DOE OSTI2024

Era of entropy: Synthesis, structure, properties, and applications of high-entropy materials

The field of high-entropy materials (HEMs) has emerged as a dynamic area of scientific exploration, driven by the exceptional properties arising from their compositional complexity. Encompassing both high-entropy alloys (HEAs) and high-entropy ceramics (HECs), these materials have garnered significant attention across diverse research domains. From investigations into phase evolution and mechanical characteristics to studies of ionic, electronic, and magnetic behaviors, HEMs demonstrate remarkable potential for a wide array of applications. These range from catalysis and tribology to energy storage and superconductivity. Fundamental research has shed light on crucial phenomena such as configurational entropy, lattice distortion, and sluggish diffusion. These discoveries are paving the way for materials design strategies that enable new functional tunability and resistance to application-specific harsh environments. This burgeoning field promises to revolutionize material design and performance across numerous technological sectors. Here, this special collection between Applied Physics Letters and the Journal of Applied Physics provides a timely overview of the latest research in this area. It highlights the growing interest in understanding the impact of high compositional complexity on conventional structure–process–property–performance relationships in HEMs.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Magnetic functionalization and catalytic behavior of magnetic nanoparticles during laser photochemical graphitization of polyimide

We report laser-assisted photochemical graphitization of polyimides (PIs) into functional magnetic nanocomposites using laser irradiation of PI in the presence of magnetite nanoparticles (MNPs). PI Kapton sheets covered with MNP were photochemically treated under ambient conditions using a picosecond pulsed laser (1064 nm) to obtain an electrically conductive material. Scanning electron microscopy of the treated material revealed a layered magnetic nanoparticle/graphite (MNP/graphite) nanocomposite structure. Four probe conductivity measurements indicated that the nanocomposite has an electrical conductivity of 1550 ± 60 S/m. Superconducting quantum interference device magnetometer-based magnetic characterization of the treated material revealed an anisotropic ferromagnetic response in the MNP/graphite nanocomposite compared to the isotropic response of MNP. Raman spectroscopy of the MNP/graphite nanocomposite revealed a fourfold improvement in graphitization, suppression in disorder, and decreased nitrogenous impurities compared to the graphitic material obtained from laser treatment of just PI sheets. X-ray photoelectron spectroscopy, x-ray diffraction, and energy-dispersive x-ray spectroscopy were used to delineate the phase transformations of MNP during the formation of MNP/graphite nanocomposite. Post-mortem characterization indicates a possible photocatalytic effect of MNP during MNP/graphite nanocomposite formation. Under laser irradiation, MNP transformed from the initial Fe 3 O 4 phase to γ-Fe 2 O 3 and Fe 5 C 2 phases and acted as nucleation spots to catalyze the graphitization process of PI.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Lithium plating induced degradation during fast charging of batteries subjected to compressive loading

Here we report the lithium plating associated capacity loss during fast charging of compressively loaded lithium-ion batteries (LIBs). The charging and discharging of LIB under compressive loading during service may affect the cell performance or initiate localized defects in the electrodes. Pouch cells of capacity 20 mAh were compressively loaded to nominal pressures of 0–440 kPa and subjected to 10 cycles of fast charging at 1 C and 4 C. Experimental results show that cells charged at 4 C-rate experienced significant capacity fade, and applying compressive loads exacerbated the capacity loss. The coulombic efficiency study shows that active lithium loss was higher for the initial cycles before gradually reducing to a minimal capacity loss for the tenth charging cycle. The cell voltage relaxation immediately after charging was monitored to identify the stripping of plated lithium after fast charging cycles and showed that the duration of lithium stripping was higher for cells under mechanical compressive loading. Scanning electron microscopy (SEM) and electron paramagnetic resonance spectroscopy (EPR) characterization of the anode showed significantly higher lithium deposits on the anodes charged at a 4 C rate under compressive loads. These results indicate that applied mechanical compression causes increased lithium plating during fast charging of batteries.

