NASA NTRS1987

Analysis of plasma nitrided steels

The analysis of plasma nitrided steels can be divided to two main categories - structural and chemical. Structural analysis can provide information not only on the hardening mechanisms but also on the fundamental processes involved. Chemical analysis can be used to study the kinetics for the nitriding process and its mechanisms. In this paper preliminary results obtained by several techniques of both categories are presented and the applicability of those techniques to the analysis of plasma-nitrided steels is discussed.

Salik, J.↗

NASA NTRS1986

Stability of surface nucleation

The growth and decomposition rates of nuclei on a surface are expressed in microscopic terms. A stability factor is defined and employed for the derivation of a criterion for nucleus stability. Simulation results indicate that the stability factor can be used as a measure of the system stability.

Salik, J.↗

NASA NTRS1986

Computer simulation of thin-film nucleation and growth - The multilayer mode

The computer simulation of thin-film nucleation and growth, which was previously performed for the case of single monolayer, has been extended to the case of multilayer growth. The simulation results show that the kinetics of multilayer growth is nearly identical to that of monolayer growth. The cluster density resulting from the multilayer mode is similar to that resulting from the monolayer mode at low coverage. At high coverage, multilayer growth results in substantially higher cluster density than that resulting from monolayer growth.

Salik, J.↗

NASA NTRS1986

Analysis of plasma-nitrided steels

Salik, J.↗

NASA NTRS1985

Monte Carlo study of reversible growth of clusters on a surface

The effect of binding energy on the growth of clusters on a two-dimensional square lattice was studied by a means of a Monte Carlo simulation. The results indicate that for binding energies higher than 0.5kT, clusters grow relative to the initial random distribution, while for binding energies lower than 0.5 kT, clusters decompose. It was also found that at low binding energies the equilibrium percentage of atoms that are bound in clusters is linearly dependent on the binding energy. The cluster density behaved in a similar manner. This similarity reflects the fact that at low binding energies the growth proceeds mainly by the formation of new clusters rather than by an increase in the size of existing ones.

Salik, J.↗

NASA NTRS1985

Computer simulation of thin film nucleation and growth

Some of the processes involved in thin film nucleation and growth were simulated by means of a digital computer. The main conclusions drawn from the simulation results are (1) Because of the random nature of the processes involved, a large variation in results is obtained. (2) Upon impingement, clusters are formed up to a coverage of ca. 0.2, and from there on growth of existing clusters, rather than formation of new ones, takes place. (3) Surface migration is responsible for the formation of most of the clusters at coverages smaller than 0.1, whereas at higher coverages most clusters are formed upon impingement. (4) Surface migration accelerates the growth and causes reduction in cluster density. (5) Reevaporation slows the growth and reduces the cluster density dramatically.

Salik, J.↗

NASA NTRS1985

Ion-beam nitriding of steels

The application of the ion beam technique to the nitriding of steels is described. It is indicated that the technique can be successfully applied to nitriding. Some of the structural changes obtained by this technique are similar to those obtained by ion nitriding. The main difference is the absence of the iron nitride diffraction lines. It is found that the dependence of the resultant microhardness on beam voltage for super nitralloy is different from that of 304 stainless steel.

Salik, J.↗

NASA NTRS1985

A computer simulation of thin film nucleation and growth: The Volmer-Weber case

The computer simulation of thin film nucleation and growth, which was previously performed for the case of single monolayer, was modified to include multilayer growth via the Volmer-Weber mechanism. The simulation results show that: (1) the kinetics of multilayer film growth is nearly identical to that of monolayer growth; (2) when no reevaporation takes place, the cluster density resulting from multilayer growth is higher at high coverage than that resulting from monolayer growth; (3) when reevaporation does take place, the cluster density resulting from multilayer growth is nearly identical to that resulting from monolayer growth. This is not due, however, to similarity in microstructure.

Salik, J.↗

NASA NTRS1984

Erosion of iron-chromium alloys by glass particles

The material loss upon erosion was measured for several iron-chromium alloys. Two types of erodent material were used: spherical glass beads and sharp particles of crushed glass. For erosion with glass beads the erosion resistance (defined as the reciprocal of material loss rate) was linearly dependent on hardness. This is in accordance with the erosion behavior of pure metals, but contrary to the erosion behavior of alloys of constant composition that were subjected to different heat treatments. For erosion with crushed glass, however, no correlation existed between hardness and erosion resistance. Instead, the erosion resistance depended on alloy composition rather than on hardness and increased with the chromium content of the alloy. The difference in erosion behavior for the two types of erodent particles suggested that two different material removal mechanisms were involved. This was confirmed by SEM micrographs of the eroded surfaces, which showed that for erosion with glass beads the mechanism of material removal was deformation-induced flaking of surface layers, or peening, whereas for erosion with crushed glass it was cutting or chopping.

