Achieving uniaxial magnetic anisotropy in Ce2⁢Fe17⁢N3 through Co- and Sm-substitution

Th2⁢Zn17−type structure-based permanent magnets, such as Sm2⁢Fe17⁢N3, offer strong potential as alternatives to neodymium magnets (NdFeB), but their practical use is limited by phase stability and the scarcity of Sm. Ce-based counterparts, particularly Ce2⁢Fe17⁢N3, are attractive low-cost candidates, yet their intrinsic planar magnetic anisotropy restricts permanent-magnet performance. Here, we induce uniaxial magnetic anisotropy in Ce2⁢Fe17⁢N3 through two approaches: (i) Co substitution on the Fe sublattice and (ii) partial substitution of Ce with Sm. Combined density functional theory and experimental results show that both strategies modify the 3⁢𝑑–4⁢𝑓 interactions and band filling, yielding magnetization values up to ∼1.2T and magnetocrystalline anisotropy energies exceeding 1MJ/m3 for Co-alloyed compositions, with significantly larger anisotropy achieved upon Sm substitution. In addition, the Sm-substituted Ce2⁢Fe17⁢N3 samples exhibit enhanced high-temperature stability compared to Sm2⁢Fe17⁢N3. These findings demonstrate that Ce2⁢Fe17⁢N3-based alloys can deliver magnetic performance suitable for permanent-magnet applications while reducing cost and reliance on critical rare-earth elements, and they provide practical design guidelines for rare-earth-lean magnets for energy and industrial applications.