25 ENERGY STORAGE↗

DOE OSTI2022

Electrochemical-driven green recovery of lithium, graphite and cathode from lithium-ion batteries using water

The expected exponential increase in consumption of lithium-ion batteries (LIBs) would pose a unique challenge to the availability of near-critical resources like lithium and graphite in the upcoming decade. In this work, we present a lithium recovery process that utilizes a degradation mechanism, i.e., lithium plating, as a tool to concentrate metallic lithium at the anode/separator interface for convenient extraction at room temperature – using only water. Electrochemical characterization of fast charged (1–6 C) LIBs yielded a maximum capacity fade of 50% over ten cycles. The lithium plating was confirmed via voltage plateau analysis, coulombic efficiency, and DC resistance measurements. A maximum lithium plating condition was observed to exist between 4C and 5C, thereby limiting the energy consumption in the extraction process. Post-mortem film thickness measurement showed an incrementing film deposition with a maximum of 35 µm thickness. SEM and XPS analysis confirmed increasing concentration of a dense dendritic metallic lithium deposition on the anode/separator interface with C-rate. A green recovery process was adopted to extract the concentrated metallic lithium using distilled water. The lithium from the plated film, solid/electrolyte interface (SEI), electrolyte, anode, and cathode, was extracted as salts. A 37% improvement in lithium recoverability was achieved with fast charging under ambient conditions. XPS analysis showed ~92% of lithium yield with no residual lithium in the graphite. In addition, the battery-grade graphite was recovered with 97% purity after heat treatment of the washed anode film, and concentrated transition metals oxides in the cathode to 93% purity for convenient extraction.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2022

Direct observation of elemental fluctuation and oxygen octahedral distortion-dependent charge distribution in high entropy oxides

The enhanced compositional flexibility to incorporate multiple-principal cations in high entropy oxides (HEOs) offers the opportunity to expand boundaries for accessible compositions and unconventional properties in oxides. Attractive functionalities have been reported in some bulk HEOs, which are attributed to the long-range compositional homogeneity, lattice distortion, and local chemical bonding characteristics in materials. However, the intricate details of local composition fluctuation, metal-oxygen bond distortion and covalency are difficult to visualize experimentally, especially on the atomic scale. Here, we study the atomic structure-chemical bonding-property correlations in a series of perovskite-HEOs utilizing the recently developed four-dimensional scanning transmission electron microscopy techniques which enables to determine the structure, chemical bonding, electric field, and charge density on the atomic scale. The existence of compositional fluctuations along with significant composition-dependent distortion of metal-oxygen bonds is observed. Consequently, distinct variations of metal-oxygen bonding covalency are shown by the real-space charge-density distribution maps with sub-ångström resolution. The observed atomic features not only provide a realistic picture of the local physico-chemistry of chemically complex HEOs but can also be directly correlated to their distinctive magneto-electronic properties.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Anodic Interfacial Evolution in Extremely Fast Charged Lithium-Ion Batteries

Interfacial reaction mechanisms at the anode/separator interface play a central role in the performance and safety of lithium-ion batteries during fast charging. We report a mechanistic study on the evolution and interactions of the aging mechanisms at the anode/separator interface in lithium cobalt oxide/graphite pouch cells charged with variable charging rates (1–6C) over 10 cycles. In situ electrochemical measurements, including voltage relaxation, Coulombic efficiency, and direct current internal resistance, indicated an incremental lithium loss until the C rates were ≤5C. A substantial capacity fade is observed in the first few cycles of fast charging, but the magnitude of capacity fade progressively diminishes with the number of cycles, indicating a suppression in the lithium deposition mechanism. Post-mortem film thickness, X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM) analyses were performed to elucidate the evolution of electrolyte decomposition, the solid–electrolyte interface (SEI), lithium plating, and film fracture mechanisms with C rate. XPS measurements confirmed an increasing lithium concentration in an SEI film with an increase in the C rate. SEM images showed a growth of dendritic lithium on the anode surface from 1C to 3C. Precrack formation leading to an interfacial film fracture was observed at higher C rates. Furthermore, a differential analysis of the discharge capacity indicated a possible two-phase delithiation from the anode and reduced cathodic lithiation due to lithium loss at high C rates.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Parametric analysis of anodic degradation mechanisms for fast charging lithium batteries with graphite anode