Salik, J.↗

NASA NTRS1984

Ion-beam nitriding of steels

Salik, J.↗

NASA NTRS1984

A study of nucleation and growth of thin films by means of computer simulation: General features

Some of the processes involved in the nucleation and growth of thin films were simulated by means of a digital computer. The simulation results were used to study the nucleation and growth kinetics resulting from the various processes. Kinetic results obtained for impingement, surface migration, impingement combined with surface migration, and with reevaporation are presented. A substantial fraction of the clusters may form directly upon impingement. Surface migration results in a decrease in cluster density, and reevaporation of atoms from the surface causes a further reduction in cluster density.

Salik, J.↗

NASA NTRS1983

A review of the use of wear-resistant coatings in the cutting-tool industry

The main mechanisms involved in the wear of cutting tools are reviewed. Evaluation of the different coating properties required for the reduction of the different kinds of wear was also reviewed. The types of coatings and their ranges of applicability are presented and discussed in view of their properties. Various coating processes as well as their advantages and shortcomings are described. Potential future developments in the field of wear-resistant coatings are discussed.

Salik, J.↗

NASA NTRS1981

Effects of erodant particle shape and various heat treatments on erosion resistance of plain carbon steel

Erosion tests were conducted on 1045 steel samples which had been subjected to different heat treatments. The weight of material removed upon erosion with glass beads and crushed glass was measured. The data show that there is no correlation between hardness and erosion resistance. The erosion rate was strongly dependent on the shape of erodant particles, being an order of magnitude higher for erosion with crushed glass than with glass beads. Heat treatment had a profound effect on the erosion resistance when the erodant particles were glass beads but little or no effect when the particles were crushed glass. It is thus concluded that different mechanisms of material removal are involved with these two erodants. This conclusion is supported by the surface morphology of annealed 1045 steel samples which had been eroded by these two types of erodant particles. SEM micrographs of the eroded surfaces show that for erosion with glass beads it is deformation induced fracture of surface layers.

Salik, J.↗

NASA NTRS1981

The effect of mechanical surface and heat treatments on the erosion resistance of 6061 aluminum alloy

The effects of both mechanical surface treatments and heat treatments on the erosion resistance of 6061 aluminum alloy were studied in order to gain a better understanding of material properties which affect erosion behavior. It was found that mechanical surface treatments have little or no effect on the erosion resistance. This is due to the formation by particle impact of a work-hardened surface layer, independent of the initial surface condition. The erosion resistance of aluminum single crystals was found to be independent of orientation, which is due to destruction of the surface microstructure and formation of a polycrystalline surface layer by the particle impact as observed by X-ray diffraction. Although on solution treatment of annealed aluminum 6061 the increase in hardness is accompanied by an increase in erosion resistance, precipitation treatment (which causes a further increase in hardness) results in a slightly lower erosion resistance.

Salik, J.↗

NASA NTRS1981

Effect of mechanical surface and heat treatments on erosion resistance

The effect of erosion by glass beads and crushed glass and by heat treatments on the erosional resistance of 6061 aluminum alloy and 1045 steel were studied. The aluminum alloy's erosion resistance was found to be insensitive to mechanical surface treatment applied before testing, and was determined to depend on the properties of the work-hardened surface layer; this was also demonstrated for aluminum alloy single crystals. The aluminum alloy heat treatments included annealing, solution, and precipitation. Solution was found to increase erosion resistance but precipitation had the opposite effect. Hardness showed no correlation with erosion resistance for either aluminum alloy steel. The steel tests showed that crushed glass provides an order of magnitude more erosion than glass beads.

Salik, J.↗

NASA NTRS1980

An investigation into the role of adhesion in the erosion of ductile metals

Existing theories of erosion of ductile metals based on cutting and deformation mechanisms predict no material removal at normal incidence which is contradictory to experience. Thus, other mechanisms may be involved. The possible role of adhesive material transfer during erosion is investigated by both single-particle impingement experiments and erosion by streams of particles. Examination of the rebounding particles as well as the eroded surfaces yields evidence of a significant adhesive mechanism for the ductile metals investigated.

Brainard, W. A.↗

NASA NTRS1980

Scanning-electron-microscope study of normal-impingement erosion of ductile metals

Scanning electron microscopy was used to characterize the erosion of annealed copper and aluminum surfaces produced by both single- and multiple-particle impacts. Macroscopic 3.2 mm diameter steel balls and microscopic, brittle erodant particles were projected by a gas gun system so as to impact at normal incidence at speeds up to 140 m/sec. During the impacts by the brittle erodant particles, at lower speeds the erosion behavior was similar to that observed for the larger steel balls. At higher velocities, particle fragmentation and the subsequent cutting by the radial wash of debris created a marked change in the erosion mechanism.

Brainard, W. A.↗

NASA NTRS1980

An investigation into the role of adhesion in the erosion of ductile metals

Existing theories of erosion of ductile metals based on cutting and deformation mechanisms predict no material removal at normal incidence which is contradictory to experience. Thus, other mechanisms may be involved. The possible role of adhesive material transfer during erosion is investigated by both single particle impingement experiments and erosion by streams of particles. Examination of the rebounding particles as well as the eroded surface yields evidence of a significant adhesive mechanism for the ductile metals investigated.

Brainard, W. A.↗