DOE OSTI2024

Impact of Backing Plate and Thermal Boundary Conditions for High-Speed Friction Stir Welding of 25-mm Thick Aluminum Alloy 7175-T79

Here this study demonstrates high-speed (150 mm/min) single pass friction stir butt joining of 25 mm thick aluminum alloy 7175-T79. To understand the impact of quenching and cooling rate on process responses, joint strength, and grain size distributions across the weld thickness, we performed a series of friction stir welding (FSW) trials in air and with a trailing water spray using steel and composite backing plates (BP). Welds made in air and trailing water spray exhibit significantly different hardness distributions across the nugget, heat affected zone (HAZ), and HAZ minimum hardness as evidenced by detailed microhardness mapping. The effect of trailing water spray (TWS) on joint efficiency overshadows the influence of BP composition due to the vastly different contribution to quenching. TWS also resulted in a multifaceted effect on FSW such as lowering processing temperature, increasing X and Z forces while lowering Y force, and narrow heat affecting zone. Finally, digital image correlation (DIC)-based fracture mode analysis and grain size measurements correlate with the hardness distribution.

42 ENGINEERING↗

DOE OSTI2024

Meshfree Process Modeling and Experimental Validation of Friction Riveting of Aluminum 5052 to Aluminum 6061

Friction riveting (Fric-riveting) is an innovative, fast, and energy-efficient process for spot-joining metal-metal structures. Although fric-riveting has been studied experimentally in recent years, its process modeling is rarely found in the literature primarily because of the associated large material deformation, extreme thermomechanical conditions, and complex contact conditions. In this work, a mesh-free smoothed particle hydrodynamics (SPH) framework that can well handle the abovementioned numerical challenges is used to simulate the fric-riveting of AA5052 to AA6061. Predicted material morphology, multi-point temperatures, and plunge force are thoroughly validated by experimental observations. The material severe plastic deformation zone in the vicinity of the riveting zone is further predicted by the SPH model, which indicates the material mixing and potential grain refinement zone. Based on the validated model, process parameters can be optimized which yields better performance over the baseline case.

Friction riveting (fric-riveting), Smoothed partic↗

DOE OSTI2023

Embedded anchoring of multi-material assemblies by friction riveting process

In this paper, we report on work that focused on extending the capability and broaden the applicability of the friction-riveting process for joining stacks composed of a wide range of multi-layer polymer-to-metals and similar and dissimilar metals. We first present direct experimental evidence of our use of this process to join aluminum-to-steel dissimilar metals with steel rivets. We have demonstrated for the first time the use of magnesium as a rivet material for joining carbon fiber reinforced polymer (CFRP) stacks, aluminum as a rivet material to laminate magnesium to CFRP, and aluminum-to-aluminum similar metal joining and aluminum-to-steel dissimilar metal joining with steel rivets. Our work sheds light on detailed process parameter optimization and the corresponding process response behavior, thus advancing our understanding of this complex joining method for a wide range of material combinations.

Friction-riveting, magnesium rivet, carbon fiber r↗

DOE OSTI2023

High speed butt joining of 1” thick 2139-T8

Thick plate (=1”) butt joining of Al alloys is challenging due to high tool forces, uneven material flow, and heat distribution in the through-thickness direction. Tool design and welding parameters used for executing thick plate butt joining have remained mostly static over the past decade. Reported welding speeds that produce viable joint strength (mostly on 6xxx alloys) typically range below 100 mm/min (4inches /min). Researchers at Pacific Northwest National Laboratory (PNNL) in association with Ground Vehicle Systems Center (US Army GVSC) have been working to demonstrate greater joining efficiency at higher welding speeds in a 1” thick AA2139-T8 plate. Using innovative tool features and effective force and temperature control a joint efficiency of 80% was demonstrated at a welding speed of 7 inches /min (178mm/min).