In this work, we report the impact of the temperature-driven synergistically-coupled anodic degradation mechanisms on the electrochemical performance of lithium batteries with graphite anode over multiple cycles. Temperature dependence of electrochemical reactions and damage mechanisms, such as solid electrolyte interface (SEI) growth, lithium plating/stripping, dead lithium storage/dissolution, and film cracking are incorporated into the degradation model. Results of a parametric analysis are presented, evaluating the effects of charging rates (1–6 C), operating temperatures (-15 – 45°C) and electrode design parameters, on the relative performance fade in the lithium-ion battery. Thermo-electrochemical process maps are developed to provide insights into the relationship between electrode performance and failure mechanisms. The simulation results predict a severe capacity loss due to lithium plating at low temperatures, which is further aggravated at high charging rates. A common strategy for mitigating lithium plating, through charging at high temperatures, also results in rapid capacity loss due to accelerated SEI formation. Simulation results are used to identify the combination of operating conditions and electrode design parameters that improve the electrochemical performance of the battery. These results demonstrate an opportunity to design safe and high-performance lithium-ion batteries, guided by anodic degradation models.

Battery design↗

DOE OSTI2021

Magnetohydrodynamic Control of Interfacial Degradation in Lithium-Ion Batteries for Fast Charging Applications

Interfacial anodic degradation in graphitic materials under fast charging conditions causes severe performance loss and safety hazard in lithium ion batteries. We present a novel method for minimizing the growth of these aging mechanism by application of an external magnetic field. Under magnetic field, paramagnetic lithium ions experience a magnetohydrodynamic force, which rotates the perpendicularly diffusing species and homogenizes the ionic transport. This phenomenon minimizes the overpotential hotspots at the anode/separator interface, consequently reducing SEI growth, lithium plating, and interfacial fracture. In situ electrochemical measurements indicate an improvement in capacity for lithium cobalt oxide/graphite pouch cell (20 mAh) charged from 1–5 C under an applied field of 1.8 kG, with a maximum capacity gain of 22% at 5C. Post-mortem FE-SEM and EDS mapping shows that samples charged with magnetic field have a reduced lithium deposition at 3C and a complete suppression of interfacial fracture at 5C. At 5C, a 24% reduction in the lithium content is observed by performing XPS on the anodic interfacial film. Finally, fast charging performance under variable magnetic field strengths indicate a saturation behavior in capacity at high fields (>2 kG), thereby limiting the field and consequent energy requirements to obtain maximum capacity gain under extreme conditions.

electromagnetism↗

DOE OSTI2021

In-situ magnetic alignment model for additive manufacturing of anisotropic bonded magnets

In this work, we report a mathematical framework which predicts the degree of alignment (DoA) in an in-situ aligned additively manufactured 3D printed bonded magnets. A multiphysics model is developed which couples the harmonious interactions of magnetic particles in a viscous flowing polymer under the presence of an external magnetic field. The hydrodynamic fluid-particle interaction is paired with the magnetophoretic force to predict the particle trajectory and distribution during extrusion through a 3D printer nozzle. Succeeding the force balance, a magnetohydrodynamic torque equilibrium analysis is performed to predict the net-orientation of the magnetic particles as a function of the applied field strength, viscous forces, and particle-to-particle interactions (P2P). Experimental validation of the DoA predictions is performed using 65 vol% Nd-Fe-B+Sm-Fe-N in Nylon12 (DoA exp = 0.620 and DoA theory = 0.686) and 15 vol% Sm-Co in PLA (DoA exp = 0.830 and DoA theory = 0.863). A parametric analysis is performed to analyze the effect of operating and design parameters like alignment field strength, magnetic loading fraction, extrusion load, and particle size. The model predicts a competing behavior between particle-fluid and particle-particle interactions under the presence of an applied field. Lastly, the model provides a framework to efficiently predict the DoA in tandem with a functionalized-magnetic 3D printer and allows the user to adjust the operating parameters according to the desired DoA.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Correlating capacity fade with film resistance loss in fast charging of lithium-ion battery

