Senanayake, Sanjaya D.

Publications and source records attributed to Senanayake, Sanjaya D..

At least 19 records
All sourcesNASA NTRSDOE OSTI
DOE OSTI2024

The Triple Component Interface of Ni–Co–Ce: Growth, Chemical State, and Stability of NiCo Bimetallic Particles on Reducible CeO 2 (111) Thin Films

The growth of NiCo particles at low coverages over reducible CeO 2 (111) thin films producing a triple interface between Ni-Co-Ce was investigated by scanning tunneling microscopy (STM) and X-ray photoelectron spectroscopy (XPS), which was compared to that of monometallic Ni and Co particles. XPS data show that deposition of either Ni or Co on CeO 2 at 300 K causes a partial reduction of Ce 4+ cations to Ce 3+ ions. At 0.3 monolayer (ML), XPS detects Co 2+ on CeO 2 . However, both Ni 0 and Ni 2+ are present as major species at 300 K and annealing causes a significant increase of Ni 2+ in Ni particles. Deposition of 0.3 ML Co over 0.3 ML Ni on CeO 2 at 300 K induces reduction of Ni 2+ to metallic Ni and Ni 0 was found as predominant species. Unlike for Co/CeO 2 , metallic Co was also present over the Co-Ni/CeO 2 surface in addition to Co 2+ . Further, this behavior indicates the formation of NiCo bimetallic particles with the possibility of Co diffusion to the interface of Ni/ceria. With heating, the intermixing of Ni and Co atoms in bimetallic particles on CeO 2 was facilitated. Furthermore, oxidation of both metals and ceria occurred as a result of the diffusion of lattice oxygen from the bulk of ceria to the surface. A slight increase in Ni 2+ was observed after heating Co-Ni/CeO 2 to 500 K or higher. Co became Co 2+ with heating to 800 K. Our STM results confirm the formation of NiCo bimetallic particles on CeO 2 at 300 K and further suggest that the addition of Co can help inhibit the sintering of Ni particles at higher temperatures. Bimetallic particles were also obtained by depositing Ni over existing Co particles on CeO 2 . However, our XPS data demonstrate that the deposition order of Co and Ni plays a role in the chemical state of these two metals in bimetallic particles, likely attributed to the difference in their compositions at the bimetallic particle surface as well as the metal-support interface.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2024

Understanding the morphology and chemical activity of model ZrO x /Au (111) catalysts for CO 2 hydrogenation

In this study, the growth of ZrO x on Au (111) was investigated using scanning tunneling microscopy (STM) and synchrotron-based ambient pressure X-ray photoelectron spectroscopy (AP-XPS). Nanostructures of ZrO x (x= 1,2) at the sub-monolayer (≤ 0.3 ML) level were prepared by vapor depositing Zr metal onto Au (111) followed by oxidation with O 2 or CO 2 . At low coverages of the admetal (< 0.05 ML), the formed ZrO x nanostructures were dispersed randomly on the terraces and steps of the Au(111) substrate. Strong oxide-metal interactions prevented the formation of islands of zirconia. The ZrO x nanostructures displayed a reactivity towards CO 2 and H 2 not seen for bulk zirconia. C 1 s AP-XPS results indicated that CO 2 molecules adsorbed on Zr/ZrO x /Au(111) surfaces could undergo partial decomposition on Zr (CO 2 , gas → CO gas + O ads ), or react with oxygen sites from ZrO x to yield carbonates (Zr-CO 3, ads ). Further, after exposing ZrO 2 /Au (111) surfaces to 1:3 mixtures of CO 2 :H 2 , the formation of HCOO, CO 3 , and CH 3 O was detected in AP-XP spectra. These chemical species decomposed at temperatures in the range of 400-600 K, making them possible reaction intermediates for methanol synthesis.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2024

CO 2 hydrogenation over rhodium cluster catalyst nucleated within a manganese oxide framework