Das, Hrishikesh↗

DOE OSTI2023

Shear Assisted Processing and Extrusion of Unhomogenized Aluminum Alloy 6063 Castings with High Iron Content

Shear Assisted Processing and Extrusion (ShAPE) was used to fabricate aluminum 6063 tubing directly from secondary scrap. Trimmings from an automotive manufacturing facility were cast into billets spiked with iron (0.3 wt% Fe) to explore the tolerance of ShAPE to Fe contamination. Billets were extruded in the unhomogenized condition to form tubing with an outer diameter of 12 mm and wall thickness of 2 mm. Tensile properties reached 0.2% YS = 206 MPa, UTS = 238 MPa, and U.E. = 16.3% in the T6 temper. Performance exceeds the ASTM minimum standard and is on par with ASM typical values for conventional extrusion of primary aluminum billets in the fully homogenized condition. Microstructural characterization shows extensive refinement of grain size along with dispersion and refinement of Fe-Al-Si intermetallic phases. This study suggests that ShAPE extrusion may offer a lower carbon manufacturing pathway through direct recycling of secondary aluminum scrap and elimination of the billet homogenization step.

solid phase processing, AA 6063, extrusion, Shear ↗

DOE OSTI2022

Effect of post-extrusion heat treatment on mechanical property of aluminum alloy 2024 tube produced using Shear Assisted Processing and Extrusion (ShAPE)

The present work deals with the Shear Assisted Processing and Extrusion (ShAPE) of aluminum alloy 2024 tubes and mechanical property optimization via post extrusion heat treatments (T3510 and T8510). The ShAPE process enables extruding AA2024 at an extrusion speed of 7.4 m/min and extrusion temperature of 480 °C, which is otherwise beyond the extrudability limit of this alloy using conventional extrusion techniques. The ultimate tensile strength reaches 466 MPa for ShAPE+T3510 condition and 503 MPa for ShAPE+T8510 condition, both of which exceed the corresponding ASTM/ASM (minimum/typical) values for the studied tube geometry. The yield strength reaches 382 MPa for ShAPE+T3510 condition and 481 MPa for ShAPE+T8510 condition, both of which surpass any reported values in the literature or the highest industrial values. In addition, the ductility of AA2024 tube fabricated from ShAPE+T3510 or ShAPE+T8510 are evidently improved by the grain size refinement, second phase refinement, and enhanced uniformity in second phase distribution due to the severe plastic deformation of ShAPE process.

Shear Assisted Processing and Extrusions (ShAPE), ↗

DOE OSTI2021

High speed manufacturing of aluminum alloy 7075 tubing by Shear Assisted Processing and Extrusion (ShAPE)

Shear assisted processing and extrusion (ShAPE) was used to extrude aluminum alloy 7075 tubing at speeds up to 12.2 m/min. This is in comparison to 2.0 m/min which is generally the limit for conventionally extruded 7075. The increased speed is primarily attributed to more extensive shear deformation, compared to conventional extrusion, which results in a high density of low angle grain boundaries that facilitate continued deformation and delay the onset of surface tearing. Mechanical testing after heat treating to the T6 condition gave an ultimate tensile strength of 565.3 ± 4.6 MPa, yield strength of 495.7 ± 8.7 MPa, and elongation of 16.8 ± 0.8%. Strength values exceed the ASTM minimum standard and are on par with ASM typical values, while elongation was substantially improved compared to 7 and 11% for the ASTM and ASM values respectively. Finally, it was observed that low temperature extrusion at 341 °C and 40 rpm gave superior material properties in the T6 condition compared to high temperature extrusion at 441 °C and 120 rpm due to variances in nanoscale second phase size and distribution.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Joining AA7099 to Ni-Cr-Mo Steel Using Single Pass Friction Stir Dovetailing and AA6061 Butter Layer

