DOE OSTI2021

Spatially-resolved lithiation dynamics from operando X-ray diffraction and electrochemical modeling of lithium-ion cells

In this study, energy dispersive X-ray diffraction is used to profile the time evolution of ordered Li x C 6 phases in solid electrodes of lithium-ion cells charged at rates between 0.2 and 4.7C (where 1C corresponds to full discharge in 1 h). The methods for quantifying lithium concentration in these phases from the acquired diffraction patterns are described. Compact expressions for time-dependent concentration gradients in the solid electrodes using orthogonal polynomial expansions are presented. Experimentally, these gradients persisted in lithiated graphite electrodes even after the cells rested at open-circuit for over 9 h. A multiphase electrochemical model of graphite intercalation captured many of the observed behaviors, including the progression of phase transitions and the persistent gradients at zero current. However, the magnitude of concentration gradients in both the oxide cathode and graphite anode is underestimated by the model, even at moderate currents.

25 ENERGY STORAGE↗

DOE OSTI2020

In situ X-ray spatial profiling reveals uneven compression of electrode assemblies and steep lateral gradients in lithium-ion coin cells

Coin cells are used extensively as test devices in battery research for evaluation of new materials and optimization of cycling protocols. Here, in situ X-ray diffraction profilometry is used to characterize spatial distribution of the active materials, lithiation, and phase distribution in electrodes of NCM523/graphite coin cells. The X-ray data indicate uneven areal compression of the electrode assembly in such cells, which we trace to a specific design feature that leads to elastic deformation of a metal spacer. Steep lithiation gradients observed in the electrodes imply radially-dependent resistivity, for which uneven compression of the separator is a likely cause. Electrochemical model calculations suggest that variable porosity of the polymer separator would account for the salient features of spatial profiles observed in these coin cells.

25 ENERGY STORAGE↗

DOE OSTI2020

Rate-Dependent Aging Resulting from Fast Charging of Li-Ion Cells

The mass electrification of personal and service vehicles is reliant on the ability of battery packs to undergo extreme fast recharging. A central challenge is that the repeated exposure to high currents can trigger and/or accelerate mechanisms of performance degradation, such as lithium deposition, mechanical damage of active material particles, and impedance rise. Here, we investigate whether constraining high-rate charging to limited state-of-charge (SOC) ranges can mitigate these aging processes. Our experiments map the boundaries of lithium plating conditions, and also indicate that permanent losses of electrode capacity appear to be a function of cycle number, but not charging rate. Interestingly, we show that impedance rise appears to depend on charging rate alone, and not on the amount of charge passed at each cycle. This observation suggests that limiting fast charging to a narrow SOC range would only delay cell aging, but not fully prevent it from happening. We identify oxide-particle cracking as the likely mechanism for this impedance rise, suggesting that particle and electrode design are essential to enable fast charging. The findings of this work can inform the development of fast-charging protocols that are less damaging to cell health.

25 ENERGY STORAGE↗