Rohatgi, A.

Publications and source records attributed to Rohatgi, A..

At least 19 records
All sourcesNASA NTRSDOE OSTI
NASA NTRS1986

Interaction of low-energy implanted atomic H with slow and fast diffusing metallic impurities in Si

The interaction of hydrogen, injected into silicon using low-energy ion bombardment, with slow (Ti and V) and fast (Cr and Au) diffusing impurities was investigated. It was found that this H ion bombardment of the Si surface was effective in reducing the electrically active concentration of only the fast diffusing impurities. The results are explained by damage enhanced diffusivity and surface gettering of the fast diffusing impurities.

Singh, R.↗
NASA NTRS1986

Effect of low-energy hydrogen ion implantation on dendritic web silicon solar cells

The effect of a low-energy (0.4 keV), short-time (2-min), heavy-dose (10 to the 18th/sq cm) hydrogen ion implant on dendritic web silicon solar cells and material was investigated. Such an implant was observed to improve the cell open-circuit voltage and short-circuit current appreciably for a number of cells. In spite of the low implant energy, measurements of internal quantum efficiency indicate that it is the base of the cell, rather than the emitter, which benefits from the hydrogen implant. This is supported by the observation that the measured minority-carrier diffusion length in the base did not change when the emitter was removed. In some cases, a threefold increase of the base diffusion length was observed after implantation. The effects of the hydrogen implantation were not changed by a thermal stress test at 250 C for 111 h in nitrogen. It is speculated that hydrogen enters the bulk by traveling along dislocations, as proposed recently for edge-defined film-fed growth silicon ribbon.

Rohatgi, A.↗
NASA NTRS1986

Impurity effects in silicon for high efficiency solar cells

Model analyses indicate that sophisticated solar cell designs including, e.g., back surface fields, optical reflectors, surface passivation, and double layer antireflective coatings can produce devices with conversion efficiencies above 20 percent (AM1). To realize this potential, the quality of the silicon from which the cells are made must be improved; and these excellent electrical properties must be maintained during device processing. As the cell efficiency rises, the sensitivity to trace contaminants also increases. For example, the threshold Ti impurity concentration at which cell performance degrades is more than an order of magnitude lower for an 18-percent cell. Similar behavior occurs for numerous other metal species which introduce deep level traps that stimulate the recombination of photogenerated carriers in silicon. Purification via crystal growth in conjunction with gettering steps to preserve the large diffusion length of the as-grown material can lead to the production of devices with efficiencies aboved 18 percent, as has been verified experimentally.

Hopkins, R. H.↗
NASA NTRS1986

High-efficiency silicon solar cells - Development, current issues and future directions

This paper provides a review of material, process, and design considerations that are essential for achieving high-efficiency silicon solar cells. It describes an approach that resulted in 18.0-18.5-percent-efficient cells on low-resistivity float-zone silicon material. It is shown experimentally that a combination of surface passivation and double-layer antireflection coating can provide 2-3 percent (absolute) improvement in cell efficiency provided the material, process and cell design are carefully selected.

Rohatgi, A.↗
NASA NTRS1986

A review of high-efficiency silicon solar cells

Various parameters that affect solar cell efficiency were discussed. It is not understood why solar cells produced from less expensive Czochralski (Cz) silicon are less efficient than cells fabricated from more expensive float-zone (Fz) silicon. Performance characteristics were presented for recently produced, high-efficient solar cells fabricated by Westinghouse Electric Corp., Spire Corp., University of New South Wales, and Stanford University.

Rohatgi, A.↗
NASA NTRS1985

Development of high-efficiency solar cells on silicon web

High-efficiency dendritic cells were discussed. The influence of twin planes and heat treatment on the location and effect of trace impurities was of particular interest. Proper heat treatment often increases efficiency by causing impurities to pile up at twin planes. Oxide passivation had a beneficial effect on efficiency. A very efficient antireflective (AR) coating of zinc selenide and magnesium fluoride was designed and fabricated. An aluminum back-surface reflector was also effective.

Rohatgi, A.↗
NASA NTRS1985

Laser-assisted solar cell metallization processing

Laser-assisted processing techniques for producing high-quality solar cell metallization patterns are being investigated, developed, and characterized. The tasks comprising these investigations are outlined.

Rohatgi, A.↗
NASA NTRS1984

Development of high efficiency solar cells on silicon web

Web base material is being improved with a goal toward obtaining solar cell efficiencies in excess of 18% (AM1). Carrier loss mechanisms in web silicon was investigated, techniques were developed to reduce carrier recombination in the web, and web cells were fabricated using effective surface passivation. The effect of stress on web cell performance was also investigated.

Rohatgi, A.↗
NASA NTRS1984

Development of high-efficiency solar cells on silicon web

The development of high efficiency solar cells on a silicon web is discussed. Heat treatment effects on web quality; the influence of twin plane lamellae, trace impurities and stress on minority carrier lifetime; and the fabrication of cells are discussed.

Rohatgi, A.↗
NASA NTRS1984

Ti/Pd/Cu Contacts for Semiconductor Devices

Copper systems equivalent in performance to silver or gold systems. Titanium layer and palladium layer deposited on semiconductor device by electron beam evaporation. Desired pattern etched using photoresist. Thin layer of copper plated on contact pattern from cyanide solution. Copper layer then built up to 4 to 8 microns by electroplatng from acid solution.

