DOE OSTI2024

Cellulose crystallinity index (CrI) of switchgrass measured by solid-state NMR

Here we present a curated dataset of switchgrass cellulose crystallinity index (CrI) measured using solid state nuclear magnetic resonance (NMR) spectroscopy. Seventy-two topline switchgrass lines grown in greenhouse were collected and ground to -20/+80 mesh. The switchgrass was then Soxhlet-extracted with toluene/ethanol for 24 h to remove extractives. The extractives-free switchgrass was holopulped by using peracetic acid at 5 g loading per g biomass and the solution consistency was adjusted to 5% with DI water. Holopulping was conducted at room temperature for 24 h with stirring. The obtained holocellulose was washed excessively with DI water and air-dried at room temperature for 24 h. The dried holocellulose was treated with hydrochloric acid (2.5 M) for 2 h to remove hemicellulose. The isolated cellulose was collected by filtration, rinsed with DI water, and used to analyze cellulose crystallinity by solid-state NMR. The NMR samples were prepared by packing the moisturized cellulose into 4-mm cylindrical Zirconia MAS rotors. Cross polarization/magic angle spinning (CP/MAS) NMR analysis of cellulose was carried out on a Bruker Avance III 400-MHz spectrometer operating at 100.59 MHz for 13C in a Bruker double-resonance MAS probe head at spinning speeds of 8 kHz. The CP/MAS experiments utilized a 5 ms (90°) proton pulse, 1.5 ms contact pulse, 4 s recycle delay and 4000 scans. The cellulose crystallinity index was determined from the areas of the cellulose crystalline C4 signal (δ 86-92 ppm) over the entire C4 regions (δ 79-92 ppm) in the NMR spectra.

Cellulose, crystallinity index, switchgrass, solid↗

DOE OSTI2024

Lignin molecular weights of Populus trichocarpa residues after CELF pretreatment

Here we present a dataset of molecular weights of lignin from a woody energy crop (Populus trichocarpa) residues after a series of co-solvent enhanced lignocellulosic fractionation (CELF) pretreatment. The natural poplar variant GW-9947 from the Center for Bioenergy Innovation (CBI) was used. The poplar was knife milled and passed through a 1 mm sieve and CELF pretreatment was performed in a Parr autoclave reactor with 7.5 wt % solids loading, 0.5 wt% H2SO4 as catalyst at 150°C with various time. Tetrahydrofuran was added in a 1:1 mass ratio with water as the pretreatment solvent. Lignin was isolated from the pretreated samples after ball-milling in a porcelain jar with ceramic balls via Retsch PM 200 at 580 rpm for 2.5 h followed by enzymatic hydrolysis in acetate buffer (pH 4.8, 50 °C) for 48 h. The solid residue was isolated by centrifugation and hydrolyzed again with freshly added buffer and enzymes for another 48 h. After filtration, the solid residue was extracted twice with 96% (v/v) 1,4-dioxane/water mixture at room temperature overnight. The extracts were combined, rotary evaporated, and freeze-dried to recover lignin. The lignin samples were then derivatized in an acetic anhydride/pyridine (1:1, v/v) mixture and stirred at room temperature for 24 h. Ethanol was added to the reaction mixture, left for 30 min and then removed with a rotary evaporator. The addition and removal of ethanol was repeated at least 3 times until all traces of acetic acid were removed. Acetylated lignin samples were then dissolved in tetrahydrofuran (THF) at a concentration of 1.0 mg/mL. The molecular weight of acetylated lignin was measured by a gel permeation chromatography (GPC) on a PSS-Polymer Standards Service (Warwick, RI, USA) GPC SECurity 1200 system featuring Agilent HPLC 1200 components equipped with four Waters Styragel columns (HR1, HR2, HR4 and HR6) and an UV detector (270 nm). Tetrahydrofuran was used as the mobile phase and flow rate was 0.3 mL/min. The Polymer Standards Service WinGPC Unity software (Build 6807) was used for data processing for all the samples. The data provides information about the effects of CELF pretreatment time at 150 ºC on lignin molecular weights.

09 BIOMASS FUELS↗

DOE OSTI2024

Cellulose molecular weight of corn stover with cotreatment

Here we present a dataset of cellulose molecular weights from corn stover after a cotreatment process. The corn stover sample was subjected to a combination of mechanical disruption (ball milling) and consolidated bioprocessing (CBP) process using the bacterium C. thermocellum at 60 grams/L solids loadings. Cellulose was isolated from control, no cotreatment control, and cotreatment corn stover. Cellulose was then derivatized using anhydrous pyridine and phenyl isocyanate over 48 h at 70 ºC. The reaction was quenched by anhydrous methanol. Methanol and water mixture (7:3, v/v) was added dropwise to promote precipitation of the cellulose derivative. The solids were collected by filtration and thoroughly washed with the methanol and water mixture followed by water. The cellulose derivative was dried overnight under vacuum at 40°C. The obtained cellulose tricarbanilates was then dissolved in tetrahydrofuran (THF) at 1.0 mg/mL and the solution was filtered through a 0.45 µm PTFE filter and placed in an auto-sampler vial. The molecular weight of cellulose was measured by Agilent GPC SECurity 1200 system equipped with four Waters Styragel columns (i.e., HR0.5, HR2, HR4, and HR6) and a UV detector (270 nm). THF was used as the mobile phase. Data collection and processing was performed by Polymer Standards Service WinGPC Unity software (Build 6807). The molecular weight was calculated relative to the polystyrene calibration curve. The data on molecular weights provided information about the effects of cotreatment on corn stover cellulose molecular changes.

