Enhanced High Temperature Piezoelectrics Based on BiScO3-PbTiO3 Ceramics
High-temperature piezoelectrics are a key technology for aeronautics and aerospace applications such as fuel modulation to increase the engine efficiency and decrease emissions. The principal challenge for the insertion of piezoelectric materials is the limitation on upper use temperature which is due to low Curie-Temperature (TC) and increasing electrical conductivity. BiScO3-PbTiO3 (BS-PT) system is a promising candidate for improving the operating temperature for piezoelectric actuators due to its high TC (greater than 400 C). Bi2O3 was shown to be a good sintering aid for liquid phase sintering resulting in reduced grain size and increased resistivity. Zr doped and liquid phase sintered BS-PT ceramics exhibited saturated and square hysteresis loops with enhanced remenant polarization (37 microC per square centimeter) and coercive field (14 kV/cm). BS-PT doped with Mn showed enhanced field induced strain (0.27% at 50kV/cm). All the numbers indicated in parenthesis were collected at 100 C.
Doping of BiScO3-PbTiO3 Ceramics for Enhanced Properties
High-temperature piezoelectrics are a key technology for aeronautics and aerospace applications such as fuel modulation to increase the engine efficiency and decrease emissions. The principal challenge for the insertion of piezoelectric materials is the limitation on upper use temperature which is due to low Curie-Temperature (T(sub c) and increasing electrical conductivity. BiScO3 -PbTiO3 (BS-PT) system is a promising candidate for improving the operating temperature for piezoelectric actuators due to its high TC (>400 C). Effects of Zr and Mn doping of the BS-PT ceramics have been studied and all electrical and electromechanical properties for Sc-deficient and Ti-deficient BS- PT ceramics are reported as a function of electrical field and temperature. Donor doping with Zr and Mn (in Sc deficient compositions) increased the DC-resistivity and decreased tan at all temperatures. Resulting ceramics exhibited saturated hysteresis loops with low losses and showed no dependence on the applied field (above twice the coercive field) and measurement frequency.
Thermoelectric Properties of Self Assembled TiO2/SnO2 Nanocomposites
Recent advances in improving efficiency of thermoelectric materials are linked to nanotechnology. Thermodynamically driven spinodal decomposition was utilized to synthesize bulk nanocomposites. TiO2/SnO2 system exhibits a large spinodal region, ranging from 15 to 85 mole % TiO2. The phase separated microstructures are stable up to 1400 C. Semiconducting TiO2/SnO2 powders were synthesized by solid state reaction between TiO2 and SnO2. High density samples were fabricated by pressureless sintering. Self assemble nanocomposites were achieved by annealing at 1000 to 1350 C. X-ray diffraction reveal phase separation of (Ti(x)Sn(1-x))O2 type phases. The TiO2/SnO2 nanocomposites exhibit n-type behavior; a power factor of 70 W/mK2 at 1000 C has been achieved with penta-valent doping. Seebeck, thermal conductivity, electrical resistivity and microstructure will be discussed in relation to composition and doping.
New Techniques in Characterization of Ferroelectric Materials
Two new techniques have been developed to characterize Pb(Mg1/3Nb2/3)O3-PbTiO3 (PMN-PT) based ferroelectric single crystals: (i) electro-thermal imaging, and (ii) single crystal x-ray diffraction in the transmission mode. (i) Electro-thermal imaging is a remote sensing technique that can detect the polarization direction and poling state of a whole crystal slice. This imaging technique utilizes an IR camera to determine the field induced temperature change and does not require any special or destructive sample preparation. In the resulting images it is possible to distinguish regions of 180 deg domains. This powerful technique can be used remotely during poling to determine the poling state of the crystal to avoid over-poling that can result in inferior properties and/or cracking of the crystals. Electro-thermal imaging produced the first direct observations of polarization rotation. Under bipolar field, the domains near the corners were the first to switch direction. As the field increased above the coercive field, domains at the center part of the crystals switched direction. (ii) X-ray diffraction in the transmission mode has long been used in structure determination of organic crystals and proteins; however, it is not used much to characterize inorganic systems. 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 single crystals were examined by this XRD technique for the first time, and a never-before-seen super-lattice was revealed with a doubling of the unit cell in all three directions, giving a cell volume eight times that of a traditional perovskite unit cell. The significance of the super-lattice peaks increased with poling, indicating a structural contribution to ordering. Lack of such observations by electron diffraction in the transmission electron microscope examinations suggests the presence of a bulk effect.