Rhodium-based manganese oxide frameworks were explored as a prototype for carbon dioxide reactive capture and conversion. Three-dimensional frameworks of MnOx were utilized as support structures to isolate Rh metal centers. V, Na, and Zn were introduced as counterions to stabilize the structure and for their beneficial effect as promoters. Here, with this multicomponent catalyst, Rh active centers with MnOxs and varied counterions, we were able to selectively tune the catalytic performance of the material via the choice of counterion and structure of the host material. With cryptomelane-type tunnel manganese oxides octahedral molecular sieve (OMS2), we found that Rh-V-OMS2 was highly stable even after 48 hours on stream with a reaction rate of around 1.5x10 -4 mol CO 2 /g Rh /s, surpassing the net reactivity of other initially more active combinations. Furthermore, during CO 2 hydrogenation, in situ XAFS showed that single Rh atoms nucleated into nanoparticles/ sub-nanometer clusters with a coordination number of 5.5 or less. Our finding of the correlation between the reaction rate and particle size offers the potential for enhanced control over the reaction rate by tuning particle size. Our activity study with control experiments demonstrates that the activities of the catalysts are proved due to the unique metal support interaction offered by the Rh-X-MnO.

10 SYNTHETIC FUELS↗
DOE OSTI2024

The Surface Chemistry of Methanol on Pd(111) and H–Pd(111) Surfaces: C–O Bond Cleavage and the Effects of Metal Hydride Formation

Palladium catalysts are frequently employed in processes where methanol is an energy vector or carrier, being useful for the synthesis of methanol from mixtures of carbon dioxide and hydrogen (CO 2 /H 2 ) or its steam reforming on demand. Results of synchrotron-based ambient pressure X-ray photoelectron spectroscopy for the adsorption of methanol on a Pd(111) model catalyst show a rich surface chemistry and complex phenomena that strongly depend on pressure and temperature. At low pressures (< 10 -6 Torr) and temperatures (< 300 K), CO is the dominant decomposition product. Further, as the pressure increases, cleavage of C-H, O-H and C-O bonds is observed, and at elevated temperatures (400-600 K) the formation of CO and CH x /C fragments compete on the surface. Thus, existing reaction networks for methanol decomposition must be modified. Furthermore, surface and subsurface hydrogen (coming from PdH x ) play a significant role in the stability and removal of CH x and C species.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2024

Directing CO 2 electroreduction pathways for selective C 2 product formation using single-site doped copper catalysts

Manipulating the selectivity-determining step in post-C–C coupling is crucial for enhancing C 2 product specificity during electrocatalytic CO 2 reduction, complementing efforts to boost rate-determining step kinetics. Here we highlight the role of single-site noble metal dopants on Cu surfaces in influencing C–O bond dissociation in an oxygen-bound selectivity-determining intermediate, steering post-C–C coupling toward ethylene versus ethanol. Integrating theoretical and experimental analyses, we demonstrate that the oxygen binding strength of the Cu surface controls the favorability of C–O bond scission, thus tuning the selectivity ratio of ethylene-to-ethanol. The Rh-doped Cu catalyst with optimal oxygen binding energy achieves a Faradaic efficiency toward ethylene of 61.2% and an ethylene-to-ethanol Faradaic efficiency ratio of 4.51 at –0.66 V versus RHE (reversible hydrogen electrode). Integrating control of both rate-determining and selectivity-determining steps further raises ethylene Faradaic efficiency to 68.8% at 1.47 A cm -2 in a tandem electrode. Our insights guide the rational design of Cu-based catalysts for selective CO 2 electroreduction to a single C 2 product.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

LaCeO x coupled N-doped graphene/Ru single-atoms as a binary-site catalyst for efficient hydrogen evolution based on hydrogen spillover

Based on the hydrogen spillover effect, versatile binary-site catalysts are promising for the alkaline hydrogen evolution reaction (HER). In which one site can adsorb and dissociate water, while the neighboring site is favorable for liberating hydrogen. Inspired by these possibilities, oxygen vacancy (O v )-rich LaCeO x coupled N-doped graphene/Ru single-atoms (LaCeO x @NGr/Ru 1 ) was synthesized as an efficient dual-site HER catalyst. It delivered an impressive low overpotential of 22 mV at a current density of 10mAcm –2 and a slight Tafel slope of 40 mV dec –1 in an alkaline medium, outstanding the advanced Ru-based catalysts. Moreover, this promising binary-component catalyst exhibited higher mass activity and longer lasting durability than commercial Pt/C catalyst (20 wt%). Finally, experimental and theoretical investigations provided insights into the HER mechanisms of LaCeO x @NGr/Ru 1 based on three indispensable steps: water adsorption and dissociation on O v -rich LaCeO x , diffusion of generated H* species towards Ce 3+ -N-Ru 1 bridges, and hydrogen evolution on Ru 1 sites.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Tuning the hydrogenation of CO 2 to CH 4 over mechano-chemically prepared palladium supported on ceria

