DOE OSTI2024

Wrought Aluminum-Cerium Alloys by Shear Assisted Processing and Extrusion

Al-Ce alloys have attracted recent interest because of their high thermal stability due to the very low solubility of Ce in the Al matrix. The Al 11 Ce 3 eutectic phase gives excellent strain hardening behavior and moderate high-temperature strength in the as-cast state. However, its strengthening effect is limited by its coarse as-cast structure. Therefore, alternative manufacturing methods such as additive manufacturing or equal channel angular pressing have been applied to refine the Al 11 Ce 3 phase to good effect. However, these techniques are both expensive and time-consuming. Therefore, this study aims to use Shear Assisted Processing and Extrusion (ShAPE), an emerging solid phase processing technique that is more easily scalable than the previously mentioned methods. ShAPE can produce useful cross-sections of an Al-8Ce-4Mg alloy while refining the Al 11 Ce 3 phase to produce a higher strength material. It was found that a low temperature ShAPE process can improve the room temperature yield strength by ~60% compared to a binary Al-4Mg alloy. Additionally, the high-temperature yield strength of the Al-Ce alloys increased by 20%, with a simultaneous 15% improvement in ductility compared to the binary Al-Mg alloy. These results highlight the potential for ShAPE as a processing technique for Al-Ce alloys.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Solid Phase Processing at the Extreme

The effective application of high-flow-stress materials in the realm of Solid Phase Processing frequently necessitates operating at elevated temperatures and substantially high force. These rigorous processing conditions give rise to intricate predicaments concerning the durability of the tools and dies involved, as well as the efficient utilization of process energy. This project is centered on the investigation of the fundamental scientific aspects inherent to these challenges. We aim to delve into the details of how materials react when subjected to intense shear forces at die interfaces, determine the metallurgical interactions occurring at the interfaces with the dies, and investigate the consequences of extreme temperatures on material flow, microstructural evolution, and resultant properties.

36 MATERIALS SCIENCE↗

DOE OSTI2023

High-speed friction stir butt welding of 25.4 mm thick 7175-T79 aluminum alloy

This presents the first experimental demonstration of friction stir butt welding of 25.4 mm thick high-strength, precipitate-strengthened 7XXX aluminum alloy at a welding speed above 500 mm/min and penetration depth greater than 10 mm. Tool pin threads that terminate away from the shoulder region, helped mitigate nearby stress concentration during tool traversing, enabling a higher welding speed while avoiding pin fracture near shoulder. Two kinds of welds—one-sided with full penetration of the plate thickness and double-sided with partial penetration of the plate thickness—were conducted. Significant grain refinement (grain size 1.3 ± 0.8 µm) was evident at the junction of double-sided friction stir welding (FSW) compared to other regions of weld-nugget or base material. Cross-weld tensile testing with digital image correlation revealed high local strains at the junction of double-sided FSW before macro-yield. This strain concentration impeded the typical early necking on advancing/retreating sides of FSW joints, improving the yield strength of as-welded double-sided FSW by 20–24% over slow- to medium-speed one-sided FSW. In conclusion, the joint efficiency of as-welded, double-sided high-speed FSW was about 76% with respect to the base material’s ultimate tensile strength.

36 MATERIALS SCIENCE↗

DOE OSTI2023

Effect of high iron content on direct recycling of unhomogenized aluminum 6063 scrap by Shear Assisted Processing and Extrusion

Not Available

36 MATERIALS SCIENCE↗

DOE OSTI2023

Extrusion processes for forming extrusions of a desired composition from a feedstock

Devices and methods for performing shear-assisted extrusion processes for forming extrusions of a desired composition from a feedstock material are provided. The processes can use a device having a scroll face having an inner diameter portion bounded by an outer diameter portion, and a member extending from the inner diameter portion beyond a surface of the outer diameter portion.Extrusion feedstocks and extrusion processes are provided for forming extrusions of a desired composition from a feedstock. The processes can include providing a feedstock having at least two different materials and engaging the materials with one another within a feedstock container.Methods for preparing metal sheets are provided that can include preparing a metal tube via shear assisted processing and extrusion; opening the metal tube to form a sheet having a first thickness; and rolling the sheet to a second thickness that is less than the first thickness.

Whalen, Scott A.↗

DOE OSTI2023

Shear Assisted Processing and Extrusion (ShAPE) of Lightweight Automotive Components (CRADA 418)

Shear Assisted Processing and Extrusion (ShAPE) was developed to manufacture non-circular multicell profiles from secondary aluminum. This was accomplished by integrating a porthole die approach within the rotating ShAPE process. Complexity of the profile geometry was deliberately advanced over the course of the project from round to square, to asymmetric trapezoidal, to two-cell asymmetric trapezoidal. Aluminum alloy 6063 in the form of briquettes (compacted shreddings and engineered machining chips) and castings from pre-consumer industrial scrap were utilized as the feedstock. Tensile properties were shown to exceed the ASTM minimum standard and ASM typical values with the best results reaching yield strength = 247 ± 10 MPa, ultimate tensile strength = 271 ± 10 MPa, and uniform elongation = 16.5 ± 2.4%. These values were achieved for porthole extrusion using unhomogenized castings made from 100% aluminum 6063 industrial scrap. The ability to extrude unhomogenized billet was made possible by in situ conversion of plate-like β-type Fe-rich intermetallics to more extrudable needle-like α-type which is not possible with conventional extrusion. By eliminating the need to dilute iron with primary aluminum during the recycling process, savings of >90% on lifecycle carbon footprint and >50% on embedded energy could ultimately result in lower cost, more environmentally friendly, automotive components.

