Engineering topics

Rosseel, Thomas M.

Publications and source records attributed to Rosseel, Thomas M..

5 records

DOE OSTI2022

Weldability of irradiated Stainless Steel 304 materials harvested from the National Research Universal (NRU) reactor

In this work, the weldability of the neutron-irradiated Stainless Steel 304 (SS 304) materials containing estimated helium levels of 12 to 44 appm has been studied through a Collaborative Research and Development Agreement between the Canadian Nuclear Laboratories and Oak Ridge National Laboratory. The work utilizes a SS 304 component harvested from the National Research Universal reactor. Laser beam welding was used to explore suitable welding conditions and associated parameters, to determine helium concentration limits for successful welding of irradiated stainless-steels. The experimental results show that maximum fusion zone void sizes, fusion zone void quantity and total heat affected zone helium-induced crack length generally increased with increasing He levels and effective weld heat input. A proper combination of welding parameters with low effective heat input, such as, laser power, weld travel speed and wire feed speed, were shown to improve the welding quality, and potentially reduce the length and probability of the formation of grain boundary helium-induced cracking and voids of irradiated SS 304 even with He concentrations as high as about 44 appm.

36 MATERIALS SCIENCE↗

DOE OSTI2022

FFT-based model for irradiated aggregate microstructures in concrete

The concrete biological shield of light water reactors is exposed to neutron and gamma irradiation throughout its lifetime, which results in the long-term degradation of the concrete’s mechanical properties. Under neutron irradiation, the concrete’s aggregates are subjected to radiation-induced volumetric expansion (RIVE), which strongly depends on the mineral content of the aggregate and exhibits the largest expansion in silicate-bearing minerals. In this work, the authors used the fast Fourier transform-based code Microstructure-Oriented Scientific Analysis of Irradiated Concrete (MOSAIC) in 2D to model the expansion of five different aggregates provided by the Japan Concrete Aging Management Program (JCAMP). Comparable rock specimens were irradiated at the JEEP-II test reactor. The model uses realistic aggregate microstructure reconstruction based on high-resolution characterization images. The model accounts for anisotropic RIVE, thermal expansion, and the associated initiation and propagation of damage. The RIVE models are calibrated based on expansion data in the literature. The authors assume that damage occurs exclusively at interfaces between the particles that compose an aggregate and that these interfaces also exhibit swelling. Using a micromechanical model, the evolution of Young’s modulus with RIVE is calculated for each aggregate and compared with Russian irradiation data. The modeled linear expansion agrees well with the experimentally measured expansion. Furthermore, the model also predicts that anisotropic RIVE and thermal expansion result in an earlier onset of damage with neutron fluence than in the isotropic case.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Microstructural Characterization of the Second High Fluence Baffle-Former Bolt Retrieved from a Westinghouse Two-loop Downflow Type PWR

