Temperature dependent interfacial microstructure in HIP-bonded Al6061/Zr joints

Pressing (HIP) at 450 °C and 560 °C under 103 MPa for 90 minutes to evaluate interfacial diffusion and microstructural evolution. Sound metallurgical bonding was achieved at both temperatures, with Zr serving as an effective diffusion barrier. Microstructural analysis revealed the the formation of a (Al,Si)3Zr intermetallic layer at the Al/Zr interface, whose thickness increased from ~100 nm at 450 °C to ~2100 nm at 560 °C, consistent with temperature-driven diffusion kinetics. The thin and continuous reaction layer observed at 450 °C indicates controlled interdiffusion and minimal reaction zone growth, favorable for maintaining interface stability and ductility. At 560 °C, enhanced atomic mobility led to pronounced intermetallic development, confirming diffusion-controlled growth behavior. These results provide valuable insights for optimizing Al/Zr interface design and diffusion barrier performance in advanced structural and energy systems.

Al/Zr interface↗
DOE OSTI2026

Grain Boundary Effects on Radiation Damage and Tritium Diffusion in Li–Al–O Ceramics from Molecular Dynamics and Experiments

Understanding irradiation damage and tritium transport in LiAlO2 ceramics is essential for their deployment in tritium-producing burnable absorber rods (TPBARs). Grain boundaries (GBs) play an important role in governing radiation response and tritium transport in LiAlO2 and its secondary phase LiAl5O8. Using molecular dynamics simulations, we investigated defect evolution and tritium diffusion during displacement cascades in single-crystal and bicrystal LiAlO2 and LiAl5O8 at 600 K. The results reveal that GBs suppress the damage in the LiAlO2 bicrystals as compared to single crystals, via interstitial emission. The effect is more pronounced for Li defects, than for Al and O. In LiAl5O8 the damage reduction due to introduction of GB is less pronounced overall. Tritium diffusion coefficients at GBs are higher by factors of 2–10 relative to diffusion inside grain bulk. The effect is particularly pronounced in LiAlO2, where S5, S17, and S25 GBs promote rapid tritium transport, whereas LiAl5O8 exhibits slower diffusion due to reduced free volume at its GBs. These findings evince a trade-off that while GBs mitigate radiation damage by absorbing interstitials, they simultaneously provide fast pathways for tritium migration which is not desirable for TPBAR application. The mechanistic insights gained here establish a foundation for microstructural design strategies to balance radiation tolerance and tritium retention in ceramic breeder materials.