42 ENGINEERING↗

DOE OSTI2022

Method for forming hollow profile non-circular extrusions using shear assisted processing and extrusion (ShAPE)

A process for forming extruded products using a device having a scroll face configured to apply a rotational shearing force and an axial extrusion force to the same preselected location on material wherein a combination of the rotational shearing force and the axial extrusion force upon the same location cause a portion of the material to plasticize, flow and recombine in desired configurations. This process provides for a significant number of advantages and industrial applications, including but not limited to extruding tubes used for vehicle components with 50 to 100 percent greater ductility and energy absorption over conventional extrusion technologies, while dramatically reducing manufacturing costs.

Joshi, Vineet V.↗

DOE OSTI2022

Solid Phase Processing of Lead-Free Brass with Carbon Additives

Currently, “lead-free” brass alloys (like C27450/C27451/C6930), used extensively in drinking water fixtures and automotive, electrical, and electronic applications contain maximum 0.25% lead to maintain mechanical performance and machinability. Adding graphite to brass as an alternative to lead, using casting, powder metallurgy, and extrusion methods, has been explored previously. However, all these methods have proven to be energy-, time-, and resource-intensive, while not enabling performance equivalent to that of C36000 brass. In this project, we developed a one-step approach using friction extrusion and ShAPE to make lead-free brass/graphite components such as wires, rods and tubes with mechanical performance equivalent to commercial lead-free brass alloys. Manufacturing temperatures were maintained ~550-730 °C with feed rates ranging between 4 – 25 mm/min. Results show larger grains at the center of the rods and wires with smaller grains developing at the edges. Graphite particles were sheared in the direction of extrusion with higher strains observed towards the edges. Hardness of the brass/graphite samples was over 25% higher than that of the corresponding brass-only samples (rods and wires), also friction extruded. Our results show that the sub-micron graphite plays an important role in limiting process temperature and restraining grain growth during friction extrusion, thus reducing grain size in composites.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Devices and methods for performing shear-assisted extrusion, extrusion feedstocks, extrusion processes, and methods for preparing metal sheets

Whalen, Scott A.↗

DOE OSTI2021

Shear Assisted Processing and Extrusion (ShAPE) of Aluminum Alloy 7075, 2024, and Al-12.4TM

The most common aluminum alloys utilized in the aerospace industry are 7075 and 2024 due to their high strength-to-weight ratio compared to advanced high strength steels and other aluminum alloys. Despite excellent performance, these aluminum alloys have seen limited use outside of the aerospace industry due in part to high cost. If high-performance aluminum extrusions could be made more cost effectively by eliminating energy intensive process steps typical of conventional extrusion, then numerous opportunities exist for more widespread adoption. A key reason for the high cost of 7075 and 2024 extrusions (25-75% higher than 6061) is their slow extrusion speed. 7075 and 2024 are limited to 2 m/min and 3.5 m/min respectively, in contrast to 6061 which can be extruded at 20–80 m/min. In addition to slow speed, aluminum alloys require numerous thermal treatments throughout the extrusion process including homogenization and pre-heating prior to extrusion, and solution heat treating and artificial aging after extrusion. Each of these steps contribute to the total energy consumed during manufacturing of extruded components. This project investigates the use of ShAPE to improve extrusion speed and reduce, or even eliminate, the typical thermal treatments for high strength aluminum alloys, all while improving material performance. The overarching goal of this project was to demonstrate that Shear Assisted Processing and Extrusion (ShAPE) can manufacture high-performance aluminum alloy tubing with lower manufacturing energy and improved mechanical properties compared to conventional extrusion. Unlike conventional extrusion where the billet is rammed against a stationary die using a strictly linear motion, the ShAPE process superimposes a rotational shear force by spinning the die while the billet is plunged. Compared to conventional linear extrusion, the ShAPE process imparts significantly more strain into the feedstock material, which enables the formation of novel microstructures. These microstructures manifest an array of property and process improvements for extrusion of high-performance aluminum alloys. The following accomplishments were achieved for this project: Extrusion of 7075 at 12.2 meters/min compared to 2 meters/min for conventional extrusion; Elimination of 7075 billet homogenization (430 °C for 20 hours) which is required prior to conventional extrusion; Elimination of 7075 billet pre-heating (400 °C for 1 hour) in a separate furnace which is required prior to conventional extrusion; Achieved 7075-T6with yield strength = 595 MPa, ultimate tensile strength = 531MPa, and elongation = 17.4% for extrusions made from unhomogenized billets. Exceeds the ASTM and ASM standard, and typical industry values; Achieved 7075-T5 (i.e., no solution heat treatment) with yield strength = 588 MPa, ultimate tensile strength = 535 MPa, and elongation = 14.8% for extrusions made from homogenized billets; Extrusion of 2024 at 7.4 meters/min compared to 3.5 meters/min for conventional extrusion; Achieved 2024-T8510 yield strength = 522 MPa, ultimate strength = 510MPa, and elongation = 7.1% for extrusions made from wrought billets. Exceeds the ASTM and ASM standard, and typical industry values; Extrusion of Al-12.4TM high-performance aluminum powder directly into tubing, in a single step, which eliminates process steps typical of powder metallurgy extrusion.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Evaluation of orthogonal strain components in friction extrusion

