Robust implementation of Physical Regime Sensitivity and demonstration on Richtmyer–Meshkov Instability experiments
Not Available
36 MATERIALS SCIENCE↗
Engineering topics
Prime, Michael B. (ORCID:0000000240985620)
Publications and source records attributed to Prime, Michael B. (ORCID:0000000240985620).
Multiscale Richtmyer-Meshkov instability experiments to isolate the strain rate dependence of strength
Theoretical analysis of Richtmyer-Meshkov instability (RMI) experiments for solid strength shows that the strain rate for a given shock should be inversely proportional to the length scale of the sine wave perturbations when η 0 k , the nondimensional amplitude to wavelength ratio, is held fixed. To isolate the effect of strain rate on strength, free-surface RMI specimens of annealed copper were prepared with three perturbation regions with the same η 0 k but different length scales, characterized by the wavelength λ varying by a factor of 4.9 from 65 to 130 to 320 µ m . Three such targets with different fixed η 0 k ′ s were impacted to a shock pressure of 25 GPa, and the instability evolution was measured with photon Doppler velocimetry. Strengths estimated by comparing hydrocode simulation to the data increased from 700 to 1200 MPa as λ decreased. The different η 0 k targets exercised increasing amounts of plastic strain yet showed no evidence of strain hardening. Physical regime sensitivity analysis determined that for 320 − 65 µ m wavelength perturbations, the effective strain rates increased from 8.7 × 10 6 to 3.3 × 10 7 s − 1 , a factor of 3.8. Thus, the predicted strain rate scaling was mostly achieved but slightly suppressed by increased strength at higher rates. The RMI strength estimates were plotted against constitutive testing data on copper from the literature to show striking evidence of the strength upturn at higher strain rates. Published by the American Physical Society 2024
36 MATERIALS SCIENCE↗
A Multi-Phase Modeling Framework Suitable for Dynamic Applications
Under dynamic loading conditions and the associated extreme conditions many metals will undergo phase transformations. The change in crystal structure associated with solid–solid phase transformations can significantly alter the subsequent mechanical response of the material. For the interpretation of experiments involving dynamic loading it is beneficial to have a modeling framework that captures key features of the material response while remaining relatively simple. We introduce a candidate framework and apply it to the metal tin to highlight a range of behaviors that are captured by the model. We also discuss potential extensions to capture additional behaviors that could be important for certain materials and loading scenarios. The model is useful for analysis of results from dynamic experiments and offers a point of departure for more complex model formulations.