NASA NTRS2003

Development of Oxidation Protection Coatings for Gamma Titanium Aluminide Alloys

Metallic material systems play a key role in meeting the stringent weight and durability requirements for reusable launch vehicle (RLV) airframe hot structures. Gamma titanium aluminides (gamma-TiAl) have been identified as high-payoff materials for high-temperature applications. The low density and good elevated temperature mechanical properties of gamma-TiAl alloys make them attractive candidates for durable lightweight hot structure and thermal protection systems at temperatures as high as 871 C. However, oxidation significantly degrades gamma-TiAl alloys under the high-temperature service conditions associated with the RLV operating environment. This paper discusses ongoing efforts at NASA Langley Research Center to develop durable ultrathin coatings for protecting gamma-TiAl alloys from high-temperature oxidation environments. In addition to offering oxidation protection, these multifunctional coatings are being engineered to provide thermal control features to help minimize heat input into the hot structures. This paper describes the coating development effort and discusses the effects of long-term high-temperature exposures on the microstructure of coated and uncoated gamma-TiAl alloys. The alloy of primary consideration was the Plansee alloy gamma-Met, but limited studies of the newer alloy gamma-Met-PX were also included. The oxidation behavior of the uncoated materials was evaluated over the temperature range of 704 C to 871 C. Sol-gel-based coatings were applied to the gamma-TiAl samples by dipping and spraying, and the performance evaluated at 871 C. Results showed that the coatings improve the oxidation resistance, but that further development is necessary.

Wallace, T. A.↗

NASA NTRS2001

Detection of Micro-Leaks Through Complex Geometries Under Mechanical Load and at Cryogenic Temperature

Polymer Matrix Composite (PMC) hydrogen tanks have been proposed as an enabling technology for reducing the weight of Single-Stage-to-Orbit reusable launch vehicles where structural mass has a large impact on vehicle performance. A key development issue of these lightweight structures is the leakage of hydrogen through the composite material. The rate of hydrogen leakage can be a function of the material used, method of 6 fabrication used to manufacture the tank, mechanical load the tank must react, internal damage-state of the material, and the temperatures at which the tank must operate. A method for measuring leakage through a geometrically complex structure at cryogenic temperature and under mechanical load was developed, calibrated and used to measure hydrogen leakage through complex X-33 liquid-hydrogen tank structure sections.

Rivers, H. Kevin↗

NASA NTRS1993

Surface compositional variations of Mo-47Re alloy as a function of temperature

Molybdenum-rhenium alloys are candidate materials for the National Aero-Space Plane (NASP) as well as for other applications in generic hypersonics. These materials are expected to be subjected to high-temperature (above 1200 C) casual hydrogen (below 50 torr), which could potentially degrade the material strength. Since the uptake of hydrogen may be controlled by the contaminant surface barriers, a study of Mo-47Re was conducted to examine the variations in surface composition as a function of temperature from 25 C to 1000 C. Pure molybdenum and rhenium were also examined and the results compared with those for the alloy. The analytical techniques employed were Auger electron spectroscopy, electron energy loss spectroscopy, ion scattering spectroscopy, and x ray photoelectron spectroscopy. The native surface was rich in metallic oxides that disappeared at elevated temperatures. As the temperature increased, the carbon and oxygen disappeared by 800 C and the surface was subsequently populated by the segregation of silicon, presumably from the grain boundaries. The alloy readily chemisorbed oxygen, which disappeared with heating. The disappearance temperature progressively increased for successive dosings. When the alloy was exposed to 800 torr of hydrogen at 900 C for 1 hour, no hydrogen interaction was observed.

Hoekje, S. J.↗

NASA NTRS1992

Oxidation characteristics of Ti-25Al-10Nb-3V-1Mo

Static oxidation kinetics of the super-alpha 2 titanium-aluminide alloy Ti-25Al-10Nb-3V-1Mo (at. percent) were investigated in air over the temperature range of 650 to 1000 C using thermogravimetric analysis. The oxidation kinetics were complex at all exposure temperatures and displayed up to three distinct oxidation rates. Breakaway oxidation occurred after long exposure times at high temperatures. Oxidation products were determined using X-ray diffraction techniques, electron microprobe analysis, and energy dispersive X-ray analysis. Oxide scale morphology was examined by scanning electron microscopy of the surfaces and cross sections of oxidized specimens. The oxides during the parabolic stages were compact and multilayered, consisting primarily of TiO2 doped with Nb, a top layer of Al2O3, and a thin bottom layer of TiN. The transition between the second and third parabolic stage was found to be linked to the formation of a TiAl layer at the oxide-metal interface. Porosity was formed during the third stage, causing degradation of the oxide and the beginning of breakaway oxidation.