Campbell, R. B.↗
NASA NTRS1984

Emitter formation in dendritic web silicon solar cells

The use of liquid dopants and liquid masks for p-n junction formation in dendritic web solar cells was investigated and found to be equivalent to the use of gaseous dopants and CVD SiO2 masks previously used. This results in a projected cost reduction of 0.02 1980$/Watt for a 25 MW/year production line, and makes possible junction formation processes having a higher throughput than more conventional processes. The effect of a low-energy (0.4 keV) hydrogen ion implant on dendritic web solar cells was also investigated. Such an implant was observed to improve Voc and Jsc substantially. Measurements of internal quantum efficiency suggest that it is the base of the cell, rather than the emitter, which benefits from the hydrogen implant. The diffusion length for electrons in the p-type base increased from 53 microns to 150 microns in one case, with dendritic web cell efficiency being boosted to 15.2 percent. The mechanism by which low-energy hydrogen ions can penetrate deeply into the silicon to effect the observed improvement is not known at this time.

Meier, D. L.↗
NASA NTRS1982

Silicon materials task of the Low Cost Solar Array Project: Effect of impurities and processing on silicon solar cells

The effects of impurities and processing on the characteristics of silicon and terrestrial silicon solar cells were defined in order to develop cost benefit relationships for the use of cheaper, less pure solar grades of silicon. The amount of concentrations of commonly encountered impurities that can be tolerated in typical p or n base solar cells was established, then a preliminary analytical model from which the cell performance could be projected depending on the kinds and amounts of contaminants in the silicon base material was developed. The impurity data base was expanded to include construction materials, and the impurity performace model was refined to account for additional effects such as base resistivity, grain boundary interactions, thermal processing, synergic behavior, and nonuniform impurity distributions. A preliminary assessment of long term (aging) behavior of impurities was also undertaken.

Hopkins, R. H.↗
NASA NTRS1981

Silicon materials task of the low-cost solar array project. Phase 4: Effects of impurities and processing on silicon solar cells

The effects of impurities, various thermochemical processes, and any impurity-process interactions upon the performance of terrestrial solar cells are defined. The results form a basis for silicon producers, wafer manufacturers, and cell fabricators to develop appropriate cost benefit relationships for the use of less pure, less costly solar grade silicon.

Hopkins, R. H.↗
NASA NTRS1981

Silicon materials task of the low-cost solar array project. Phase 4: Effects of impurities and processing on silicon solar cells

The results of the study form a basis for silicon producers, wafer manufacturers, and cell fabricators to develop appropriate cost-benefit relationships for the use of less pure, less costly solar grade silicon. Cr is highly mobile in silicon even at temperatures as low as 600 C. Contrasting with earlier data for Mo, Ti, and V, Cr concentrations vary from place to place in polycrystalline silicon wafers and the electrically-active Cr concentration in the polysilicon is more than an order of magnitude smaller than would be projected from single crystal impurity data. We hypothesize that Cr diffuses during ingot cooldown after growth, preferentially segregates to grain and becomes electrically deactivated. Accelerated aging data from Ni-contaminated silicon imply that no significant impurity-induced cell performance reduction should be expected over a twenty year device lifetime.

Hopkins, R. H.↗
NASA NTRS1981

The properties of polycrystalline silicon solar cells with controlled titanium additions

By coupling the results of electrical measurements, such as spectral response, lighted and dark I-V determinations, and deep-level-transient spectroscopy with optical and laser scan photomicroscopy, the effects of grain boundaries and impurities on silicon solar cells were evaluated. Titanium, which produces two deep levels in silicon, degrades cell performance by reducing bulk lifetime and thus cell short-circuit current. Electrically active grain boundaries induce carrier recombination in the bulk and depletion regions of the solar cell. Experimental data imply a small but measurable segregation of titanium into some grain boundaries of the polycrystalline silicon containing high Ti concentration. However, for the titanium-contaminated polycrystalline material used in this study, solar cell performance is dominated by the electrically active titanium concentration in the grains. Microstructural impacts on the devices are of secondary importance

Rohatgi, A.↗
NASA NTRS1980

Investigation of contact metallization systems for solar cells

In conventional solar cells, evaporated Ti-Pd-Ag metallization system has been found reliable. However, for low cost terrestrial applications, its cost effectiveness may be questioned. Electroplated Ag and Cu have been investigated as replacements for evaporated Ag and have given results comparable to the evaporated Ti-Pd-Ag system.

Campbell, R. B.↗
NASA NTRS1980

Impurities in silicon solar cells

The paper investigates the effects of metallic impurities on the performance of silicon solar cells. Czochralski and polycrystalline ingots were employed with boron and phosphorus as primary dopants and with controlled additions of secondary impurities. The data obtained from over 200 crystals indicate that impurity-induced performance loss is primarily due to a reduction of the base diffusion length. Based on this observation, a model is developed which predicts cell performance as a function of secondary impurity concentrations. The model calculations are in good agreement with experimental values except for Cu, Ni, Fe, and to a lesser degree, carbon, which at higher concentrations degrade the cell by junction defect mechanisms.

Davis, J. R., Jr.↗