Roadmap on exsolution for energy applications

Over the last decade, exsolution has emerged as a powerful new method for decorating oxide supports with uniformly dispersed nanoparticles for energy and catalytic applications. Due to their exceptional anchorage, resilience to various degradation mechanisms, as well as numerous ways in which they can be produced, transformed and applied, exsolved nanoparticles have set new standards for nanoparticles in terms of activity, durability and functionality. In conjunction with multifunctional supports such as perovskite oxides, exsolution becomes a powerful platform for the design of advanced energy materials. In the following sections, we review the current status of the exsolution approach, seeking to facilitate transfer of ideas between different fields of application. We also explore future directions of research, particularly noting the multi-scale development required to take the concept forward, from fundamentals through operando studies to pilot scale demonstrations.

25 ENERGY STORAGE↗

DOE OSTI2023

Atomic layer deposition for surface area determination of solid oxide electrodes

Surface area measurements are important for characterizing porous solids, but commonly used methods such as Brunauer–Emmett–Teller (BET) gas adsorption and computed nanotomography are lacking for certain applications such as the development of solid oxide fuel cell electrodes, which often have absolute surface areas <1 m 2 and contain nanoscale features. Presented is a novel method for the surface area determination of samples with total measurable areas of 1–1000 cm 2 with a standard deviation ± 1 cm 2 , utilizing the atomic layer deposition (ALD) of Al 2 O 3 over microstructurally complex internal porosity. The volume of alumina is then quantified using plasma spectroscopy and converted to an area using the known ALD layer thickness. Under the modest ALD reactor soak times used (8.5 s), the precursor penetration depth is found to be ~50 μm, exceeding the requirement for uniformly coating SOFC functional layers. A model system, (La 0.8 Sr 0.2 ) 0.98 MnO 3–δ /Ce 0.9 Gd 0.1 O 1.95 (LSM/GDC) scaffolds of ~2.7 m 2 g –1 , was measured using the technique and compared against the BET method, and comparable results were obtained but with 1000 times less material needed. The technique is demonstrated for measurements in two example areas of active SOFC research: exsolved (Ni, Fe) nanoparticles on an Sr(Ti, Fe, Ni)O 3–δ electrode and PrO x catalyst nanoparticles infiltrated onto LSM/GDC scaffolds. Finally, the technique may be broadly useful wherever the accurate surface area determination of small absolute quantities of porous ceramic structures on the order of 0.1–50 m 2 g –1 is sought.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