CO 2 methanation reactivity, reaction mechanism, and surface structure were investigated on a mechanochemically prepared Pd/CeO 2 catalyst (PdAcCeO 2 -M), where an oxidative pretreatment (-o) increased methane yield by a factor of two compared to a reductive pretreatment (-h). Methanation rates were maintained for over 48 h and further increased upon oxidative regeneration treatments. The surface species of both PdAcCeO 2 -M-o and PdAcCeO 2 -M-h were explored via in situ CO 2 and CO hydrogenation DRIFTS, where CO hydrogenation effectively models the dissociative CO 2 mechanism (CO 2 → CO → CH 4 ). PdAcCeO 2 -M-o yielded distinct Pd-CO adsorption and the absence of monodentate carbonate at ~ 1400 cm -1 , while AP-XPS showed that PdAcCeO 2 -M-o yielded a unique Pd δ+ contribution at 335.9 eV. By gaining insights from various in situ spectroscopic techniques, and by breaking the CO 2 hydrogenation mechanism into piecewise steps, a deeper understanding of the direct CO 2 reduction towards methane and CO over mechanochemically prepared Pd/CeO 2 catalysts was obtained.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2023

Atomic Structural Origin of the High Methanol Selectivity over In 2 O 3 –Metal Interfaces: Metal–Support Interactions and the Formation of a InO x Overlayer in Ru/In 2 O 3 Catalysts during CO 2 Hydrogenation

CO 2 hydrogenation to methanol is of great environmental and economic interest due to its potential to reduce carbon emissions and produce valuable chemicals in one single reaction. Compared with the unmodified traditional Cu/ZnO/Al 2 O 3 catalyst, an indium oxide (In 2 O 3 )-based catalyst can double the methanol selectivity from 30–50 to 60–100%. It is worth noting that over catalysts involving various active metals dispersed on indium oxide (M/In 2 O 3 , M = Pd, Ni, Au, etc.), although the methanol yield is boosted, the selectivity remains similar to that of plain In 2 O 3 despite the distinct chemical properties of the added metals. Here, to investigate the phenomena behind this behavior, we used RuO 2 /In 2 O 3 as a test catalyst. The results of ambient pressure photoelectron spectroscopy, in situ X-ray absorption fine structure, and time-resolved X-ray diffraction indicate that the structure of the RuO 2 /In 2 O 3 catalyst is highly dynamic in the presence of a reactive environment. Specifically, under CO 2 hydrogenation conditions, Ru clusters facilitate the reduction of In 2 O 3 to generate In 2 O 3–x aggregates, which encapsulate the Ru systems in a migration driven by thermodynamics. In this way, the Ru O sites for CH 4 production are blocked while creating RuO x –In 2 O 3–x interfacial sites with tunable metal–oxide interactions for selective methanol production. In an inverse oxide/metal configuration, indium oxide has properties not seen in its bulk phase that are useful for the binding and conversion of CO 2 . This work reveals the dynamic nature of In 2 O 3 -based catalysts, providing insights for a rational design of materials for the selective synthesis of methanol.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Conversion of CO 2 to Methanol and Ethanol on Pt/CeO x /TiO 2 (110): Enabling Role of Water in C–C Bond Formation

The surface chemistry of alcohol synthesis from CO 2 hydrogenation has been investigated using kinetic testing, ambient pressure x-ray photoelectron spectroscopy (AP-XPS) and DFT calculations over a multicomponent system where Pt and ceria nanoparticles coexisted on a titania template, Pt/CeO x /TiO 2 (110). Due to its high ability to bind and activate CO 2 , not seen for typical Cu-ZnO catalysts, the Pt-CeO x -TiO 2 interface is excellent for the hydrogenation of CO 2 to methanol with some ethanol also being produced (21% selectivity). The results of AP-XPS and DFT calculations indicate that the active state involves a mixture of Ti 4+ /Ti 3+ , Ce 3+ and Pt 0 /Pt + . A fast pathway for the formation of CH 3 O species is only plausible when Ce 3+ and Pt are present. The addition of water to the reaction feed facilitates the first hydrogenation of CO 2 and substantially enhances the surface coverage of C-containing species (CH 3 O, HCOO, CO 3 , CH x ), facilitating the formation of C-C bonds and the production of ethanol (38% selectivity).