Not Available

36 MATERIALS SCIENCE↗

DOE OSTI2021

Discovering SPP Thermomechanical Pathways

Final report for SPPSi project in Thrust One Friction extrusion is a thermomechanical process that combines conventional extrusion with the action of a rotating die. The plastic deformation of the material being sheared and extruded is the primary source of process heat and it produces strain distributions unlike those resulting from conventional extrusion. This paper proposes an improved strain analysis that evaluates three main strain components in a series of rate-controlled friction extrusions in which the steady state was achieved. Cylindrical AA1100 extrusion billets with two embedded markers were extruded to wire with a 10:1 diametral reduction. The shape change of the embedded markers was determined via serial, transverse sectioning and quantitative metallography of the extruded wires. Three mutually orthogonal strain components (longitudinal, circumferential, and radial) were calculated at different positions along each extruded wire from the marker's shape change. The development of strain from the initial transient to the steady state is discussed. The variation of the steady-state strain with different process parameters is correlated with the die advance per revolution.

42 ENGINEERING↗

DOE OSTI2019

Friction stirring interlocking of dissimilar materials

A method for solid state joining of dissimilar materials using a friction stir welding device wherein a pin is inserted through an aperture defined in a first material and a second material to hold the materials together and then held in place by friction stir welding a portion of the pin to a material adjacent said pin, or by friction stir welding a cap or plug that holds the pin in place to the adjacent material. The result is a connection or join wherein the central portion of the pin is not friction stir welded but the portions holding the pin in place (the ends or caps) generally are.

Whalen, Scott A.↗

DOE OSTI2019

High Ductility Aluminum Alloy made from Powder by Friction Extrusion

Shear processing has been used to consolidate and extrude aluminum alloy Al-12.4TM powder into bulk nanostructured rods. Extrudates exhibited 450 MPa ultimate tensile strength, 380 MPa yield strength, and 15.7% elongation at ambient temperature. Twice the elongation was achieved compared to conventional extrusion, with similar ultimate and yield strengths, and is attributed to reduction of the Al grain size and refinement and redistribution of nanoscale second phases. Quasicrystalline approximants within the starting powder were not observed in the extrudate, indicating shear processing was effective in solutionizing some fraction of the alloying elements and re-precipitating them as second phase nanoscale intermetallics.

Extrusion, Friction, Nanostructured Materials, Alu↗

DOE OSTI2018

Joining thick section aluminum to steel with suppressed FeAl intermetallic formation via friction stir dovetailing

A new solid-phase technique called friction stir dovetailing (FSD) has been developed for joining thick section aluminum to steel. In FSD, mechanical interlocks are formed at the aluminum-steel interface and are reinforced by metallurgical bonds where intermetallic growth has been uniquely suppressed. Lap shear testing shows superior strength and extension at failure compared to popular friction stir approaches where metallurgical bonding is the only joining mechanism. High resolution microscopy revealed the presence of a 40-70 nm interlayer having a composition of 76.4 at% Al, 18.4 at% Fe, and 5.2 at% Si, suggestive of limited FeAl3 intermetallic formation.

Friction stir dovetailing, Joining, Intermetallics↗

DOE OSTI2017

Effects of thread interruptions on tool pins in friction stir welding of AA6061

In this paper, effects of pin thread and thread interruptions (flats) on weld quality and process response parameters during friction stir welding (FSW) of 6061 aluminium alloy were quantified. Otherwise, identical smooth and threaded pins with zero to four flats were adopted for FSW. Weldability and process response variables were examined. Results showed that threads with flats significantly improved weld quality and reduced in-plane forces. A three-flat threaded pin led to production of defect-free welds under all examined welding conditions. Spectral analyses of in-plane forces and weld cross-sectional analysis were performed to establish correlation among pin flats, force dynamics and defect formation. Finally, the lowest in-plane force spectra amplitudes were consistently observed for defect-free welds.