As one of the pressurized water reactor (PWR) internal components, baffle-former bolts (BFBs) are subjected to significant mechanical stress and neutron irradiation from the reactor core during the plant operation. Over the long operation period, these conditions lead to potential degradation and reduced load-carrying capacity of the bolts. In support of evaluating long-term operational performance of materials used in core internal components, the Oak Ridge National Laboratory (ORNL), through the Department of Energy (DOE), Light Water Reactor Sustainability (LWRS) Program, Materials Research Pathway (MRP) has harvested two high fluence BFBs from a commercial Westinghouse two-loop downflow type PWR. The two bolts of interest, i.e. bolts # 4412 and 4416, were withdrawn from service in 2011 as part of a preventative replacement plan. No identification of cracking or potential damage was found for these bolts during their removal in 2011. However, the bolts required a lower torque for removal from the baffle structure than the original torque specified during installation. Irradiation displacement damage levels in the bolts range from 15 to 41 displacements per atom. The goal of this project is to perform detailed microstructural and mechanical property characterization of BFBs following in-service exposures. The information from these bolts will be integral to the LWRS program initiatives in evaluating end of life microstructure and properties. Furthermore, valuable data will be obtained that can be incorporated into model predictions of long-term irradiation behavior and compared to results obtained in high flux experimental reactor conditions. In this report, we present our latest study in FY22 on microstructural characterizations of the second high fluence baffle-former bolt, i.e., bolt # 4412. Analytical electron microscopy and atom probe tomography characterization were performed. The radiation-induced defects in the material add to the large wealth of knowledge for neutron-induced defects in 304/316 grades of stainless steels, specifically for radiation-induced precipitation after high fluence commercial PWR irradiation. The main findings are summarized as follows: 1) The cavity size was considerably larger in the bolt thread section than in the bolt head, with the bolt thread section having a bimodal distribution of cavities greater than ~6 nm in diameter and less than ~3 nm in diameter. The bolt head only had the small-sized cavities. In addition, there was a denuded zone of large cavities near grain boundaries in the thread section of the bolt. 2) Radiation-induced precipitation in the BFB #4412 was highly complex, with the volume fraction, size, and number density of Ni/Si and Cu-rich precipitates depending strongly on the radiation temperature/dose. In many cases, co-precipitates of adjoined clusters were found with Ni/Si-rich precipitates sandwiched between Cu-rich clusters and Mo/Cr/P-rich clusters. 3) Solute segregation out of solution was highest for most solutes in the thread section of the bolt #4412 with the exception of Cu, which experienced more separation out of solution into Curich clusters in the bolt head section. This highlights the difference in the mechanisms for precipitation of Ni/Si clusters, which have the Ni 3 Si phase composition, and precipitation of Cu-rich clusters. 4) There appear to be multiple simultaneous influences that affect the microstructural variation along the length of the bolt that overcomes the ~2X difference in irradiation dose between the bolt head and the bolt thread. The irradiation temperature, thermal/fast neutron ratio variation, potential strain gradient, and exposure to PWR coolant water that each section of the bolt sees may have more influence on the microstructural evolution than the total irradiation dose. The bolt thread and shank, with higher temperature, higher relative fast neutron flux, higher strain, and exposure to coolant but lower dose, underwent more enhanced cavity formation, precipitation, and solute segregation than the bolt head section.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗

DOE OSTI2022

Ultra-high gamma irradiation of calcium silicate hydrates: Impact on mechanical properties, nanostructure, and atomic environments

The concrete biological shield in a nuclear power plant receives ~100–200 MGy gamma dosage during an 80-year design life. However, precise changes in the mechanical properties and atomic environments of C-S-H at ultrahigh irradiation dosages have not been systematically documented. Here, we report that irradiation decreases C-S-H basal spacing (~ 0.6 ± 0.1 Å for 189 MGy) and increases its Young's modulus, which is attributed to the lower basal spacing as the nano porosity potentially increased and microporosity remained unchanged. Irradiation also decreased the molecular water content and increased hydroxyl groups in C-S-H, showing that interlayer water removal reduces the basal spacing. Finally, 1 H and 29 Si NMR results indicate some disorder in the local proton CaO-H species and slight depolymerization of the silicate structure. Together, these results indicate that the C-S-H gel stiffens upon ultrahigh gamma irradiation dosage, a finding which concerns long-term nuclear power plants operations worldwide.

1H NMR↗

DOE OSTI2022

Assessment of San Onofre Concrete Susceptibility Against Irradiation Damage

The work performed under this contract covers the characterization of unirradiated concrete specimens cored from the walls of the steam generator room of the SONGS Unit 2, currently under decommission. This report documents the extensive set of characterization conducted at the Oak Ridge National Laboratory, at the University of Tennessee, Knoxville, at the Ohio State University, and at ALG Global. The susceptibility of irradiation-induced damage in concrete is governed by the exposure level (fast neutron fluence > 10 19 n.cm -2 at E > 0.1 MeV) and the mineralogy of the aggregates (high quartz content and chemical heterogeneity of the assemblage). Both conditions are met for the SONGS concrete biological shield. Hence, harvesting in-service irradiated concrete from the SONGS Unit 2 or 3 biological shield is currently an unparalleled opportunity to study the flux effects of neutron irradiation.

36 MATERIALS SCIENCE↗