Wallace, T. A.↗

NASA NTRS1991

Titanium aluminides - Surface composition effects as a function of temperature

Results are presented from an AES investigation of the surface characteristics of pure Ti, Ti-14Al-21Nb (alpha-2 aluminide), and Ti-33Al-6Nb-1.4Ta (gamma aluminide) under ultrahigh vacuum conditions over the 20-1000 C temperature range. The observed variations in surface composition are noted to be dramatic and indicative of a direct relationship between the amount of retained oxygen and carbon on the surface and the quantity of Al in that surface's vicinity. While TiO2 was the main surface oxide for pure Ti and the alpha-2 and gamma aluminides, only metallic peaks were observable at 600 C; at 1000 C, metallic Al and Ti were observed.

Outlaw, R. A.↗

NASA NTRS1991

Oxidation characteristics of Ti-33Al-6Nb-1.4Ta

Static oxidation kinetics of the gamma titanium-aluminide alloy Ti-33Al-6Nb-1.4Ta (wt pct) have been investigated in air from 700 to 1000 C and in oxygen from 800 to 1000 C using thermogravimetric analysis. The oxidation kinetics were controlled by the presence of alumina for all oxygen exposures and in air below 800 C, while the kinetics in air above 800 C were more complex. Oxidation products were identified using X-ray diffraction techniques. Oxide scale morphology was examined by SEM and TEM of the surfaces and across sections of oxidized specimens. The oxidation products formed depended on the exposure: Al2O3 and TiO2 were identified on all specimens exposed in and air and oxygen; the nitride phases TiN and Ti2AlN were also found on specimens exposed in air.

Wallace, T. A.↗

NASA NTRS1990

The surface variation of Ti-14Al-21Nb as a function of temperature under ultrahigh vacuum conditions

The effect of temperature, at conditions of ultrahigh vacuum, on the surface composition of the Ti-14Al-21Nb (in wt pct) alloy was investigated in samples heated to 1000 C in 100 C increments. Results of AES spectroscopy revealed that the Ti-14Al-21Nb alloy surface is extremely sensitive to temperature. At 300 C, the carbon and oxygen began to rapidly dissolve into the alloy, and at 600 C, bulk S segregated to the surface. The variation in the surface composition was extensive and different over the temperature range studied, indicating that there may be substantial changes in the hydrogen transport.

Lee, W. S.↗

NASA NTRS1989

Static and dynamic oxidation of Ti-14Al-21Nb and coatings

The oxidation of Ti-14Al-21Nb (wt pct) was studied under static conditions at 649 to 1093 C for as long as 120 hr, and under simulated hypersonic flight (dynamic oxidation) conditions at 982 C for as many as 16 half-hour cycles. Under simulated hypersonic flight conditions heavy oxidation and spalling of the oxide was observed. It was concluded that titanium aluminides used in hypersonic applications must have oxidation-protective coatings. In this preliminary study coatings about 1 micron thick were applied by sputter deposition, from solutions, and from sol-gels. It was found that, because of cracks and porosity, the sputter-deposited coatings did not have sufficient film integrity to shield the alloy. Some of the coatings applied from sol-gels demonstrated film integrity in 1 hr exposures at 982 C.

Wiedemann, K. E.↗

NASA NTRS1988

Oxygen transport through high-purity, large-grain Ag

The permeability of oxygen through pure, large-grain Ag membrames has been found to be linear and repeatable over the 400-800 C range, but only at a magnitude that is a factor of 3.2 smaller than ascribed by prior research. AES data indicate the pertinence of grain-boundary considerations, due to the virtual undetectability of intragranular oxygen. Vacuum-desorption of oxygen-saturated Ag is found to occur at the critical temperature of 630 C; this is consistent with the increased mobility of oxygen atoms in the higher temperature regime.

Outlaw, R. A.↗