Cellulose, molecular weights, corn stover, cotreat↗

DOE OSTI2024

Carbon-13 NMR spectra of lignin isolated from field grown transgenic poplar

Here we present a curated dataset of a series of 13C nuclear magnetic resonance (NMR) spectra of lignin isolated from transgenic monolignol 4-O-methyltransferase (MOMT4) engineered poplar. The transgenic poplar was collected from a 3-year field trial experiment. The poplar was Soxhlet-extracted with toluene/ethanol and the extractives-free poplar was then ball-milled in a Retsch PM100 planetary ball mill using a porcelain jar with ceramic balls at 600 rpm for 2 h. The ball-milled materials were then subjected to enzymatic hydrolysis for 48 h followed by centrifugation and washing with deionized water. The solid residue was extracted twice with 96:4 (v/v) 1,4-dioxane/water mixture at room temperature overnight. The extracts were combined, rotary evaporated, and freeze-dried to recover the lignin. The dry lignin samples were dissolved in deuterated dimethyl sulfoxide for NMR characterization. 13C experiments were performed in a Bruker Avance III HD 500 MHz NMR spectrometer operating at a frequency of 125.12 MHz for the 13C nucleus using a standard Bruker pulse sequence (zgpg) on a Prodigy platform cryoprobe. The NMR spectra were acquired under the following conditions: spectra width 229 ppm, 64k data points, 1s pulse delay, and 6k scans. All the data was processed using the Bruker’s TopSpin 3.6 software. Additional meta data is embedded in the raw spectra files.

13C NMR, lignin, poplar, field trial, MOMT4, CBI↗

DOE OSTI2024

Two-dimensional heteronuclear single quantum coherence (HSQC) NMR spectra of lignin isolated from Populus trichocarpa residues after CELF pretreatment and CBP fermentation

Here we present a curated dataset of a series of two-dimensional heteronuclear single quantum coherence (HSQC) nuclear magnetic resonance (NMR) spectra of lignin isolated from a woody energy crop (Populus trichocarpa) residues after co-solvent enhanced lignocellulosic fractionation (CELF) pretreatment and consolidated bioprocessing (CBP) process. The natural poplar variant GW-9947 from the Center for Bioenergy Innovation (CBI) was used. The poplar was knife milled and passed through a 1 mm sieve. The CELF pretreatment was performed in a Parr autoclave reactor with 7.5 wt % solids loading, 0.5 wt% H2SO4 as catalyst at 150°C with 15, 25 and 30 minutes, respectively. Tetrahydrofuran was added in a 1:1 mass ratio with water as the pretreatment solvent. The residues from CELF pretreatment were then subjected to CBP using the bacterium C. thermocellum DSM 1313. CBP fermentations were performed at 60 °C in a shaker at 50 grams/L solids loadings. Lignin was isolated from the pretreated samples after ball-milling in a porcelain jar with ceramic balls via Retsch PM 200 at 580 rpm for 2.5 h followed by enzymatic hydrolysis in acetate buffer (pH 4.8, 50 °C) for 48 h. The lignin samples were characterized using 13C–1H HSQC experiments which were performed in a Bruker Avance III HD 500 MHz NMR spectrometer operating at a frequency of 125.12 MHz for the 13C nucleus. A standard Bruker pulse sequence was used on a Prodigy platform cryoprobe. The dry lignin samples were dissolved in deuterated dimethylsulfoxide for HSQC experiments. The spectra were acquired under the following acquisition conditions: 210 ppm spectral width in F1 (13C) dimension with 256 data points and 11 ppm spectral width in F2 (1H) dimension with 1024 data points, a 90° pulse, a one bond C–H coupling constant of 145 Hz, a 1.0 s pulse delay, and 64 scans. All the data was processed using the TopSpin 3.6 software (Bruker BioSpin). The NMR spectra provides structural characteristics information about lignin remaining in solids after CELF (150 °C with 15, 25 and 30 minutes) process and C. thermocellum CBP.

Lignin structure, HSQC, poplar, CELF, CBP, CBI↗

DOE OSTI2024

Investigation of Cyrene organosolv fractionation of softwood biomass and alkaline post-incubation

Cyrene organosolv fractionation effectively extracted 78% of lignin from recalcitrant softwood biomass pine at a mild temperature of 120°C. However, the enzymatic conversion of the fractionated cellulose-rich solid did not improve significantly. Alkali post-incubation of the fractionated cellulose fraction notably enhanced the glucan conversion. This phenomenon has also been observed in other organosolv processes, but how this approach transforms pretreated biomass has not yet been comprehensively investigated. In this study, small-angle X-ray scattering (SAXS) was employed to understand the structural changes in biomass during fractionation and post-incubation at the nanometer scale. Further, no lignin aggregation was found on the microfibrils, whereas the distance between the microfibrils increased after pretreatment and decreased after alkaline post-incubation. These results suggests that the Cyrene molecules remained between the microfibrils and were removed by post-incubation. In addition, the pine lignin recovered after pretreatment was characterized by NMR to understand the impact of Cyrene pretreatment on the lignin structure.

09 BIOMASS FUELS↗