Effect of Excess Lead and Bismuth Content on the Electrical Properties of High-Temperature Bismuth Scandium Lead Titanate Ceramics
Aeronautic and aerospace applications require piezoelectric materials that can operate at high temperatures. The air-breathing aeronautic engines can use piezoelectric actuators for active combustion control for fuel modulation to mitigate thermo-acoustic instabilities and/or gas flow control to improve efficiency. The principal challenge for the insertion of piezoelectric materials is their limitation for upper use temperature and this limitation is due low Curie temperature and increasing conductivity. We investigated processing, microstructure and property relationship of (1-x)BiScO3-(x)PbTiO3 (BS-PT) composition as a promising high temperature piezoelectric. The effect of excess Pb and Bi and their partitioning in grain boundaries were studied using impedance spectroscopy, ferroelectric, and piezoelectric measurement techniques. Excess Pb addition increased the grain boundary conduction and the grain boundary area (average grain size was 24.8 m, and 1.3 m for compositions with 0at.% and 5at.% excess Pb, respectively) resulting in ceramics with higher AC conductivity (tan d= 0.9 and 1.7 for 0at.% and 5at.% excess Pb at 350 C and at 10kHz) that were not resistive enough to pole. Excess Bi addition increased the resistivity (rho= 4.1x10(exp 10) Omega cm and 19.6 x10(exp 10) Omega.cm for compositions with 0at.% and 5at.% excess Bi, respectively), improved poling, and increased the piezoelectric coefficient from 137 to 197 pC/N for 5at.% excess Bi addition. In addition, loss tangent decreased more than one order of magnitude at elevated temperatures (greater than 300 C). For all compositions the activation energy of the conducting species was similar (approximately equal to 0.35-0.40 eV) and indicated electronic conduction.
Challenges and New Trends for Piezoelectric Actuators
BiScO3-PbTiO3 ceramics with TC greater than 400 C has been successfully processed. Despite the increase in TC, excess Pb addition increases both the bulk conductivity and the grain boundary contribution to conductivity at elevated temperatures. Conductivity at elevated temperatures, that limits the operating temperature for actuators, has been greatly reduced by excess Bi additions. Excess Bi doping improves poling conditions resulting in enhanced piezoelectric coefficient (d(sub 33) = 408 pC/N).
Thermoelectric Properties of Self Assemble TiO2/SnO2 Nanocomposites
Recent advances in improving efficiency of thermoelectric materials are linked to nanotechnology. Thermodynamically driven spinodal decomposition was utilized to synthesize bulk nanocomposites. TiO2/SnO2 system exhibits a large spinodal region, ranging from 15 to 85 mole % TiO2. The phase separated microstructures are stable up to 1400 C. Semiconducting TiO2/SnO2 powders were synthesized by solid state reaction between TiO2 and SnO2. High density samples were fabricated by pressureless sintering. Self assemble nanocomposites were achieved by annealing at 1000 to 1350 C. X-ray diffraction reveal phase separation of (Ti(x)Sn(1-x))O2 type phases. The TiO2/SnO2 nanocomposites exhibit n-type behavior; a power factor of 70 (mu)W/m sq K at 1000 C has been achieved with penta-valent doping. Seebeck, thermal conductivity, electrical resistivity and microstructure will be discussed in relation to composition and doping.
High-Temperature Properties of Piezoelectric Langatate Single Crystals
Langasite type crystals belong to non-polar point group of 32 and do not show any phase transformations up to the melting temperature. Langatate (La3Ga(5.5)Ta(0.5)O14) demonstrates piezoelectric activity better than quartz and possesses attractive properties for high temperature sensors, resonators and filter applications. High-quality and colorless langatate crystals were grown by the Czochralski technique. The electromechanical and electrical properties of langatate crystals in different crystallographic directions were characterized at elevated temperature. The piezoelectric coefficient along x-axis was 7 pC/N as measured by a Berlincourt meter for a plate geometry with an aspect ratio of 10:1. The dielectric constant did not exhibit any significant temperature dependence (K33 approx. 21 at 30 C and K33 approx. 23 at 600 C). Loss tangent at 100 kHz remained <0.003 up to 300 C and <0.65 at 600 C. The dielectric properties along the y-axis were similar and its temperature dependence was analogous to the x-axis. Electromechanically, the inactive z-axis exhibited no resonance with K33 approx. 84 at room temperature, decreasing down to approx. 49 at 600 C. Resistivity of these crystals along x-axis decreased from approx. 6x10(exp 11) omega-cm at room temperature, to approx. 1.6x10(exp 6) omega-cm at 600 C.