NASA NTRS1985

Polyimide matrix resins for up to 700 deg F service

TRW is in the process of data accumulation that strongly indicates that incorporation of the perfluorsisopropylidene linkage in molecular structures other than those employed in DU Pont's NR-150B polyimides likewise yield polymers demonstrating extremely high thermo-oxidative stability. Polyimide synthetic and characterization studies conducted to date on new polymers incorporating the perfluoroisopropylidene linkage are presented and discussed.

Jones, R. J.↗

NASA NTRS1984

Development of partially fluorinated resin apex seals

Partially fluorinated polyimides were prepared and molded in the form of discs and pins for test as potential apex seal materials for advanced rotary combustion engines. The polyimides were formulated from the diamine 2,2-bis 4-(4-aminophenoxy)phenyl hexafluoropropane (4-BDAF) and the dianhydrides of pyromellitic acid (PMDA) and benzophenonetetracarboxylic acid (BTDA). Tribological testing was performed at sliding speeds of 0.31 to 11.6 m/s and at temperatures of from 298K to 573K. It is shown that the carbon fiber filled polyimides, particularly the 80/20 compositions, have an excellent balance of wear/friction at 573K. The unfilled, 80/20 and 60/40 compositions indicate an unusual combination of high friction and low wear which may be advantageous in such applications as brakes and traction drives.

Green, H. E.↗

NASA NTRS1983

Improved high temperature resistant matrix resins

The objective was to develop organic matrix resins suitable for service at temperatures up to 644 K (700 F) and at air pressures up to 0.4 MPa (60 psia) for time durations of a minimum of 100 hours. Matrix resins capable of withstanding these extreme oxidative environmental conditions would lead to increased use of polymer matrix composites in aircraft engines and provide significant weight and cost savings. Six linear condensation, aromatic/heterocyclic polymers containing fluorinated and/or diphenyl linkages were synthesized. The thermo-oxidative stability of the resins was determined at 644 K and compressed air pressures up to 0.4 MPa. Two formulations, both containing perfluoroisopropylidene linkages in the polymer backbone structure, exhibited potential for 644 K service to meet the program objectives. Two other formulations could not be fabricated into compression molded zero defect specimens.

Chang, G. E.↗