Effects of sodium hydroxide contamination level on physical and chemical properties of phenolic resin and carbon/phenolic composites described in report. NaOH degrades both carbon and phenolic components of carbon/phenolic laminates.
The effect on the flexural properties of a glass/epoxy composite of immersion in deionized water or seawater at 0, 25, and 80 C for 451 hr was examined. The percent weight gain at 0 and 25 C was low (0.06 to 0.17 percent) and there was no significant change in the flexural properties for these environmental conditions. At 80 C there was a decrease in the flexural strength of 17 and 20 percent in seawater and deionized water, respectively. This is a comparison to control samples exposed to 80 C heat alone. These decreases were found to be nearly reversible once the samples were dried. Optical microscopy did not reveal cracking of the matrix. The flexural modulus was essentially unaffected by exposure to deionized water and seawater at 80 C.
Preliminary studies have been conducted on two types of dielectric cure monitoring systems employing both epoxy resins and phenolic composites. An Audrey System was used for 23 cure monitoring runs with very limited success. Nine complete cure monitoring runs have been investigated using a Micromet System. Two additional measurements were performed to investigate the Micromet's sensitivity to water absorption in a post-cure carbon-phenolic material. While further work is needed to determine data significance, the Micromet system appears to show promise as a feedback control device during processing.
Five samples tested in one cooldown. Holder mounted in testing machine. Submerged in cryogenic liquid held in cryostat. Movable crosshead of testing machine moves gradually downward. Samples placed under tension, one after another, starting with top one; each sample fails in turn before next is stressed.