Fast charging of lithium-ion (Li-ion) batteries makes it susceptible to lithium plating. Here, we report the correlation between capacity loss and cell impedance changes in the battery due to lithium electrodeposition. Li-ion pouch cells with nickel-manganese-cobalt cathode and graphite anode were charged at rates varying from 0.5C to 6C. The cell voltage evolution immediately after charging was monitored to identify the C-rates that result in lithium plating. Electrochemical impedance spectroscopy (EIS) was used to monitor the cell impedance evolution. The impedance of battery cells at C-rates lower than 1C and no lithium plating showed minimal changes from their baseline values in the period immediately after charging. However, the impedance of battery cells undergoing lithium plating and C-rates higher than 3C showed a substantial reduction immediately after charging, with recovery back to baseline values after 30 min of relaxation. These observations suggest that lithium plating causes damage to the solid electrolyte interface (SEI) layer on the anode particles during the charging period, followed by the reformation of the SEI during the relaxation period. The measured capacity loss has a linear correlation with observed impedance change. The linear relationship suggests that impedance monitoring may be used for prognostication of the state-of-health of Li-ion batteries.

25 ENERGY STORAGE↗

DOE OSTI2020

Performance degradation due to anodic failure mechanisms in lithium-ion batteries

Here, we report a mechano-chemical model for anodic degradation during fast-charging of nickel-manganese-cobalt (NMC)/graphite (C) cell due to SEI growth, lithium plating/stripping, dead lithium storage, and film fracture of composite SEI and plated lithium film. Degradation of the battery is analyzed for a range of charging rates from 1 to 6 C-rates, and the influence of plating mechanisms – lithium plating and dead lithium deposition and recovery during stripping – on the film resistance of the anode are accounted for in the model. Dynamic evolution of the interfacial properties is modeled using rule-of-mixture approach. Model predictions of plating associated stress fields are used to compute critical energy release rate for film cracking. The results indicate an increased tendency of fracture for thinner SEI film with lithium plating at higher charging rates. The process of reforming the cracked film absorbs a significant portion of the electrode current thereby reducing the cell capacity and plating efficiency. The mechano-chemical model provides an extensive analytical framework for understanding the synergistic coupling of anodic degradation mechanisms, prognosticating conditions of SEI failure, and evaluating the capacity fade and efficiency of lithium-ion battery.

25 ENERGY STORAGE↗

DOE OSTI2020

Functionalizing magnet additive manufacturing with in-situ magnetic field source

Additive manufacturing via 3-D printing technologies have become a frontier in materials research, including its application in the development and recycling of permanent magnets. This work addresses the opportunity to integrate magnetic field sources into 3-D printing process in order to enable printing, alignment of anisotropic permanent magnets or magnetizing of magnetic filler materials, without requiring further processing. Specifically, a nonaxisymmetric electromagnet-type field source architecture was designed, modelled, constructed, installed to a fused filament commercial 3-D printer, and tested. The testing was performed by applying magnetic field while printing composite anisotropic Nd-Fe-B + Sm-Fe-N powders bonded in Nylon12 (65 vol.%) and recycled Sm-Co powder bonded in PLA (15 vol.%). Magnetic characterization indicated that the degree-of-alignment of the magnet powders increased both with alignment field strength (controlled by the electric current applied to the magnetizing system) and the printing temperature. Both coercivity and remanence were found to be strongly dependent on the degree-of-alignment, except for printing performed below but near the Curie temperature of Nd-Fe-B (310 ° C). At applied field of 0.15 kOe, Sm-Co and hybrid Nd-Fe-B/Sm-Fe-N printed samples showed degrees-of-alignment of 83 % and 65 %, respectively. The variations in coercivity were consistent with previous observations in bonded magnet materials. This work verifies that integration of magnetic field sources into 3-D printing processes will result in magnetic alignment of particles while ensuring that other advantages of 3-D printing are retained.

3-D printing↗