Optimization of a Non-arsenic Iron-based Superconductor for Wire Fabrication
Here we report on the optimization of synthesis of iron selenide-based superconducting powders and the fabrication of selenide-based wire. The powders were synthesized by an ammonothermal method, whereby Ba is intercalated between FeSe layers to produce Ba x (NH 3 ) y Fe 2 Se 2 , with tetragonal structure similar to AFe 2 X 2 (X: As, Se), '122', superconductors. The optimal T c (up to 38 K) and Meissner and shielding superconducting fractions are obtained from the shortest reaction time (t) of reactants in liquid ammonia (30 min). With the increase of t, a second crystalline 122 phase, with a smaller unit cell, emerges. A small amount of NH 3 is released from the structure above ~200 °C, which results in loss of superconductivity. However, in the confined space of niobium/Monel tubing, results indicate there is enough pressure for some of NH 3 to remain in the crystal lattice, and thermal annealing can be performed at temperatures of up to 780 °C, increasing wire density and yielded a reasonable T c ≈ 16 K. Here, we report of the first successful wire fabrication of non-arsenic high-T c iron-based superconductor. We find that although bulk materials are estimated to carry critical current densities >100 kA cm ₋2 (4 K, self-field), the current transport within wires need to be optimized (J c ~ 1 kA cm ₋2 ).