DOE OSTI2024

Vertical GaN Superjunction Diode on Sapphire with Kilovolt Dynamic Breakdown Voltage

The development of superjunction structures for use in vertical wide bandgap power devices promise to break the 1-D material limits. Additionally, the possibility of utilizing heteroepitaxial GaN-on-Sapphire wafer for vertical devices can significantly trim the material and device cost. This work introduces a quasi-vertical GaN-on-Sapphire superjunction PN diode design utilizing sputtered p-NiO on the etched GaN fins for superjunction formation. DC breakdown voltage is shown to vary with superjunction charge imbalance and significantly exceed the expected 1-D planar limit of 350V given the epilayer design used. A maximum breakdown voltage of 840 V is extracted for near charge balance conditions limited by leakage current. Dynamic breakdown of the device is characterized as a function of reverse voltage slew rate. A maximum dynamic breakdown voltage of 1160 V under a reverse voltage slew rate of 2000 V/μs is found.

Porter, Matthew↗

DOE OSTI2023

2 kV, 0.7 mΩ•cm2 Vertical Ga2O3 Superjunction Schottky Rectifier with Dynamic Robustness

We report the first experimental demonstration of a vertical superjunction device in ultra-wide bandgap (UWBG) Ga 2 O 3 . The device features 1.8 μm wide, 2×10 17 cm -3 doped n-Ga 2 O 3 pillars wrapped by the charge-balanced p-type nickel oxide (NiO). The sidewall NiO is sputtered through a novel self-align process. Benefited from the high doping in Ga 2 O 3 , the superjunction Schottky barrier diode (SJ-SBD) achieves a ultra-low specific on-resistance (R ON,SP ) of 0.7 mΩ•cm 2 with a low turn-on voltage of 1 V and high breakdown voltage (BV) of 2000 V. The R ON,SP ~BV trade-off is among the best in all WBG and UWBG power SBDs. The device also shows good thermal stability with BV > 1.8 kV at 175 °C. In the unclamped inductive switching tests, the device shows a dynamic BV of 2.2 kV and no degradation under 1.7 kV repetitive switching, verifying the fast acceptor depletion in NiO under dynamic switching. Such high-temperature and switching robustness are reported for the first time in a heterogeneous superjunction. These results show the great potential of UWBG superjunction power devices.

Qin, Yuan↗

DOE OSTI2023

1 kV Self-Aligned Vertical GaN Superjunction Diode

This work demonstrates vertical GaN superjunction (SJ) diodes fabricated via a novel self-aligned process. The SJ comprises n-GaN pillars wrapped by the charge-balanced p-type nickel oxide (NiO). After the NiO sputtering around GaN pillars, the self-aligned process exposes the top pillar surfaces without the need for additional lithography or a patterned NiO etching which is usually difficult. The GaN SJ diode shows a breakdown voltage (B V) of 1100 V, a specific on-resistance (R ON ) of 0.4 mΩ· cm2, and a SJ drift-region resistance ( R dr ) of 0.13 mΩ· cm2. Further, the device also exhibits good thermal stability with B V retained over 1 kV and R ON dropped to 0.3 mΩ· cm2 at 125°C. The trade-off between B V and R dr is superior to the 1D GaN limit. These results show the promise of vertical GaN SJ power devices. The self-aligned process is applicable for fabricating the heterogeneous SJ based on various wide- and ultra-wide bandgap semiconductors.