NASA NTRS1985

Thermo-oxidative stability of graphite fiber/PMR-15 polyimide composites at 350 deg C

A series of graphite fiber/PMR-15 polyimide composites were subjected to isothermal aging at 350 C in flowing air (100 cc/min and 1000 cc/min) over a 520 hr time period. The graphite fibers were analyzed by ISS/SIMS techniques before composite fabrication. Fibers exposed at the surface of the composite due to the isothermal aging process were also analyzed by the ISS/SIMS method. Component and composite weight less studies were also conducted for similarly exposed materials. Optical micrograph investigations of composites to follow the progress of the thermo-oxidative process were also conducted. Flexural and interlaminar shear strengths of the imaged and aged composites were measured. The relationship of component and composite properties as they relate to the thermo-oxidative behavior of the materials was discussed.

Scola, D. A.↗

NASA NTRS1984

Imide modified epoxy matrix resins

The results of a program designed to develop tough imide modified epoxy resins cured by bisimide amine (BIA) hardeners are described. State-of-the-art epoxides MY720 and DER383 were used, and four bismide amines were evaluated. These were the BIA's derived from the 6F anhydride (4,4'-(hexafluoroisopropylidene) bis(phthalic anhydride) and the diamines 3,3'-diaminodiphynyl sulfone, 4,4'-oxygianiline, 4,4'-methylene dianiline, and 1,12-dodecane diamine. A key intermediate, designated 6F anhydride, is required for the synthesis of the bisimide amines. Reaction parameters to synthesize a precursor to the 6F anhydride (6FHC) in high yields were investigated. The catalyst trifluoromethane sulfonic acid was studied. Although small scale runs yielded the 6FHC in 50 percent yield, efforts to ranslate these results to a larger scale synthesis gave the 6FHC in only 9 percent yield. Results show that the concept of using bisimide amine as curing agents to improve the toughness properties of epoxies is valid.

Scola, D. A.↗

NASA NTRS1983

Synthesis and characterization of bisimide amines and bisimide amine-cured epoxy resins

An attempt is made to develop tough, moisture resistant, high char yield epoxy resins by means of novel bisimide amine (BIA) hardener curing agents and a state-of-the-art epoxy resin system. The BIAs are isolated as mixtures containing monomer, oligomer, and polymeric species, and then characterized by elemental analysis and high pressure liquid chromatography. The bisimide amine-cured epoxies (IMEs) were characterized with respect to moisture absorption, thermal properties, and physical and mechanical properties, as well as in the role of matrices in Celion 6000/IME composites. The relative toughness characteristics of each IME formulation was measured by the 10 deg off-axis tensile test, measuring the uniaxial tensile strength, shear strength, and shear-strain-to-failure of the composite systems.

Scola, D. A.↗

NASA NTRS1982

Synthesis and characterization of bisimide amines and bisimide amine-cured epoxy resins

A study has been conducted with the objective of developing tough, moisture resistant, high char yield epoxy resins using novel bisimide amine (BIA) hardeners as curing agents with MY-720, a commercial state-of-the-art epoxy resin system. BIA cured epoxies are shown to have lower moisture absorption than MY-720 and other state-of-the-art epoxy resins; the tensile strengths and strain-to-failures of several of the bisimide epoxy resins (IME's) are higher than those of the state-of-the-art epoxies. Most IME's have compression properties equivalent to those of state-of-the-art epoxies. Two resin systems, IME-10 and IME-12-3, have better overall properties than other resin systems investigated.