36 MATERIALS SCIENCE↗
DOE OSTI2022

Enhanced Oxide Reduction by Hydrogen at Cuprous Oxide–Copper Interfaces near Ascending Step Edges

We report that understanding the dynamic processes involved in the interaction of hydrogen with oxides is of fundamental importance in catalysis. This paper probes the reduction of Cu 2 O-‘29’ surfaces by hydrogen at room temperature combining in situ ambient pressure scanning tunneling microscopy (STM), X-ray photoelectron spectroscopy (XPS), and density functional theory (DFT) calculations. Reduction of the atomic layer thin Cu 2 O film is observed to be preferentially initiated2 at step edges and terrace defects, where perfect Cu 2 O(111) terraces are found to be stable towards hydrogenation under the same conditions. After a long induction period, regions of partially reduced Cu 2 O-‘29’ and metallic Cu co-exist before the surface is fully reduced to Cu(111). The reduction rate strongly depends on the nature of nearby Cu step edges. We propose a mechanism for the reduction of Cu 2 O-‘29’ by hydrogen where free copper atoms from ascending metallic step edges facilitate the formation of active ensembles for H 2 dissociation and transfer H to the edges of Cu2O regions

08 HYDROGEN↗
DOE OSTI2022

Tuning the Placement of Pt “Single Atoms” on a Mixed CeO 2 –TiO 2 Support

Defect sites on the oxide supports can be used to anchor and activate "single-atoms" catalysts (SACs). By engineering the anchoring sites for supporting SACs, one can alter their electronic and atomic structures which, in turn, define their activity, selectivity, and stability for catalytic reactions. To create and tune unique sites for Pt SACs on CeO 2 support, in this work, we synthesized a system consisting of CeO 2 decorated on TiO 2 nano-oxides for supporting the Pt SACs and investigated the effect of Pt weight loading. Here, a combination of multiple structural characterization methods including diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS), X-ray photoelectron spectroscopy (XPS) and X-ray absorption spectroscopy (XAS) were employed to characterize the distribution of charge states of single atoms and evaluate the heterogeneity of their binding sites. We have found that the placement of Pt atoms can be tuned on a mixed oxide surface by changing the weight loading of Pt.

77 NANOSCIENCE AND NANOTECHNOLOGY↗
DOE OSTI2022

Highly Selective Methane to Methanol Conversion on Inverse SnO 2 /Cu 2 O/Cu(111) Catalysts: Unique Properties of SnO 2 Nanostructures and the Inhibition of the Direct Oxidative Combustion of Methane

Direct methane to methanol (CH 4 → CH 3 OH) conversion in heterogeneous catalysis has been a long-standing challenge due to the difficulties in equalizing the activation of methane and protection of the methanol product at the same reaction conditions. Here, we report an inverse catalyst, consisting of small structures of SnO 2 (0.5-1 nm in size) dispersed on Cu 2 O/Cu(111), for highly selective CH 3 OH production from CH 4 . This system was investigated by combining theoretical [density functional theory calculations (DFT), kinetic Monte Carlo simulations (KMC)] and experimental methods [scanning tunneling microscopy (STM), ambient-pressure X-ray photoelectron spectroscopy (AP-XPS)]. The DFT and AP-XPS studies showed that on SnO 2 /Cu 2 O/Cu(111) the conversion of CH 4 by oxygen (O 2 ) preferred complete combustion to carbon dioxide (CO 2 ). The addition of water (H 2 O) enhanced the production of CH 3 OH to nearly 100% selectivity in KMC simulations. This trend was consistent with results of AP-XPS. The presence of water in the reaction environment rendered an extremely high amount of methoxy species (*CH 3 O), a precursor for CH 3 OH production. Further, the high CH 3 OH selectivity of SnO 2 /Cu 2 O/Cu(111) reflected the unique atomic and electronic structure of the supported SnO 2 nanoparticles. As a result, the O 2 adsorption and dissociation, and thus the full combustion of CH 4 to CO 2 , was completely suppressed; while the H 2 O dissociative adsorption was still feasible, providing active hydroxyl species for a truly selective CH 4 to CH 3 OH conversion.

03 NATURAL GAS↗