Polyimide/metal composite films via in situ decomposition of inorganic additives - Soluble polyimide versus polyimide precursor

Polyimide-metal oxide (Co3O4 or CuO) composite films have been prepared via in situ thermal decomposition of cobalt (II) chloride or bis(trifluoroacetylacetonato)copper(II). A soluble polyimide (XU-218) and its corresponding prepolymer (polyamide acid) were individually employed as the reaction matrix. The resulting composites exhibited a greater metal oxide concentration at the air interface with polyamide acid as the reaction matrix. The water of imidization that is released during the concurrent polyamide acid cure and additive decomposition is believed to promote metal migration and oxide formation. In contrast, XU-218 doped with either HAuCl4.3H2O or AgNO3 yields surface gold or silver when thermolyzed (300 C).

Rancourt, J. D.↗
NASA NTRS1988

Characterization of microcomposite polyimide films

Thermally stable microcomposite polyimide films were prepared by the homogeneous incorporation of either a soluble metal salt or a metal complex into a poly(amide-acid)/N,N-dimethylacetamide solution. The thermal processing of films solvent cast onto glass substrates and cured in an appropriate atmosphere yields films containing not only a fairly uniform dispersion of submicrometer particles, but also a new surface layer of metal or metal oxide. These polymeric systems have been characterized using X-ray photoelectron spectroscopy, Auger electron spectroscopy with depth profiling via argon ion etching, transmission electron microscopy of ultramicrotomed cross-sections, scanning electron microscopy, elemental analysis, thermal analysis, and variable temperature electrical resistivity determinations. The data from these techniques were used cooperatively to develop a model for these microcomposite polyimide films.

Rancourt, J. D.↗
NASA NTRS1988

Characterization of cobalt(II) chloride-modified condensation polyimide films

The effect of solvent extraction on the properties of cobalt(II) chloride-modified polyimide films was investigated. Solvent-cast films were prepared from solutions of cobalt chloride in poly(amide acid)/N,N-dimethylacetamide (DMAc) and were subsequently dried and cured in static air, forced air, or inert gas ovens with controlled humidity. The films were extracted by either of the three processes (1) soaking in a tray with distilled water at room temperature, (2) soxhlett extraction with distilled water, or (3) soxhell extraction with DMAc. Extraction with DMAc was found to remove both cobalt and chlorine from the films and to slightly increase bulk thermal stability and both surface resistivity and electrical resistivity.

Rancourt, J. D.↗
NASA NTRS1987

DC electrical, thermal, and spectroscopic properties of various condensation polyimides containing surface cobalt oxide

Doping polyimides with cobalt ion causes the room temperature direct current electrical resistivity to decrease relative to the polymer alone, the reduction being most pronounced for the air-side of the cobalt modified polyimides. At a constant electrical field, resistivity for the volume, air-side and glass-side modes decreases yet further with an increase in temperature as expected for semiconductors and insulators. X-ray photoelectron spectroscopy indicates the air-side of the cobalt modified polyimides is predominantly Co3O4. The bulk resistivity of the air-side and activation energy of conduction for this surface are comparable to high purity sintered Co3O4. Charging characteristics at room temperature indicate a substantial polymer matrix contribution to both the glass-side and volume mode measurements but a negligible contribution to the air-side electrical properties. Volume electrical resistivity for similar additive levels is reduced by increasing the molecular flexibility of the host polymer.

Rancourt, J. D.↗
NASA NTRS1987

Electrical properties of polyimides containing a near-surface deposit of silver

Films containing a surface or near-surface deposit of palladium, gold or copper metal as well as tin, cobalt, copper, or lithium oxides have been prepared by dissolving appropriate metal salts into poly(amide-acid)/N,N-dimethylacetamide solutions and curing the solvent cast films to temperatures up to 300 C. This preparation technique has been extended to evaluate the thermal, spectroscopic, and electrical characteristics of condensation polyimide films modified with silver nitrate. A near-surface deposit of metallic silver results but the reflective surface has high electrical resistivity (sheet resistivity) due to a polymer coating or overlayer above the metal. Details pertaining to the silver nitrate modified condensation polyimides are presented. Also, the applicability of the structural model and electrical model previously proposed for the cobalt oxide system are assessed.