Acceptance testing of the LCLS-II-HE production cavities is approximately 65% complete. In this report, we present details of the test results, including summaries of the quench fields, intrinsic quality factors, and experience with field emission. We also offer an outlook on the remaining tests to be performed.
Nitrogen-doped niobium SRF cavities are sensitive to trapped magnetic flux, which decreases the cavity intrinsic Q₀. Prior experimental results have shown that heat treatments to 900°C and higher can result in stronger flux expulsion during cooldown; the precise temperature required tends to vary by vendor lot/ingot of the niobium material used in the cavity cells. For LCLS-II-HE, to ensure sufficient flux expulsion in all cavities, we built and tested single-cell cavities to determine this required temperature for each vendor lot of niobium material to be used in cavity cells. In this report, we present the results of the single-cell flux expulsion testing and the Q₀ of the nine-cell cavities built using the characterized vendor lots. We discuss mixing material from different vendor lots, examine the lessons learned, and finally present an outlook on possible refinements to the single-cell technique.
Nb3Sn offers better RF performance (Q and Eacc) than Nb at any given temperature because of its superior superconducting properties. The potential deployment of Nb3Sn-coated SRF cavities at 4 K, delivering similar performance to that of Nb cavities at 2 K, will be a transformational technology to enable new classes of SRF accelerator applications. A clean and smooth surface can enhance the performance of the Nb3Sn-coated cavity, typically, the attainable acceleration gradient. The reduction of surface roughness is often linked with a correlative reduction in average coating thickness and grain size. A new approach to enhance the nucleation centers using the pre-deposition of Sn on Nb is introduced for surface roughness reduction. Besides Sn supply's careful tuning, the temperature profiles were varied to engineer the coating surface with reduced roughness as low as ~40 nm in 20 µm × 20 µm AFM scans, one-third that of the typical coating. Electropolishing of coated sample shows surface a clear surface smoothening. A few sets of coating parameters were used to coat 1.3 GHz sin-gle-cell cavities to understand the effects of roughness variation on the RF performance. This presentation discusses ways to reduce surface roughness with results from a systematic analysis of the samples and Nb3Sn-coated single-cell cavities.