Compilation of information on design procedures, electrical properties, and fabrication. Guide provides information on design procedures; magnetic and insulating material electrical properties; impregnating, encapsulating and processing techniques.
The 25-kVA space transformer was developed under contract by Thermal Technology Laboratory, Buffalo, N. Y. The NASA Lewis transformer technology program attempted to develop the baseline technology. For the 25-kVA transformer the input voltage was chosen as 200 V, the output voltage as 1500 V, the input voltage waveform as square wave, the duty cycle as continuous, the frequency range (within certain constraints) as 10 to 40 kHz, the operating temperatures as 85 deg. and 130 C, the baseplate temperature as 50 C, the equivalent leakage inductance as less than 10 micro-h, the operating environment as space, and the life expectancy as 10 years. Such a transformer can also be used for aircraft, ship and terrestrial applications.
The magnetization and core loss of Supermendur were measured up to 900 C under conditions of slow temperature cycling in vacuum. As a consequence of this heating, the coercivity at 25 C increased from 21 A/m to about 110 A/m. This increase is less than previously reported. A prominent anomalous Barkhausen effect, pinched-in hysteresis loops, and a magnetic viscosity field in excess of 20 A/m were observed in the range of 600 to 700 C. At 850 C, Supermendur had a coercivity of 23 A/m, a saturation induction exceeding 1.5 T, a core loss of 26 W/kg at 400 Hz, and a maximum induction of 1.5 T. Supermendur may be useful for high temperature soft magnetic material applications where some history dependence of properties and instability of minor loops at lower temperatures is acceptable.