Wrought Aluminum-Cerium Alloys by Shear Assisted Processing and Extrusion

Al-Ce alloys have attracted recent interest because of their high thermal stability due to the very low solubility of Ce in the Al matrix. The Al 11 Ce 3 eutectic phase gives excellent strain hardening behavior and moderate high-temperature strength in the as-cast state. However, its strengthening effect is limited by its coarse as-cast structure. Therefore, alternative manufacturing methods such as additive manufacturing or equal channel angular pressing have been applied to refine the Al 11 Ce 3 phase to good effect. However, these techniques are both expensive and time-consuming. Therefore, this study aims to use Shear Assisted Processing and Extrusion (ShAPE), an emerging solid phase processing technique that is more easily scalable than the previously mentioned methods. ShAPE can produce useful cross-sections of an Al-8Ce-4Mg alloy while refining the Al 11 Ce 3 phase to produce a higher strength material. It was found that a low temperature ShAPE process can improve the room temperature yield strength by ~60% compared to a binary Al-4Mg alloy. Additionally, the high-temperature yield strength of the Al-Ce alloys increased by 20%, with a simultaneous 15% improvement in ductility compared to the binary Al-Mg alloy. These results highlight the potential for ShAPE as a processing technique for Al-Ce alloys.

36 MATERIALS SCIENCE↗

Upcycling of Mixed Aluminum Alloy Shredder Scrap using Shear Processing

Conservation of critical materials is an increasing area of focus in the Unites States. In 2023, aluminum was added to the US Department of Energy Final Critical Materials List which has spurred public and private research into sustainable management of these resources. Additionally, efficiency in manufacturing and conservation of natural resources are growing concerns with targets to lower global carbon emissions, as primary aluminum alloy production is energy intensive, requiring 14 MWh of electricity plus 0.4 tonnes of CO2 per tonne of Al. Due to these factors, is essential that more sustainable manufacturing methods for aluminum alloys are developed going forward. To this end, much research is ongoing on the topic of more efficient utilization and recovery. However, most of this research still requires primary aluminum in the production process. Here, it will be attempted to bypass the use of primary aluminum and produce useful material recycled from 100% post-consumer scrap. Even considering recent developments in recycling of Al scrap, there is still a large amount of post-consumer scrap that is underutilized due to high impurity content, and that amount will increase significantly as more and more aluminum alloys are utilized in vehicles. This “scrap wave” is expected to cover 80% of the demand for automotive aluminum alloys by 2050 . A challenge to be addressed before the coming scrap wave can be fully utilized is that the tolerance of manufacturing techniques to impurities or off-spec alloy compositions must be increased. Particularly, in 5000-and 6000-series alloys (the most common wrought alloys in durable products), excess iron, copper, and silicon create brittle intermetallics during casting that remain in the extruded microstructure which limit the formability, ductility, and corrosion resistance of the alloy. Concerningly, many of the highest-volume post-consumer aluminum scrap streams such as automotive shredder scrap contain a mix of alloys including both wrought and cast alloys. Their compositions can vary widely depending on geography and the time of year. Because they are mixed, they often contain high content of multiple alloying elements such as Si and Cu in higher concentrations than are found in typical wrought alloys. They may also be contaminated with non-Al alloys from fasteners that get mixed in and often have high content of unwanted elements such as Fe. As a method for utilizing these underused scrap streams that are high in tramp elements, an emerging extrusion technology is being developed at the Pacific Northwest National Laboratory (PNNL) that aims to upcycle 100% post-consumer aluminum scrap directly into extruded components without the addition of primary aluminum . This new technology, called Shear Assisted Processing and Extrusion (ShAPE), is enabling a shift away from today’s recycling paradigm by reaching deeper into lower-value scrap streams, using shredder scrap as the extrusion billet material. Sometimes referred to as Twitch or Tweak, these scrap streams result from shredding and sorting of automobiles, building materials, appliances, and consumer goods. ShAPE combines the linear axis of conventional extrusion with a rotating extrusion die. This rotating die applies large strain to the material during extrusion, which breaks up large impurity-containing intermetallic particles, reducing their deleterious effects. This has been demonstrated for 6063 machining scrap spiked with excess Fe, and Twitch scrap high in Fe, Si and Cu where strength and ductility were retained for both feedstock compositions. Additionally, the extreme plastic deformation during ShAPE enables extrusion of billets with high Si that are too brittle for processing by conventional extrusion. By using 100% post-consumer shedder scrap as feedstock, ShAPE has the potential to slash embodied energy and carbon in extruded components by >80% compared to conventional extrusion of primary aluminum alloys.

Milligan, Brian K.↗

An innovative and alternative approach toward gear fabrication

In this paper, we present the first demonstration of single-step gear manufacturing via an innovative in-situ friction stir forging approach. This novel process is a natural extension to the friction stir processing technique and relies on shear and normal stresses to form the complex shapes. Friction stir welding pin tool with shoulder is plunged at high revolutions per minute (rpm) into the sample to heat it to the desired temperature and enable plastic flow. Then, the tool is forged at high plunge rate to form the desired structurally-sound and defect free complex shapes. To better visualize the process the experiments are complemented by a 3D thermomechanically coupled, smoothed particle hydrodynamics (SPH) model to understand the material flow pattern both radially and through thickness in the gear teeth, plastic strain distribution, and temperature profile. We have demonstrated application of I-FSF to inherently poor formable AZ31 Mg, AA 7075-T6, and AA5083–10 vol% TiB 2 composite and fabricated 14-tooth spur gears from these materials with minimal farther machining. In conclusion, microstructure of the forged gears exhibited a directional material flow pattern due to the normal forging action and refinement of grains to 6–13 μm through dynamically recrystallization across the radial, through-thickness direction, which is in good agreement with the corresponding SPH simulation results.

