution and Strain Relaxation in a Melt Infiltrated SiC/SiC Composite

With CMC components poised to complete flight certification in turbine engines on commercial aircraft within the near future, there are many efforts within the aerospace community to model the mechanical and environmental degradation of CMCs. Direct observations of damage evolution are needed to support these modeling efforts and provide quantitative measures of damage parameters used in the various models. This study was performed to characterize the damage evolution during tensile loading of a melt infiltrated (MI) silicon carbide reinforced silicon carbide (SiC/SiC) composite. A SiC/SiC tensile coupon was loaded to a maximum global stress of 30 ksi in a tensile fixture within an SEM while observations were made at 5 ksi increments. Both traditional image analysis and DIC (digital image correlation) were used to quantify damage evolution. With the DIC analysis, microscale damage was observed at the fiber-matrix interfaces at stresses as low as 5 ksi. First matrix cracking took place between 20 and 25 ksi, accompanied by an observable relaxation in strain near matrix cracks. Matrix crack opening measurements at the maximum load ranged from 200 nm to 1.5 m. Crack opening along the fiber-matrix interface was also characterized as a function of load and angular position relative to the loading axis. This characterization was funded by NASA GRC and was performed to support NASA GRC modeling of SiC/SiC environmental degradation

testing↗