A novel single pass friction stir dovetailing (FSD) was developed to join thick plate AA7099 to Ni-Cr-Mo steel in a lap configuration through the use of an AA6061 butter layer. The butter layer approach can be shown to significantly reduce interfacial failures by inhibiting the formation of brittle Fe–Al intermetallic compounds (IMCs) which are typically formed during conventional friction stir welding (FSW) of AA7099 directly to steel. This study evaluates the strength and microstructural evolution of the aluminum/steel joint interface between single pass FSD of AA7099/AA6061(butter)/steel fabricated using three different FSD tool configurations. The butter layer was achieved by placement of a free-floating strip of AA6061 within the dovetail groove that was pre-machined in the steel substrate. Friction stir welding was then used to simultaneously join the thick plate AA7099, the AA6061 strip and the AA7099 in a single weld pass. To optimize the joining process, three different pin geometries (full thread, half smooth/half thread, no thread) were evaluated; it was demonstrated that the half smooth/half thread tool produced the strongest weld joint due to the absence of a Zn rich layer at the Al/steel interface. The efficacy of this unique processing technique was tested using lap shear tensile testing as well as high resolution transmission electron microscopy (TEM). A discussion of the new FSD technique, joint configurations, and process parameters are provided along with joint microstructural analyses and mechanical performance.

Olszta, Matthew J.↗

DOE OSTI2021

Microstructure and Mechanical Properties of the AA7075 Tube Fabricated using Shear Assisted Processing and Extrusion (ShAPE)

Shear Assisted Processing and Extrusion (ShAPE) experimental setup and tooling were adopted for extruding thin-walled AA7075 aluminum tube from as-cast non-homogenized billet material in a single run. The mechanical and microstructural characterizations were performed on the extrudate in the as-extruded condition without subsequent heat treating. It was shown that the ShAPE process developed a significantly refined microstructure with uniform and almost equiaxed grain structure on both hoop and axial cross-sections of the extrudate as well as through the thickness of the material. The pole figures and inverse pole figures of the EBSD data showed an strong shear texture development, and it was found out that axial shear is the dominant deformation mechanism in the regions near the inner surface of the tube, while combined axial and torsional shears are the two dominant modes of deformation near the outer surface of the extrudate. As for the mechanical properties, there was an increase of 150% and 73% in the yield and ultimate strengths of the tube produced using ShAPE process, respectively, and a 18% decrease in maximum uniform plastic elongation compared to the conventionally extruded AA7075-O tube.

Shear Assisted Processing and Extrusion, Friction ↗

DOE OSTI2021

Shear Assisted Processing and Extrusion of Aluminum Alloy 7075 Tubing at High Speed

Conventional extrusion of aluminum alloy 7075 is limited to 1-2 meters per minute in order to avoid surface tearing and cracking. An emerging technique called Shear Assisted Processing and Extrusion (ShAPE) was used to extrude aluminum alloy 7075 tubing at a speed of 7.4 meters per minute without inducing surface defects. The faster extrusion speed is attributed to the unique flow characteristics inherent to the ShAPE process compared to conventional extrusion. Tubes with an inner diameter of 10 mm, outer diameter of 12 mm, and length of 2 meters were extruded at temperatures ranging from 340°C to 466°C. Tensile testing was performed per ASTM B557-15 with strain measured using digital image correlation. An ultimate tensile strength of 565 ± 4.6 MPa, yield strength of 496 ± 8.7 MPa, and elongation of 16.4 ± 1.0 % were measured for extrusion made at 362°C and heat treated to the T6 condition.

Shear Assisted Processing and Extrusion, Friction ↗

DOE OSTI2021

Shear Assisted Processing and Extrusion of Thin-Walled AA6063 Tubing

Shear Assisted Processing and Extrusion (ShAPE) was used to fabricate thin-walled AA6063 tubing with improved mechanical properties compared to conventional extrusion. Namely, tensile properties for ShAPE extrusions after T5 heat treating far exceed conventional T5 properties and are on par with T6 tensile properties. Die rotational speed did not affect tensile properties, although increased extrusion speed did lead to moderate increases in elongation.

