A microstructural study of the Tishomingo meteorite
Metallography, electron microscopy, and X-ray diffraction techniques were employed to study a fragment of the Tishomingo iron meteorite. The results suggest the following thermal-mechanical history: The fragment was originally a large crystal of taenite (gamma). Cooling through the alpha + gamma phase boundary did not result in accompanying precipitation of kamacite (alpha). Transformation to a martensitic structure initiated between -25 and -65 C. Transformation continued as the temperature fell to -75 to -115 C, resulting in approx 80% martensite (alpha-prime). Subsequent shock deformation and thermal aging processes substantially modified the taenite and martensite microstructures. Twins in the retained taenite phase are attributed to shock deformation at a pressure estimated for a single event at about 170 kbar. The existing complex altered martensite structure containing both taenite and kamacite (3-15% Ni) particles was apparently the product of both shock deformation and thermal aging processes. The maximum temperature reached during thermal aging is estimated to be less than 400 C and perhaps below 310 C.