Insight into the interfacial microstructure and chemistry of hot isostatically pressed AA6061-AA6061 bonds for U-10Mo fuel cladding application

Here, in the present study, hot isostatic pressing (HIP) bonding was carried out using AA6061-AA6061 plates for U-10Mo monolithic fuel cladding application. HIP was performed at 560°C with an applied isostatic pressure of 103 MPa for 90 min. Interfacial microstructure characterizations were performed using scanning electron microscopy (SEM) combined with electron backscatter diffraction (EBSD) to quantify precipitate fractions and study recrystallization, grain growth, and orientation relationships across the interface. EBSD results confirmed that no interfacial grain growth occurred during the HIP process. Transmission electron microscopy (TEM) was also employed to quantify composition and identify phases of various precipitates and an oxide layer that formed at the interface during HIP bonding. Microstructural analyses revealed the formation of a large fraction of Mg 2 Si precipitate and a ~50 nm thick Mg-oxide layer at the interface. Further TEM analysis confirmed that the oxide layer was not continuous, and Mg 2 Al 2 O 5 oxide particles with an average size of 18 nm were present in the oxide layer. Finite element modeling analysis was performed to study the stress distribution at the interface during HIP processing.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2023

Hot Rolling of ZK60 Magnesium Alloy with Isotropic Tensile Properties from Tubing Made by Shear Assisted Processing and Extrusion (ShAPE)

In the present work, we utilized Shear Assisted Processing and Extrusion (ShAPE), a solid-phase processing technique, to extrude hollow tubes of ZK60 Mg alloy. Hot rolling was performed on these as-extruded tubes (after slitting them longitudinally) to thickness reductions of 37%, 68%, and 93% to investigate their viability as rolling feedstock material. EBSD analysis showed the formation of twinned grains in the ShAPE processed material and a gradual re-orientation of the basal texture parallel to the extrusion direction with each rolling step. Moreover, an equiaxed grain size of 5.15 ± 3.39 μm was obtained in the ShAPE extruded material, and the microstructure was retained even after 93% rolling reduction. The rolled sheets also showed excellent tensile strengths and no mechanical anisotropy, a critical characteristic for formability. The unique microstructures developed and their excellent mechanical properties, combined with the ease of scalability of the process, make ShAPE a promising alternative to existing methods for producing rolling feedstock material.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Reinforcing the exit hole from friction stir welding and processing

After friction stir welding/processing (FSW/P), an exit hole remains at the end of the run, which can be the weakest region of the welded/processed workpiece. In addition, tensile residual stress around the exit hole resulting from heating during FSW/P facilitates incipient crack initiating from the exit hole under external loading. Current solutions include removing or repairing the exit hole, which are time-consuming and costly. Here, we propose a novel method to reinforce the exit hole by applying an additional FSW/P pass around it, in a way that replaces preexisting tensile residual stress with compressive residual stress. Under external loading, there is no evident strain accumulation around the exit hole, and the workpiece ultimately fails along the FSW/P heat affected zone. This method provides a more convenient way to reinforce the exit hole than the current exit-hole repair or removal methods for industrial applications.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Correlation between Interface Microstructure and Bond Strength of Al6061/Al6061 HIP-Bonded Plates for Fuel Cladding Application

The effects of hot isostatic pressing (HIP) processing parameters on microstructure and bond strength of Al6061/Al6061 plate interfaces were systemically investigated at the micro- and nanoscale. The HIP bonding of the two aluminum plates was performed at four temperatures: 350°C, 400°C, 450°C, and 560°C. The results reveal the formation of micron scaled Mg 2 Si precipitate and uniform nano scaled Mg 2 Al 2 O 5 oxide at the interface. The formation of Mg 2 Al 2 O 5 is closely associated with the fast bulk diffusion of Mg from the Al matrix to the amorphous Al 2 O 3 /Al interface and subsequent reaction between Mg and Al 2 O 3 . Finally, the highest and lowest bond strengths were observed in samples HIP bonded at 450°C and 350°C, respectively.