Friction Extrusion, ShAPE, AA 6063, friction stir ↗

DOE OSTI2021

Process Robustness of Friction Stir Dovetailing of AA7099 to Steel with In Situ AA6061 Interlayer Linking

Rolled homogeneous armor (RHA) steel was joined to aluminum alloy AA7099-T7451 with an interlayer of AA6061-T651 by single-pass friction stir dovetailing (FSD). The evolution of the AA7099/AA6061 and AA6061/steel interfacial microstructures and mechanical properties of the joints were examined. The AA6061 interlayer prevented Zn migration from the AA7099 to the steel during FSD and inhibited formation of brittle, Zn-rich, Fe-Al intermetallic compounds within the joint. The flow of the dissimilar aluminum alloys at the interface was controlled with a partially threaded friction stir welding pin and a dovetail geometric configuration optimized in previous work. The process robustness was explored to establish parameter windows by elucidating parametric effects on the relationship between process conditions and the joint’s microstructure and mechanical properties. Ranges of process forge force (50–70 kN) and interface temperature (475°C–515°C) consistently yielded joints with adequate performance. The load-carrying capacity in lap shear tensile tests was 2025 ? 100 N/mm.

Friction Stir Dovetailing, FSW, AA7099, AA6061, Ro↗

DOE OSTI2021

Friction Stir Dovetailing of AA7099 to Steel with AA6061 Interlayer for Reduced Zn Embrittlement at Dissimilar Interface

Joining of high strength Al alloy (AA7099) to steel (rolled homogeneous armor) with and without AA6061 interlayer was achieved using a friction stir dovetailing (FSD) method. Detailed investigations were conducted to establish correlations between mechanical performance and microstructural evolution of FSD joints. Lap shear tensile testing revealed that incorporation of the AA6061 interlayer combined with tailored processing methodology significantly improved both mechanical interlocking and load transmission across the dovetail interface. Following incorporation of the interlayer, the maximum load carrying capacity and peak extension (of the AA7099/AA6061/steel joint) are 60% and 210% higher, respectively, than results obtained from an AA7099/steel joint without an interlayer. Without an AA6061 interlayer, formation of zinc rich intermetallic compounds led to brittle interfacial failure of the AA7099-steel FSD joint. Incorporation of novel tool and joint configuration eliminated asymmetric joint performance as a function of loading direction, which is generally observed in friction stir lap welding. The efficacy of the use of an AA6061 interlayer in joining AA7099 to steel was demonstrated through mechanical testing as well as high resolution analytical electron microscopy characterization.

Dissimilar metal joining, Friction stir dovetailin↗

DOE OSTI2020

Joining of Thermoset Carbon Fiber Reinforced Polymer and AZ31 Magnesium Alloy Sheet Via Friction Stir Interlocking

A new technique called friction stir interlocking (FSI) was applied for lap-joining of AZ31 magnesium sheet and thermoset carbon fiber reinforced polymer (TS-CFRP) sheet. Instead of directly joining AZ31 and TS-CFRP, a series of magnesium interlocks were used to friction stir weld with AZ31 sheet to enable joining with TS-CFRP. Microstructural characterization of joint cross sections showed that a tool rotation rate of 800 rpm produced incomplete mixing of magnesium interlocks and the top AZ31 sheet, while 1200 rpm achieved sufficient material mixing to avoid unwelded regions. Mechanical property characterization showed that AZ31/TS-CFRP dissimilar joints failed through the magnesium interlock shanks during lap shear tensile testing, with a maximum normalized joint strength reaching ~100 MPa.

Wang, Tianhao↗

DOE OSTI2020

Numerical Simulation and Experimental Validation of Joint Performance in Aluminum-Steel Lap Welds Formed by Friction Stir Dovetailing

Friction stir dovetailing (FSD) is a new dissimilar material joining process that simultaneously forms a mechanical interlock and metallurgical bond at the dissimilar material interface. This work presents development of a modeling and simulation approach to predict mechanical performance of FSD thick section aluminum to steel joints. A finite element analysis (FEA) was carried out in order to predict the load-carrying capacity and failure location for aluminum thicknesses between 12.7 mm and 50.8 mm with different numbers of dovetails. The numerical results and corresponding experimental investigation are in agreement and suggest that the developed methods can be used effectively for design and analysis of FSD joints using standard FEA tools.

Friction stir dovetailing, Friction stir welding, ↗