42 ENGINEERING↗

PNNL's Characterization Summary for MP-2 Experiment

Characterization of as-fabricated fuel was performed at Pacific Northwest National Laboratory (PNNL) in accordance with the characterization plan for the fabrication of U 10Mo plate fuel for the U.S. High Performance Research Reactor conversion program’s Fuel Fabrication Pillar (INL 2021). Similar characterization work is also being performed at Idaho National Laboratory to provide a detailed understanding of the as-fabricated foils that would be irradiated in the Mini-Plate 2 (MP 2) experiment. Under the MP 2 characterization plan, foils are studied that have different fabrication parameters (such as rolling condition, rolling thickness reduction, co-rolling with Zr layers). Similar samples from master foils were sent to both the organizations, so that the testing and analysis can be done independently using similar equipment and standardized measurement and analysis procedures. A final, consolidated report will be prepared based on this work and will summarize all the information obtained from the two laboratories. The MP 2 experiment will provide an opportunity to understand the effects of processing conditions on the final fuel microstructure, to compare results obtained independently, and achieve a two-way validation. In Fiscal Year 2022, PNNL received five MP 2 cast (PD STD2) samples to examine the foils’ chemistry and microstructure. For each cast sample, PNNL received samples from three different locations. PNNL also received and characterized 24 U 10Mo foil samples, by sectioning four pieces/specimens from each foil, in accordance with the MP 2 Characterization Plan (INL 2021). These 24 samples consist of four types of foils from BWX Technologies: 0.047 in. thick hot-rolled and annealed samples with Zr layers; 0.025 in. thick cold-rolled and annealed samples with Zr layers; 0.0105 in. thick cold-rolled and annealed samples with Zr layers. Along with these, PNNL also received four plates with Zr layers that were 0.025 in. and 0.0105 in. thick. This report describes the results of PNNL’s MP 2 foil characterization. Microstructure, Mo homogeneity, carbide fraction and morphology, U 10Mo foil thickness, and Zr thickness were evaluated in both the longitudinal and transverse directions for all the foils of the three different thicknesses.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Automated Calculation of U-10Mo Fuel and Zr Cladding Thickness

Hand calculation and verification of cladding and fuel thickness in a hot-isostatically pressed uranium-molybdenum (U-10Mo) alloy can incur human errors and longer image processing time when analyzing a large set of cross-sectional images. To help alleviate both time cost and errors made in hand measurements, an automated image processing procedure was developed using Octave, an open-source MATLAB alternative, to repeatedly determine the thickness of Zr and U-10Mo layers. U-10Mo specimens were imaged using standard secondary electron and backscattered-electron imaging at 250× magnification to capture the various layers present in U-10Mo. Further image processing used pixel-by-pixel calculation of the Zr and U-10Mo layers to gather quantitative statistics on the thickness variations associated with each of the layers.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

Microstructural Characterization of As-Cast MP-1 Experiment U-10Mo Alloy

The Mini-Plate-1 (MP-1) test is the first in a series of fuel testing campaigns with the purpose of achieving regulatory qualification for the U-10Mo monolithic plate-type fuel system. The objective of MP-1 is to assess fuel performance behavior of fuel plates fabricated by a commercial fuel fabricator (BWX Technologies, Inc.) and make sure that the fuel maintains mechanical integrity and geometric stability and behaves in a stable and predictable manner. As a part of MP1 fabrication campaign several castings were prepared. The castings were vacuum induction melted using HEU pieces mixed with a master alloy made up of DU and molybdenum pieces. The Master Alloy was poured by a commercial vendor. There was little mixing during melting. A three-plate mold was utilized to form three U-10Mo plates per melt pour. The work described here shows that the resulting microstructure varies greatly from one cast plate to another, and from the top to the bottom of each cast plate. The extent of variation in microstructural features such as grain size, second phase particle (SPP) distribution and morphology, microsegregation of constituents within the dendritic microstructure, porosity, and casting abnormalities are presented and discussed.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

The Effect of Homogenization Heat Treatment on the Texture Evolution in U-10Mo Alloy

Uranium alloyed with 10 wt% Mo (U-10Mo) undergoes discontinuous precipitation (DP) when subjected to sub-eutectoid heat-treatment. It is hypothesized that the crystallographic texture of the U-10Mo can be modified to minimize the degree of DP, however the evolution of texture throughout the manufacturing process is not well understood. Crystallographic textures of two U-10Mo samples homogenized at 900°C and 1000°C were studied after uniaxial rolling and annealing. A total of 6 samples were analyzed upon rolling using a combination of hot and cold rolling conditions to strains of 83%, 90% and 97% and subsequently annealed at 700°C for one hour. Microstructures and textures were analyzed via electron backscatter diffraction (EBSD) for each homogenization, strain and post-annealed states. Results show that the U-10Mo exhibits typical rolling textures seen in body-centered cubic materials with increasing intensities of both a- and ?-fibers with increasing strain. After recrystallization, the texture appeared to be effectively randomized in all samples. Homogenization temperature showed no effect on the rolling and recrystallization behavior. Potential factors leading to the randomization of texture are discussed along with the implications of textures on the minimization of DP.

nuclear fuel, texture, rolling↗