Scola, D. A.↗

NASA NTRS1982

Imide modified epoxy matrix resins

Results of a program designed to develop tough imide modified epoxy (IME) resins cured by bisimide amine (BIA) hardeners are presented. State of the art epoxy resin, MY720, was used. Three aromatic bisimide amines and one aromatic aliphatic BIA were evaluated. BIA's derived from 6F anhydride (3,3 prime 4,4 prime-(hexafluoro isopropyl idene) bis (phthalic anhydride) and diamines, 3,3 prime-diam nodiphenyl sulfone (3,3 prime-DDS), 4,4 prime-diamino diphenyl sulfone (4,4 prime-DDS), 1.12-dodecane diamine (1,12-DDA) were used. BIA's were abbreviated 6F-3,3 prime-DDS, 6F-4,4 prime-DDS, 6F-3,3 prime-DDS-4,4 prime DDS, and 6F-3,3 prime-DDS-1,12-DDA corresponding to 6F anhydride and diamines mentioned. Epoxy resin and BIA's (MY720/6F-3,3 prime-DDS, MY720/6F-3,3 prime-DDS-4,4 prime-DDS, MY720/6F-3,3 prime-DDS-1,12-DDA and a 50:50 mixture of a BIA and parent diamine, MY720/6F-3,3 prime-DDS/3,3 prime-DDS, MY720/6F-3,3 prime-DDS-4,4 prime-DDS/3,3 prime-DDS, MY720/6F-3,3 prime-DDS-1,12-DDA/3,3 prime-DDS were studied to determine effect of structure and composition. Effect of the addition of two commercial epoxies, glyamine 200 and glyamine 100 on the properties of several formulations was evaluated. Bisimide amine cured epoxies were designated IME's (imide modified epoxy). Physical, thermal and mechanical properties of these resins were determined. Moisture absorption in boiling water exhibited by several of the IME's was considerably lower than the state of the art epoxies (from 3.2% for the control and state of the art to 2.0 wt% moisture absorption). Char yields are increased from 20% for control and state of the art epoxies to 40% for IME resins. Relative toughness characteristics of IME resins were measured by 10 deg off axis tensile tests of Celion 6000/IME composites. Results show that IME's containing 6F-3,3 prime-DDS or 6F-3,3 prime-DDS-1,12-DDA improved the "toughness" characteristics of composites by about 35% (tensile strength), about 35% (intralaminar shear strength), and about 78% (shear strain to failure) relative to the control composite.

Scola, D. A.↗

NASA NTRS1982

The properties of novel bisimide amine cured epoxy/Celion 6000 graphite fiber composites

The study is concerned with the further development of bisimide amine cured epoxy resins first reported by Serafini et al. (1979). Attention is given to properties of the neat resins and composites made with these novel epoxy resins and Celion 6000 graphite fibers. The use of bisimide amine hardeners to cure epoxy resins causes a significant improvement in the char-forming characteristics of the cured resin. Compared to epoxy resins cured with a conventional amine, such as 4,4'-diaminodiphenylsulfone, the bisimide cured epoxies exhibit about a twofold improvement in the aerobic char yield at 800 C. The levels of moisture absorption exhibited by the bisimide amine cured epoxies were found to be considerably lower than those exhibited by state-of-the-art epoxies (0.5 wt.% versus 2.0%).

Scola, D. A.↗

NASA NTRS1982

Bisimide amine cured epoxy /IME/ resins and composites. II - Ten-degree off-axis tensile and shear properties of Celion 6000/IME composites

Bisimide amines (BIAs), which are presently used as curing agents in a state-of-the-art epoxy resin, are oligomeric and polymeric mixtures. A series of composites consisting of the novel BIA-cured epoxy resin reinforced with Celion 6000 graphite fibers were fabricated and evaluated, and the ten-degree, off-axis uniaxial tensile and shear properties of these composites were determined. The use of the intralaminar shear strain-to-failure was used in the calculation of resin shear strain-to-failure. Study results indicate that several of these novel composite systems exhibit shear strain properties that are superior to those of the control composite system of the present experiments, which employed a sulfone curing agent.

Scola, D. A.↗

NASA NTRS1981

Imide modified epoxy matrix resins

High char yield epoxy using novel bisimide amines (BIA's) as curing agents with a state of the art epoxy resin was developed. Stoichiometric quantities of the epoxy resin and the BIA's were studied to determine the cure cycle required for preparation of resin specimens. The bisimide cured epoxies were designated IME's (imide modified epoxy). The physical, thermal and mechanical properties of these novel resins were determined. The levels of moisture absorption exhibited by the bisimide amine cured expoxies (IME's) were considerably lower than the state of the art epoxies. The strain-to-failure of the control resin system was improved 25% by replacement of DDS with 6F-DDS. Each BIA containing resin exhibited twice the char yield of the control resin MY 720/DDS. Graphite fiber reinforced control (C) and IME resins were fabricated and characterized. Two of the composite systems showed superior properties compared to the other Celion 6000/IME composite systems and state of the art graphite epoxy systems. The two systems exhibited excellent wet shear and flexural strengths and moduli at 300 and 350 F.

Scola, D. A.↗

NASA NTRS1980

Coatings for graphite fibers

Graphite fibers released from composites during burning or an explosion caused shorting of electrical and electronic equipment. Silicon carbide, silica, silicon nitride and boron nitride were coated on graphite fibers to increase their electrical resistances. Resistances as high as three orders of magnitude higher than uncoated fiber were attained without any significant degradation of the substrate fiber. An organo-silicone approach to produce coated fibers with high electrical resistance was also used. Celion 6000 graphite fibers were coated with an organo-silicone compound, followed by hydrolysis and pyrolysis of the coating to a silica-like material. The shear and flexural strengths of composites made from high electrically resistant fibers were considerably lower than the shear and flexural strengths of composites made from the lower electrically resistant fibers. The lower shear strengths of the composites indicated that the coatings on these fibers were weaker than the coating on the fibers which were pyrolyzed at higher temperature.

Galasso, F. S.↗

NASA NTRS1980

Coatings for Graphite Fibers

Several approaches for applying high resistance coatings continuously to graphite yarn were investigated. Two of the most promising approaches involved (1) chemically vapor depositing (CVD) SiC coatings on the surface of the fiber followed by oxidation, and (2) drawing the graphite yarn through an organo-silicone solution followed by heat treatments. In both methods, coated fibers were obtained which exhibited increased electrical resistances over untreated fibers and which were not degraded. This work was conducted in a previous program. In this program, the continuous CVD SiC coating process used on HTS fiber was extended to the coating of HMS, Celion 6000, Celion 12000 and T-300 graphite fiber. Electrical resistances three order of magnitude greater than the uncoated fiber were measured with no significant degradation of the fiber strength. Graphite fibers coated with CVD Si3N4 and BN had resistances greater than 10(exp 6) ohm/cm. Lower pyrolysis temperatures were used in preparing the silica-like coatings also resulting in resistances as high as three orders of magnitude higher than the uncoated fiber. The epoxy matrix composites prepared using these coated fibers had low shear strengths indicating that the coatings were weak.

Galasso, F. S.↗

NASA NTRS1979

Study of high resistance inorganic coatings on graphite fibers

Coatings made of boron, silicon carbide, silica, and silica-like materials were studied to determine their ability to increase resistance of graphite fibers. The most promising results were attained by chemical vapor depositing silicon carbide on graphite fiber followed by oxidation, and drawing graphite fiber through ethyl silicate followed by appropriate heat treatments. In the silicon carbide coating studies, no degradation of the graphite fibers was observed and resistance values as high as three orders of magnitude higher than that of the uncoated fiber was attained. The strength of a composite fabricated from the coated fiber had a strength which compared favorably with those of composites prepared from uncoated fiber. For the silica-like coated fiber prepared by drawing the graphite fiber through an ethyl silicate solution followed by heating, coated fiber resistances about an order of magnitude greater than that of the uncoated fiber were attained. Composites prepared using these fibers had flexural strengths comparable with those prepared using uncoated fibers, but the shear strengths were lower.

Galasso, F. S.↗

NASA NTRS1978

Synthesis of improved moisture resistant polymers

The synthesis and characterization of novel moisture resistant aliphatic polyimides are described. Several novel aliphatic imides of diversified functionalities were synthesized, purified, and characterized, they include: (1) N-(12-aminododecyl)-5-norbornene-2,3-dicarboximide; (2) N,N'-2,2,2-trifluoro-1-(trifluoromethyl)ethylidene bis (1,3-dioxo-5,2-iosoindolinediyl)dodecamethylene di-5-norbornene-2,3-dicarboximide; (3) N,N'-dodecamethylenedi-5-nobornene-2,3-dicarbonoximide; (4) N,N'-dodecamethylenebis 5,6-epoxy-2,3-norbornanedicarboximide ; and (5) N,N'-Bis 12-(5-norbornene-2, 3-dicarboximidido)dodecyl - 1,2,3,4- butanetetracarboxylic 1,2:3,4-diimide. The structures of these compounds were established by elemental analysis, IR, NMR, and mass spectra.

Scola, D. A.↗